Coating process of environmentally friendly paint on metal surface

A technology of coating and anti-corrosion coatings, which is applied in the direction of anti-corrosion coatings and coatings, and can solve problems such as poor stability of the treatment process

Inactive Publication Date: 2013-02-20
QINGDAO WINTEC SYSTEM CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the presence of strong oxidants, the stability of the treatment process is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Prepare the following components (parts by mass):

[0028] a Bis-(3-(triethoxy)silylpropyl)tetrasulfide 11;

[0029] b propanol 60;

[0030] c SiO 2 Particle 6;

[0031] d Yttrium oxide6;

[0032] e deionized water 26;

[0033] f Triethylamine 3;

[0034] g carbon fiber 8;

[0035] h polyimide 3;

[0036] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 2

[0038] (1) Prepare the following components (parts by mass):

[0039] a Bis-(3-(triethoxy)silylpropyl)tetrasulfide 20;

[0040] b propanol 80;

[0041] c SiO 2 grain 10;

[0042] d Yttrium oxide 10;

[0043] e deionized water 50;

[0044] f triethylamine 5;

[0045] g carbon fiber 10;

[0046] h polyimide 5;

[0047] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

Embodiment 3

[0049] (1) Prepare the following components (parts by mass):

[0050] a Bis-(3-(triethoxy)silylpropyl)tetrasulfide 15;

[0051] b propanol 70;

[0052] c SiO 2 particle 8;

[0053] d Yttrium oxide8;

[0054] e deionized water 38;

[0055] f triethylamine 4;

[0056] g carbon fiber 9;

[0057] h polyimide 4;

[0058] (2) Mix the above components and perform aging treatment, then spray, brush or dip on the surface of the substrate, and form a coating on the surface of the substrate after deposition to achieve surface anti-corrosion treatment.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a coating process of an environmentally friendly paint on a metal surface. The invention discloses a coating method of an anticorrosive paint. The coating method comprises the following steps: mixing such components as siloxane, a solvent, silica particles, a rare earth compound, deionized water, a catalyst, carbon fibers and polyimide, then curing the mixture, then filtering the cured mixture, then spraying, brushing or impregnating the filtered mixture on the surface of a base material and forming a coat on the surface of the base material after deposition, thus achieving anticorrosive treatment of the surface.

Description

technical field [0001] The invention relates to an anti-corrosion paint coating method, in particular to a coating method for an environmentally friendly paint which is suitable for the surface of a metal structure, has excellent gloss and mechanical and physical properties, and does not contain aromatic hydrocarbon solvents. Background technique [0002] In modern industry and daily life, metal corrosion can be seen everywhere, especially in the form of crevice corrosion, stress corrosion and corrosion fatigue in the storage containers of fuel oil and hazardous chemicals, which cause great safety hazards to people's lives. [0003] The metal protection methods currently used can be roughly divided into three categories: one is anodic oxidation treatment, that is, an anodic oxidation film with a thickness of tens of microns is formed on the metal surface, but due to the large energy consumption of the anodic oxidation process and the contamination of the electrolyte solution ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/08C09D179/08C09D7/12C09D5/08
Inventor 殷良策
Owner QINGDAO WINTEC SYSTEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com