A kind of high barrier property film and preparation method thereof

A technology with high barrier properties and manufacturing methods, which is applied in the direction of chemical instruments and methods, layered products, synthetic resin layered products, etc., can solve the problems of film brittleness, poor toughness, and poor barrier properties, and achieve improved barrier properties and barrier properties. The effect of less drop and good flexibility

Inactive Publication Date: 2016-01-20
厦门长塑实业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, compared with other barrier materials such as PVDC, EVOH, and aluminum-plastic composite films, MXD6 still has the problem of slightly poorer barrier properties.
Moreover, compared with PA6 (polyamide 6 or nylon 6) films, MXD6 also has the characteristics of poor toughness, and the film is brittle if used alone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high barrier property film and preparation method thereof
  • A kind of high barrier property film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Such as figure 1 The high barrier film of the three-layer structure consisting of the first surface layer 1, the core layer 2 and the second surface layer 3 is shown, and the components of the first surface layer 1 are 10wt% of MXD6, 89.6wt% of PA6, 0.2wt% % anti-blocking agent and 0.2wt% slip agent; the above-mentioned core layer 2 consists of 60wt% MXD6, 40wt% PA6; the above-mentioned second surface layer 3 consists of 10wt% MXD6, 89.6wt% PA6, 0.2wt% anti-blocking agent and 0.2wt% slip agent.

Embodiment 2

[0039] Such as figure 1 The high barrier film of the three-layer structure consisting of the first surface layer 1, the core layer 2 and the second surface layer 3 is shown, and the components of the first surface layer 1 are 20wt% of MXD6, 79.4wt% of PA6, 0.3wt% % anti-blocking agent and 0.3wt% slip agent; the above-mentioned core layer 2 consists of 65wt% MXD6, 35wt% PA6; the above-mentioned second surface layer 3 consists of 20wt% MXD6, 79.4wt% PA6, 0.3wt% anti-blocking agent and 0.3wt% slip agent.

Embodiment 3

[0041] Such as figure 1 The high barrier film of the three-layer structure consisting of the first surface layer 1, the core layer 2 and the second surface layer 3 is shown, and the components of the first surface layer 1 are 30wt% of MXD6, 69.5wt% of PA6, 0.3wt% % anti-blocking agent and 0.2wt% slippery agent; the above-mentioned core layer 2 consists of 80wt% MXD6, 20wt% PA6; the above-mentioned second surface layer 3 consists of 30wt% MXD6, 69.5wt% PA6, 0.3wt% anti-blocking agent and 0.2wt% slip agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a high barrier film and a manufacturing method thereof. The high barrier film is a three-layer structure composed of a first surface layer, a core layer, and a second surface layer. The first surface layer is composed of 0-0.3wt% of a slipping agent, 0-0.5wt% of an anti-block agent, 10-40 wt% of MXD6, and 59.2-90 wt% of PA6 chips; the core layer is composed of 60-95 wt% of MXD6, and 5-40 wt% of PA6 chips; and the second surface layer is composed of 0-0.3wt% of a slipping agent, 0-0.5wt% of an anti-block agent, 10-40 wt% of MXD6, and 59.2-90 wt% of PA6 chips. The high barrier film above has greatly improved barrier performance, and has the characteristics of excellent barrier property, low oxygen transmission rate of the film, and good transparency and flexibility.

Description

Technical field: [0001] The invention relates to a film used in the field of packaging and a manufacturing method thereof, in particular to a film with high gas barrier properties and a manufacturing method thereof. Background technique: [0002] In the traditional process, PVDC (polyvinylidene chloride), EVOH (ethylene-vinyl alcohol copolymer), aluminum-plastic composite film and other materials are generally used as barrier packaging materials. Among them, although PVDC has high barrier performance, it is difficult to process and has certain environmental protection problems; EVOH may affect the processing process and the use of end customers due to the problem of hygroscopicity. The performance drops significantly, so the use is limited; although the aluminum-plastic composite film has excellent barrier properties, it has the disadvantage of being opaque, which is obviously limited in the packaging field. [0003] In order to prevent the above problems, the barrier mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/08B32B27/28C08L77/02B29C47/06B29C55/12
Inventor 林凤龙梁文东曾进兴
Owner 厦门长塑实业有限公司