High-light-transmission high-light-shading ABS (acrylonitrile butadiene styrene) material and preparation method thereof

A technology of ABS material and ABS resin, which is applied in the field of high light transmittance, high light shading ABS material and its preparation, can solve the problems of insufficient light transmittance, poor light shading performance, poor astigmatism, etc., and achieve high light transmittance and high product quality. High, low production cost effect

Active Publication Date: 2014-07-16
东莞市银禧光电材料科技股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of ABS resin is that its light transmittance is low
Although the light transmittance of the ABS composite material prepared by this prior art has been improved to a certain extent, the light transmittance is still not high enough, the astigmatism is poor, the haze value is low, and the shading performance is poor, which cannot meet the requirements of the outer cover for LED lighting fixtures. High light transmission and high shading requirements for materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-light-transmission high-light-shading ABS (acrylonitrile butadiene styrene) material and preparation method thereof
  • High-light-transmission high-light-shading ABS (acrylonitrile butadiene styrene) material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] First, put 0.2% antioxidant 1076, 0.3% silicone resin light diffusing agent with a particle size of 1 μm into a high-speed mixer and stir evenly. The stirring speed is 100r / min, and the stirring time is 4min; then add 99.5% East Li company's ABS 920 / 900 resin is mixed in three stages. The stirring speed of the first stage is 20r / min, and the stirring time is 4min. The stirring speed of the second stage is 100r / min, and the stirring time is 4min. The stirring speed of the three-stage stirring is 10r / min, and the stirring time is 3min; finally, the uniformly mixed material is put into a twin-screw extruder for extrusion granulation; the extrusion temperature of the pellet feeding section is 170°C, and the plasticizing section extrudes The temperature is 190°C, the extrusion temperature in the melt delivery section is 190°C, the head temperature is 200°C, and the vacuum degree during extrusion granulation is 0.8MPa.

Embodiment 2

[0043] First put 0.3% antioxidant 168 and 1.3% silicone resin light diffusing agent with a particle size of 2 μm into a high-speed mixer and stir evenly. The stirring speed is 120r / min and the stirring time is 4min; then add 98.4% Chimei The company's ABS 758 resin is mixed in three stages. The stirring speed of the first stage is 25r / min, and the stirring time is 3min. The stirring speed of the second stage is 120r / min, and the stirring time is 3min. The stirring speed is 20r / min, and the stirring time is 2.5min; finally, put the uniformly mixed material into the twin-screw extruder for extrusion and granulation; the extrusion temperature of the pellet feeding section is 175°C, and the extrusion temperature of the plasticizing section is 190°C, the extrusion temperature in the melt conveying section is 190°C, the head temperature is 200°C, and the vacuum degree during extrusion granulation is 0.75MPa.

Embodiment 3

[0045] First put 0.1% antioxidant 1076, 0.1% antioxidant 168, and 2.3% silicone resin light diffusing agent with a particle size of 2 μm into a high-speed mixer and stir evenly. The stirring speed is 140r / min, and the stirring time is 3min; then add 97.5% ABS 920 / 900 resin from Dongli Company and carry out three-stage stirring, the stirring speed of the first stage is 30r / min, the stirring time is 3min, and the stirring speed of the second stage is 140r / min , the stirring time is 3min, the stirring speed of the third stage stirring is 30r / min, and the stirring time is 2min; finally, the mixed homogeneous material is put into a twin-screw extruder for extrusion granulation; the extrusion temperature of the pellet feeding section is 180 °C, the extrusion temperature in the plasticizing section is 195 °C, the extrusion temperature in the melt delivery section is 195 °C, the head temperature is 205 °C, and the vacuum degree during extrusion granulation is 0.7 MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to the technical field of ABS materials, in particular to a high light-transmitting, high-shading ABS material, comprising the following raw material components in mass percentages: 93.0-99.5% ABS resin, 0.1-0.6% antioxidant, 0.1-2.3% organic Silicone resin light diffusing agent; the antioxidant is one or a mixture of antioxidant 1076 or antioxidant 168; the sum of the mass percentages of the above components is 100%. The preparation method is as follows: first put the antioxidant and the silicon-based light diffusing agent into a high-speed mixer and stir evenly, then add ABS resin for three-stage mixing, and finally put the evenly mixed material into a twin-screw extruder for extrusion Pellet out to make ABS material. The ABS material of the present invention has good light astigmatism performance, can achieve the balance of haze and light transmittance at the same time, meets the requirements of the outer cover of LED lighting lamps, has a simple preparation method, and is favorable for popularization and application.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to an ABS material with high light transmission and high light shielding and a preparation method thereof. Background technique [0002] Light-emitting diodes (Light Emitting Diode, LED) are increasingly widely used in the fields of display, transportation, electrical appliances and lighting due to their small size, long life, rich color rendering and outstanding energy-saving and environmental protection characteristics. , one of the key technologies for cleaner production and sustainable development. [0003] Due to its light-emitting characteristics of point light sources and high brightness, LEDs have disadvantages compared with conventional light sources such as strong light, glare, people can't look directly, or can't get soft visual effects in the field of lighting. In order to make up for the lack of application of LED light sources in the field of lighting, it is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L55/02C08L51/00C08L83/04
Inventor 傅轶邓虎招启强谭颂斌
Owner 东莞市银禧光电材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com