High-temperature glisten glaze and preparation method thereof

A flash glaze and high temperature technology, applied in the field of decorative powder for ceramics, can solve the problems of unsatisfactory overall product quality, lack of decorative effect, glaze blistering, etc., achieve flash and color stability, good glaze decorative effect, Delicate glaze effect

Inactive Publication Date: 2013-03-27
威远县大禾陶瓷原料有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The actual situation of the production of architectural ceramics is going to two poles: one is firing at low temperature, which is conducive to energy saving, but the overall quality of its products is not ideal; surface texture
The wear resistance of the glaze surface, its thermal stability, etc.) are much better than the previous one; but because the commonly used flash glaze can only be used at medium and low temperatures, it is used at high temperature, especially for one-time firing, flash It quickly deteriorates and disappears, and the glaze surface is also blistered, which cannot play a decorative effect; therefore, there is an urgent need for a flash that can be used at high temperature, especially at a high temperature for one firing, and can have a good decorative effect on the ceramic glaze surface. glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be described in further detail below in conjunction with specific embodiments.

[0021] The process flow is as follows: raw material entering the factory, inspection, batching, melting, water quenching, inspection, ball milling, inspection, drying, milling, inspection, packaging. According to the following mass percentage ingredients: Al 2 o 3 1~16%, SiO 2 50~75%, CaO 0.5~5%, MgO 0~2%, K 2 O 2~9%, Na 2 O 0~2%, ZnO 2~16%, PbO 0~2%, ZrO 2 3~9%, CeO 2 3~10%, B 2 o 3 0.5~8%. The melting temperature is 1550-1600°C. The fineness of the ball-milled glaze slurry is less than 0.3% (remainder of 325 mesh sieve). The glaze slurry must be dried after the ball milling, and the drying temperature is 150-250°C. The milling parameters are as follows: pulverize through a 250-mesh sieve, and the fineness is <0.3% (325 mesh).

[0022] Experiments were carried out according to the parameters in Table 1, and the results showed that the flash glaze...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature glisten glaze and a preparation method thereof. The glaze comprises, by mass, 1-16% of Al2O3, 50-75% of SiO2, 0.5-5% of CaO, 0-2% of MgO, 2-9% of K2O, 0-2% of Na2O, 2-16% of ZnO, 0-2% of PbO, 3-9% of ZrO2, 3-10% of CeO2 and 0.5-8% of B2O3. The glisten glaze is wide in application range, good in firing performance and high in stability and glisten strength; and the preparation method is reasonable and simple in technology.

Description

technical field [0001] The invention belongs to the field of decorative powder for ceramics, and in particular relates to a high-temperature flash glaze and a manufacturing method thereof. Background technique [0002] The actual situation of the production of architectural ceramics is going to two poles: one is firing at low temperature, which is conducive to energy saving, but the overall quality of its products is not ideal; Surface texture. The wear resistance of the glaze surface, its thermal stability, etc.) are much better than the previous one; but because the commonly used flash glazes can only be used at medium and low temperatures, they are used at high temperatures, especially for one-time firing. The flash will quickly deteriorate and disappear, and the glaze surface will also blister, which will not have a decorative effect; therefore, there is an urgent need for a ceramic glaze that can be used at high temperatures, especially at high temperatures for one firi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 张健胡智敏
Owner 威远县大禾陶瓷原料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com