Metal antirust agent containing ammonium molybdate

A technology of metal antirust agent, ammonium molybdate, which is applied in the field of metal antirust, can solve the problems of inability to form antirust protection, and achieve good gas phase antirust effect, good gas phase antirust effect, and excellent contact antirust performance

Active Publication Date: 2013-04-10
广州市昌东化工工程材料有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing anti-rust agents are all composed of base oil and oil-soluble corrosion inhibitors, which can only play the function of contact anti-rust, and cannot form effective anti-rust protection for those parts that are not in contact with the anti-rust agent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal antirust agent containing ammonium molybdate
  • Metal antirust agent containing ammonium molybdate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] A kind of metal rust inhibitor containing ammonium molybdate, it is made by the raw material of following parts by weight (kg):

[0020] Castor oil 95, ferrocene 1.8, polyisobutene 1.2, ammonium molybdate 1.2, sodium diacetate 1.8, 2-methylimidazoline 1.1, diethanolamine 1.2, dialkylzinc dithiophosphate 0.7, dodecylbenzene Sodium sulfonate 1.1, polydimethylsiloxane 1.2, film-forming resin 5.7, modified kaolin 1;

[0021] The film-forming resin is prepared from the following raw materials in parts by weight: rosin 6, urea 2, zinc powder 1, dimethyl silicone oil 3, liquefied paraffin 10, 3-aminopropyltrimethoxysilane 3, acetylcitric acid Tris (2-ethylhexyl) ester 12, epoxy linseed oil 15, xylene 10, polyvinyl alcohol 5;

[0022] The preparation method of the modified kaolin is as follows: kaolin is soaked with 15% hydrochloric acid for 3 hours, washed with deionized water, then soaked with 11% hydrogen peroxide solution for 3 hours, then washed with deionized water unt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a metal antirust agent containing ammonium molybdate. The metal antirust agent is prepared from the materials in parts by weight: 95-105 parts of castor oil, 1.2-2.4 parts of ferrocene, 0.8-1.6 parts of polyisobutene, 1-2 parts of ammonium molybdate, 1.3-2.5 parts of sodium diacetate, 0.8-1.6 parts of 2-methyl imidazoline, 1-1.8 parts of diethanol amine, 0.3-0.9 parts of dialkyl group phosphorodithioic acid, 0.7-1.2 parts of sodium dodecyl benzene sulfonate, 0.9-1.7 parts of polydimethylsiloxane, 5.2-6.4 part6s of film-forming resin and 1-2 parts of modified kaolin. The metal antirust agent has excellent contact antirust performance and good gas phase antirust effect, and has good gas phase antirust effect and contact antirust effect to coppers and brass.

Description

technical field [0001] The invention relates to the technical field of metal antirust, in particular to a metal antirust agent containing ammonium molybdate. Background technique [0002] Corrosion is one of the main forms of damage to metal products. According to statistics, the annual direct economic loss caused by metal corrosion accounts for about 2%-4% of the total output value of the national economy. the [0003] In order to avoid corrosion and reduce losses, people have adopted various methods, and using antirust agents to protect metal products is one of the most common protection methods at present. Antirust agent grease is composed of one or more antirust additives (also known as oil-soluble corrosion inhibitors) and auxiliary additives added to the basic components of petroleum. It is easy to use, low in cost, good in effect, and simple in operation. Metalwork industries are heavily used. However, the existing anti-rust agents are all composed of base oil and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/02
Inventor 朱再清
Owner 广州市昌东化工工程材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap