High-hydroscopicity polyvinyl chloride (PVC) material and preparation method

A high water absorption, granular material technology, applied in the field of plastic products, can solve problems such as poor water absorption, and achieve the effect of good mechanical properties and good water absorption

Active Publication Date: 2012-07-18
ZHEJIANG HONGSHENGYUAN CAR ACCESSORIES
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the water absorption of PVC material in the prior art is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hydroscopicity polyvinyl chloride (PVC) material and preparation method
  • High-hydroscopicity polyvinyl chloride (PVC) material and preparation method
  • High-hydroscopicity polyvinyl chloride (PVC) material and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] First, stir PVC SG-3 90Kg, plasticizer DOP 75Kg, composite stabilizer 4Kg, antioxidant 1010 0.3Kg, third monomer TMPTMA 3Kg at a speed of 900 rpm until the temperature of the mixture is 50-56 ℃;

[0025] Then, add initiator DCP 0.2Kg, carboxymethyl cellulose 35Kg and stir at a speed of 900 rpm for 5-6 minutes, and stop stirring when the temperature of the mixture reaches 90-92°C;

[0026] Finally, extrude and granulate the above mixture in a twin-screw extruder, and the temperature of each section of the twin-screw extruder is 1#130°C, 2#140°C, 3#160°C, 4#165°C, 5#160°C , 6# 160°C, machine head 150°C, the PVC granular material with high water absorption performance is obtained.

Embodiment 2

[0028] Same as the preparation steps in Example 1, with the following differences:

[0029] PVC SG-3 100Kg, plasticizer DOP 80Kg, aluminum salt composite stabilizer 5Kg, antioxidant 10100.4Kg, third monomer TMPTMA 4Kg, initiator DCP 0.3Kg, carboxymethyl cellulose 40Kg.

Embodiment 3

[0031] Same as the preparation steps in Example 1, with the following differences:

[0032] PVC SG-3 100Kg, plasticizer DOP 86Kg, aluminum salt composite stabilizer 6Kg, antioxidant 10100.5Kg, third monomer TMPTMA 5Kg, initiator DCP 0.4Kg, carboxymethyl cellulose 46Kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-hydroscopicity polyvinyl chloride (PVC) material and a preparation method. The material is prepared by the following raw materials according to parts by weight: PVC SG- 3: 90-100, carboxymethylcellulose: 35-46, initiator dibasic calcium phosphate (DCP): 0.2-0.4, a third monomer trimethylopropane trimethacrylate (TMPTMA): 3-5, an antioxygen 1010: 0.3-0.5, a plasticizer Di N octyl phthalate (DOP): 75-86, and a compound stabilizer: 4-6. The preparation method for the PVC granular material includes the following steps: the PVC SG-3, the third monomer TMPTMA, the antioxygen 1010, the plasticizer DOP and the compound stabilizer are placed in a mixer to be mixed until mixed material temperature is 50-56 DEG C, an initiator and carboxymethylcellulose are then added to be mixed and mixing does not stop until mixed material temperature is 90-92 DEG C. Finally, the mixed material is placed in a hopper and extruded and granulated through a double-screw extruder, and the high-hydroscopicity PVC granular material is obtained.

Description

technical field [0001] The invention belongs to the technical field of plastic products, and in particular relates to a high water-absorbing PVC material. The invention also relates to a preparation method of the PVC material. Background technique [0002] PVC material is polyvinyl chloride, which is one of the plastic products with the largest output in the world. It is cheap and widely used. The polyvinyl chloride resin is white or light yellow powder. Different additives can be added according to different uses, and PVC plastics can exhibit different physical and mechanical properties. Adding an appropriate amount of plasticizer to polyvinyl chloride resin can make a variety of hard, soft and transparent products. Polyvinyl chloride plastic has good mechanical properties, wear resistance, and chemical corrosion resistance, and can be made into a variety of daily necessities. It is a general-purpose plastic with the most cost-effective performance. But the water absorpt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F291/00C08F2/44C08K5/134
Inventor 孙放明范高锋
Owner ZHEJIANG HONGSHENGYUAN CAR ACCESSORIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com