Super-tough green nylon 11 alloy prepared by using in-situ process and preparation method thereof
A green nylon and super-tough technology, applied in the field of materials, can solve the problems of less super-tough green nylon 11 alloy, unsuitable for mass use, strong equipment corrosion, etc., to achieve easy popularization and application, low equipment corrosion, excellent comprehensive performance Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0063] A kind of ultra-tough green nylon 11 alloy, its raw material composition and parts by weight are:
[0064]
[0065] The preparation method of the above-mentioned super-tough super-tough green nylon 11 alloy comprises the following steps:
[0066] (1) Dissolve the initiator dicumyl peroxide (DCP) in glycidyl methacrylate (GMA) to obtain a solution and place it for later use;
[0067] (2) Dry nylon 11 in a vacuum oven at 90°C for 4 hours, and place POE in a vacuum oven at 70°C for 4 hours. After cooling, mix nylon 11 and POE evenly, and then add high-density polyethylene grafted Malay Acid anhydride (HDPE-g-MAH), finally add the solution of step (1) to obtain a premix;
[0068] (3), the premix of step (2) is placed in the parallel twin-screw extruder to melt and extrude, and granulate. ℃, the temperature in the second zone is 190℃, the temperature in the third zone is 200℃, the temperature in the fourth zone is 200℃, the temperature in the fifth zone is 200℃, the tem...
Embodiment 2
[0071] A kind of ultra-tough green nylon 11 alloy, its raw material composition and parts by weight are:
[0072]
[0073] The preparation method of the above-mentioned super-tough super-tough green nylon 11 alloy comprises the following steps:
[0074] Step (1), step (2) are identical with step (1), step (2) of embodiment 1;
[0075] (3), the premix of step (2) is placed in the parallel twin-screw extruder to melt and extrude, and granulate. ℃, the temperature in the second zone is 190℃, the temperature in the third zone is 200℃, the temperature in the fourth zone is 200℃, the temperature in the fifth zone is 200℃, the temperature in the sixth zone is 200℃, the temperature in the seventh zone is 200℃, and the temperature of the die head is 195℃.
Embodiment 3
[0077] A kind of ultra-tough green nylon 11 alloy, its raw material composition and parts by weight are:
[0078]
[0079] The preparation method of the above-mentioned super-tough super-tough green nylon 11 alloy comprises the following steps:
[0080] (1) Dissolve the initiator 2,5-dimethyl-2,5-di-tert-butylperoxyhexane (L-101) in glycidyl methacrylate (GMA) to obtain a solution and place it spare;
[0081] (2) Dry nylon 11 in a vacuum oven at 90°C for 4 hours, and place POE in a vacuum oven at 70°C for 4 hours. After cooling, mix nylon 11 and POE evenly, and then add high-density polyethylene grafted Malay Acid anhydride (HDPE-g-MAH), finally add the solution of step (1) to obtain a premix;
[0082] (3), the premix of step (2) is placed in the parallel twin-screw extruder to melt and extrude, and granulate. ℃, the temperature in the second zone is 190℃, the temperature in the third zone is 200℃, the temperature in the fourth zone is 200℃, the temperature in the fifth ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap