Graphite oxide-cadmium sulfide compounds applied to electrode materials

An electrode material, cadmium sulfide technology, applied in the direction of material electrochemical variables, hybrid capacitor electrodes, measuring electricity, etc., can solve problems such as danger, and achieve the effect of good electrochemical performance

Inactive Publication Date: 2015-07-08
LIAOCHENG UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technology has the following defects or deficiencies: it uses toxic drug dimethyl sulfoxide in its preparation process, which is more dangerous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphite oxide-cadmium sulfide compounds applied to electrode materials
  • Graphite oxide-cadmium sulfide compounds applied to electrode materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1 A preparation method of graphite oxide-cadmium sulfide composite applied to electrode material, the preparation steps are:

[0029] (1) Preparation of graphite oxide: graphite powder was used as raw material to prepare graphite oxide by Hume method, centrifugally washed with secondary water, and then placed in a vacuum drying oven at 60 °C for 24 h to obtain dry graphite oxide;

[0030] (2) Preparation of microemulsion: add 20 mg of graphite oxide, 30 mL of cyclohexane, 4 mL of Triton X-10(OP), 0.4 g of hexadecyltrimethyl into a 100 mL conical flask Ammonium Bromide (CTAB) and 2 mL CdCl 2 solution, and then vigorously stirred for 15min to obtain A solution. CdCl in A 2 Change to Na 2 S, and then vigorously stirred for 15 min to obtain liquid B. After A / B is mixed, stir slightly to obtain an inverse microemulsion system;

[0031] (3) Preparation of graphite oxide-cadmium sulfide composite by hydrothermal method: transfer the microemulsion into a 100 m...

Embodiment 2

[0033] Example 2 A preparation method of a graphite oxide-cadmium sulfide composite applied to an electrode material, the preparation steps are as in Example 1, but the difference is that in Example 1, the ratio of the amount of graphite oxide to the amount of cadmium salt is 1:1, In Example 2, the ratio is 2:1.

Embodiment 3

[0034] Example 3 A preparation method of a graphite oxide-cadmium sulfide composite applied to an electrode material, the preparation steps are as in Example 1, but the difference is that in Example 1, the ratio of the amount of graphite oxide to the amount of cadmium salt is 1:1, In Example 2, the ratio was 5:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses graphite oxide-cadmium sulfide compounds applied to electrode materials and a preparation method thereof. As is confirmed by an experiment, the compounds have good electrochemical performance. The method is simple in process and easy to operate, and the preparation method avoids pollution to the environment to the maximum. The preparation technology is green and environment-friendly, and the prepared compounds serving as the electrode materials have wide application prospect in the field of supercapacitors.

Description

technical field [0001] The invention relates to the technical field of inorganic synthesis of electrode materials, in particular to a method for preparing graphite oxide-cadmium sulfide composites applied to electrode materials. Background technique [0002] Energy is the material basis for the existence and development of human society and the driving force for the operation of the social and economic system. In the new century, our country is facing the problems of energy supply security and economic security. Under such a severe energy situation, various new energy sources need to be developed urgently. Among them, supercapacitors have attracted extensive attention of researchers at home and abroad because of their excellent pulse charge and discharge performance and large-capacity energy storage performance that traditional capacitors do not have. Including metal sulfides with excellent electrochemical properties, metal oxides and their composite materials are all rega...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/30H01G11/86G01N27/48G01R31/00
Inventor 邵鑫王敏刘凤珍刘雪华孟宪华
Owner LIAOCHENG UNIV