Shock-proof ring of air conditioner motor

A technology of anti-vibration ring and air conditioner, which is applied in the direction of electromechanical devices, electrical components, electric components, etc., can solve the problems of poor oil-proof and anti-vibration performance, high-temperature flow of anti-vibration ring, easy aging hardness, etc., and achieve excellent resistance to cold and heat shocks and save costs , excellent performance

Active Publication Date: 2013-11-13
NINGGUO ZOYE PLASTIC & RUBBER CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The anti-vibration ring of the traditional air conditioner motor has the phenomenon of high temperature flow and low temperature cracking. At the same time, the anti-oil and anti-vibration performance is poor. At high temperature and low temperature, it is easy to age and the hardness decreases.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The anti-vibration ring of an air conditioner motor is made of the following raw materials in parts by weight: 1 part of sulfur powder, 140 parts of EPDM rubber, 0.5 part of vulcanizing agent TRA, 120 parts of calcined clay, accelerator 1.5 parts of M, 20 parts of carbon black, 0.5 parts of accelerator TMTD, 30 parts of light calcium carbonate, 3 parts of antioxidant BZ, 90 parts of paraffin oil, 1.5 parts of accelerator CZ, 10 parts of zinc stearate, 10 parts of zinc oxide , 1.5 parts of coupling agent, 0.3 parts of stearic acid, 15 parts of white carbon black, 5 parts of processing aid WB-16, 6 parts of PEG4000, 1.5 parts of antioxidant 2246.

[0014] The carbon black is carbon black N550, the paraffin oil is paraffin oil 2550, and the coupling agent is a silane coupling agent.

[0015] It is prepared by mixing process and vulcanization process.

[0016] The preparation process is as follows: taking each raw material according to the weight part, fully mixing to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardness changeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a shock-proof ring of an air conditioner motor. The shock-proof ring is manufactured by fully mixing all raw materials in parts by weight to obtain mixed compound, then vulcanizing and machining. The shock-proof ring has superior oil resistance, high temperature and low temperature resistance, and cold and heat resistance and is used for manufacturing the shock-proof ring of the air conditioner motor; the cost is saved; and the performance is superior.

Description

technical field [0001] The invention relates to the field of air conditioner motor accessories, in particular to an antivibration ring for an air conditioner motor. Background technique [0002] The anti-vibration ring of the traditional air conditioner motor has the phenomenon of high temperature flow and low temperature cracking. At the same time, the anti-oil and anti-vibration performance is poor, and it is easy to age and the hardness decreases at high temperature and low temperature. Contents of the invention [0003] The object of the present invention is to provide an anti-vibration ring for an air conditioner motor with excellent oil resistance, high temperature and low temperature resistance. [0004] The above purpose is achieved through the following schemes: [0005] An anti-vibration ring for an air conditioner motor, characterized in that it is made of the following raw materials in parts by weight: 1.5-2.5 parts of sulfur powder, 130-150 parts of EPDM rubb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/16C08K13/02C08K3/04C08K3/06C08K3/22C08K3/26C08K5/09C08K5/098H02K5/24
Inventor 汪德成
Owner NINGGUO ZOYE PLASTIC & RUBBER CO LTD