Anti-impact diamond layer, diamond composite sheet and preparation method for diamond composite sheet

A technology of diamond composite sheet and diamond layer is applied in the field of superhard material products, which can solve the problems of high brittleness, high hardness of diamond composite sheet, and inability to meet drilling use, etc., so as to improve the footage, reduce the abnormal damage of drill teeth, and reduce cutting. Sharpness effect

Inactive Publication Date: 2012-11-28
河南亚龙金刚石制品股份有限公司
View PDF8 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the disadvantages of high hardness and high brittleness of the existing diamond composite sheet, which cannot meet the needs of drilling under large impact loads, the present invention provides an impact-resistant diamond layer, a diamond composite sheet and a preparation method thereof. The composite sheet prepared by the method has the advantages of strong impact resistance and good sharpness, and is especially suitable for mining and drilling in hard strata.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The impact-resistant diamond composite sheet of this embodiment is prepared by the following steps:

[0033] (1) Ingredients: Weigh the following raw materials according to the following weight ratio: diamond: 76 parts, graphite powder: 19 parts, catalyst: 5 parts; the catalyst is composed of the following weight ratio materials: iron: 59 parts , nickel: 17 parts, cobalt: 10 parts, manganese: 6 parts, silicon: 8 parts.

[0034] (2) Mixing: Pour the material into the mixing tank, then add cemented carbide balls with the same weight and diameter of 8-10mm into the mixing tank as the mixing medium, and install them in a three-dimensional mixer for mixing. Feed time was 4.5 hours.

[0035] (3) Purification treatment: Implant the material obtained in step 2 into a high-temperature furnace for treatment at a temperature of 860° C., a pressure of 50 Pa, and a time of 3.5 hours.

[0036] (4) Assembly: put the material obtained in step 3 into a metal sleeve cup, and then put i...

Embodiment 2

[0042] The impact-resistant diamond composite sheet of this embodiment is prepared by the following steps:

[0043] (1) Ingredients: Weigh the following raw materials according to the following weight ratio: diamond: 77.5 parts, graphite powder: 15 parts, catalyst: 5 parts; the catalyst is composed of the following weight ratio materials: iron: 55 parts , nickel: 20 parts, cobalt: 10 parts, manganese: 10 parts, silicon: 5 parts.

[0044] (2) Mixing: Pour the material into the mixing tank, then add cemented carbide balls with the same weight and diameter of 8-10mm into the mixing tank as the mixing medium, and install them in a three-dimensional mixer for mixing. Feed time was 5.5 hours.

[0045] (3) Purification treatment: Implant the material obtained in step 2 into a high-temperature furnace for treatment at a temperature of 870° C., a pressure of 50 Pa, and a time of 3 hours.

[0046] (4) Assembly: put the material obtained in step 3 into a metal sleeve cup, and then put ...

Embodiment 3

[0052] The impact-resistant diamond composite sheet of this embodiment is prepared by the following steps:

[0053] (1) Ingredients: Weigh the following raw materials according to the following weight ratio: diamond: 79 parts, graphite powder: 10 parts; catalyst: 4.7 parts; the catalyst is composed of the following weight ratio materials: iron: 48 parts , nickel: 16 parts, cobalt: 11 parts, manganese: 16 parts, silicon: 9.6 parts.

[0054] (2) Mixing: Pour the material into the mixing tank, then add cemented carbide balls with the same weight and diameter of 8-10mm into the mixing tank as the mixing medium, and install them in a three-dimensional mixer for mixing. The feeding time is 5 hours.

[0055] (3) Purification treatment: Implant the material obtained in step 2 into a high-temperature furnace for treatment at a temperature of 860° C., a pressure of 20 Pa, and a time of 4 hours.

[0056] (4) Assembly: put the material obtained in step 3 into a metal sleeve cup, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-impact diamond layer, an anti-impact diamond composite sheet and a preparation method for the diamond composite sheet. Coarse granular diamond is used as a main raw material, graphite is used as a filling agent, and iron-based powder is used as an accelerant; the diamond layer comprises the following components in part by weight: 70 to 80 parts of diamond, 10 to 20 parts of graphite powder, and 3 to 12 parts of accelerant; and the accelerant consists of the following materials in part by weight: 45 to 60 parts of iron, 15 to 20 parts of nickel, 5 to 15 parts of cobalt, 5 to 20 parts of manganese, and 3 to 10 parts of silicon. The method comprises the following steps of: mixing the raw materials in the ratio uniformly, pre-pressing the mixture and a hard alloy matrix into a composite sheet, filling into a pyrophyllite block to form a structural block, putting the structural block into a 6-surface diamond presser, sintering and electrolyzing at a high temperature under high pressure, and thus obtaining the diamond composite sheet. The diamond composite sheet has the characteristics of big pores and a mesh connection structure, and is quite suitable for drilling medium hard and hard strata due to excellent sharpness and impact toughness.

Description

[0001] Technical field [0002] The invention involves the field of super hard materials products. It specially involves an impact -resistant diamond layer, diamond composite and its preparation methods. Background technique [0003] Vajrayana composite refers to the addition of a small amount of metal or non -metallic adhesive to diamond particles, which are made by high temperature and high -voltage synthetic composite materials. It has excellent performanceIt has been widely used in the fields of oilfield mining, infrastructure construction, house maintenance, mechanical processing, and geological exploration. With the development of science and technology, it has also become an indispensable key material in high -tech fields such as microelectronics, communication, and aerospace.At present, diamond composite tablets are generally used as the main raw materials, adding a small amount of catalyst catalyst CO, Ni, etc., combined with hard alloy, sintering.Its product is characte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F7/06B22F3/24C25F3/02
Inventor 李富玲王恒陈强花波波方艳娜
Owner 河南亚龙金刚石制品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com