Modified carcass ply compound of all-steel radial tire

A radial tire and carcass rubber technology, which is applied to special tires, tire parts, transportation and packaging, etc., can solve the problems of reduced adhesion performance, environmental pollution, easy sublimation and smoke, etc., and achieves increased extraction force and reduced loss The effect of factor drop

Inactive Publication Date: 2014-11-26
QINGDAO UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the difficulty of dispersing resorcinol in the m-formazan-white-cobalt adhesion promotion system of the prior art during low-temperature mixing, and the high-temperature mixing is easy to sublimate and emit smoke, which seriously pollutes the environment and affects human health. Moreover, it is easy to cause blooming and reduce the adhesive performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The tackifying resin involved in this example is modified phenolic resin Penacolite B-20-S, its component is 3g, and the remaining components are characterized by (g is the unit measurement) NR 100, carbon black N326 40, white carbon black 10, Peptizer SJ-103 0.2, zinc oxide 6, antioxidant 4020 2, cobalt boroacylate 1, hexamethoxymelamine (HMMM) 5, insoluble sulfur IS7020 4, accelerator DZ 1.25, anti-scorch agent CTP 0.4.

[0016] The two-stage mixing process is used for mixing, and the first stage of mixing is carried out in a 1.5L small internal mixer, adding all small materials such as raw rubber, carbon black, white carbon black, tackifying resin and cobalt boroacylate. The second-stage mixing is carried out on the open mill, and the first-stage mixing rubber, sulfur and accelerator are added, and the next piece is removed. The samples were vulcanized on a flat vulcanizer.

[0017] The Mooney viscosity is tested according to the standard GB / T1232.1-2000, the test t...

Embodiment 2

[0020] The tackifying resin is modified phenolic resin Elaztobond A250, and the rest are the same as in Example 1.

Embodiment 3

[0022] The tackifying resin is phenolic resin TYC-0219, and the rest are the same as in Example 1. Phenolic resin TYC-0219 is a product of Tongyue Chemical (Yangzhou), http: / / www.tong-yue.com / product / 0219.asp.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a modified carcass ply compound of an all-steel radial tire. According to the modified carcass ply compound, resorcin is replaced with phenolic resin. The resorcin is replaced with modified phenolic resin Penacolite B-20-S, modified phenolic resin Elaztobond A250 and phenolic resin TYC-0219, the Mooney viscosity of a sizing material is increased, and the scorch time is prolonged; except for the condition that the resin TYC-0219 enables the vulcanizing time to be prolonged obviously, and little difference of other resin exists; the tensile strength and the stretching stress of vulcanized rubber are reduced slightly, and other physical and mechanical properties are not changed much; and storage moduli and loss factors are all reduced; and the drawing force between the sizing material and a coppered steel wire is increased obviously.

Description

technical field [0001] The invention relates to an improved all-steel radial tire carcass rubber by using phenolic resin instead of resorcinol. Background technique [0002] All-steel radial tires are made of steel cord for the belt layer and carcass layer, and are generally medium-duty truck tires and light-duty truck tires. It mainly has the following advantages: 1) wear-resistant, puncture-resistant, durable, high mileage and long service life; 2) small rolling resistance, low fuel consumption, low heat generation, energy saving and reduced exhaust emissions; 3) high-speed safety, reduced Comfortable vibration and stable handling [0003] Steel wire has been widely used as a skeleton material in the belt layer and carcass layer of radial tires. In order to improve the adhesion between steel wire and rubber, the surface is generally treated with brass plating. During vulcanization, the sulfur in the compound reacts with zinc oxide and copper oxide on the surface of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L61/14C08L61/06C08K13/02C08K3/04C08K3/36C08K3/22C08K5/55C08K5/3492C08K3/06B60C1/00
Inventor 孙洪广曲晓
Owner QINGDAO UNIV OF SCI & TECH