Production technology of aluminum alloy sectional bar for automobile bumper
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for aluminum alloy profiles and automobile bumpers, applied in the field of metal machining, can solve the problems of high price, complex molding process, feather crystals, etc., and achieve the effect of eliminating external conditions, chemical composition and temperature uniformity
Active Publication Date: 2014-12-31
丛林铝业科技(山东)有限责任公司
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Automobile bumper is a thin-arm structural part with large surface area and complex shape. It requires excellent high and low temperature impact toughness, rigidity, aging resistance, heat resistance and cold resistance; while the existing automobile bumpers mostly use Preparation of materials such as polyurethane elastomer and ABS. The molding process of these materials is complicated and expensive, which increases the cost of automobiles and increases the burden on buyers; polypropylene materials are widely used in Automotive applications are increasing, but the polypropylene material has low toughness and impact strength, which increases the risk for drivers and passengers, and the gloss and smoothness of the finished surface are poor
[0003] 7NB46 belongs to the Al-Zn-Mg superhard aluminum alloy. Because of its good thermal deformation properties, it has high strength after on-line quenching during extrusion. The product has good welding performance and corrosion resistance, and has a certain resistance to stress corrosion. performance, especially the strong ability to absorb impact and resist folding, so it is especially suitable for extruding into hollow profiles to make automobile bumpers. How to process aluminum alloy profiles with similar or better performance is what we want to solve However, when processing this type of aluminum alloy profiles, defects such as feather crystals often appear in the production process
Feather crystal has a thick and straight crystal axis, and its mechanical properties have strong anisotropy, which not only destroys the process performance but also greatly reduces the mechanical properties
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0030] The present invention is used for the aluminum alloy profile production process of automobile bumper, comprises the following steps;
[0031] (1) Ingredients: Aluminum ingot of 99.85 grade is selected as the base of the alloy. Mg and Zn elements are added in the form of pure metals. Considering that Cu, Cr, Ti, and Zr elements have high melting points and low content in the alloy, they are added in the form of master alloys.
[0032] (2) Smelting: smelting in a 25-ton regenerative gas furnace. Considering that the alloy contains a relatively high Zn content and the melting point of Zr is high, it is easy to produce specific gravity segregation and feather crystals of Zn and Zr, so the following measures are taken: In order to prevent To produce feather crystals, the smelting temperature should not be too high, which is 755°C;
[0033](3) In order to prevent the specific gravity segregation of Zn and Zr, add the Zn ingots into the furnace in three batches with a feeding...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a production technology of an aluminum alloy sectional bar for an automobile bumper and belongs to the technical field of metal machining. The aluminum alloy sectional baral bar for the bumper is processed through the steps of mixing, melting, permanent magnetic stirring, temperature measurement, sampling, ingredient and temperature adjustment, turning down, refining(first purification), standing still, online addition of Al-Ti-B wire, online removal of gas and sand (secondary purification), two-stage filtration, same-level hot top casting, cast ingot homogenization, machining of cast ingot, inspection of cast ingot, heating of cast ingot by an induction furnace, extrusion, precise on-line quenching, stretching and straightening, aging, structure and property inspection of sectional bars, and delivery. The aluminum alloy sectional bar processed by the technology is excellent in thermal deformation performance, and high in strength due to on-line quenching during extrusion. The product has excellent welding performance and corrosion resistance, certain resistance to stress corrosion, and especially has strong shock absorption and folding resistance.
Description
technical field [0001] The invention relates to metal machining, in particular to a production process of aluminum alloy profiles used for automobile bumpers. Background technique [0002] At present, with the rapid development of the automobile industry, people have higher and higher requirements for the cost performance of automobiles. Automobile bumper is a thin-arm structural part with large surface area and complex shape. It requires excellent high and low temperature impact toughness, rigidity, aging resistance, heat resistance and cold resistance; while the existing automobile bumpers mostly use Preparation of materials such as polyurethane elastomer and ABS. The molding process of these materials is complicated and expensive, which increases the cost of automobiles and increases the burden on buyers; polypropylene materials are widely used in Automotive applications are increasing, but the low toughness and impact strength of polypropylene materials increase the ris...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.