Lightweight aluminum alloy material and preparation method thereof
A lightweight, aluminum alloy technology, applied in the field of preparation of aluminum alloy lightweight materials, can solve the problems of being unsuitable for automobile load-carrying, and achieve the effect of broadening the application of new fields
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
specific Embodiment approach 1
[0014] Embodiment 1, an aluminum alloy lightweight material, characterized in that the weight percentage of the components is: Mg: 2%, Zn: 4%, Mn: 0.1%, Cr: 0.2%, Cu: 0.4%, Ti: 0.18%, Si≤0.25%, Fe≤0.4%, single impurity≤0.05%, total impurity≤0.15%, the balance is aluminum.
[0015] A method for preparing an aluminum alloy lightweight material, characterized in that it comprises the following steps:
[0016] ①At a temperature of 720-740°C, put each raw material into the flame furnace for melting according to the formula;
[0017] ②At a temperature of at least 720°C, inject common refining agents with argon gas and refine for 10-20 minutes;
[0018] ③After melt refining and removing scum on the surface, sprinkle sodium modifier evenly, then stir it into the melt, and let it stand for 10-20 minutes;
[0019] ④Semi-continuous direct water-cooled casting, casting temperature: 715-730°C, casting speed: 20-40mm / min, cooling water pressure: 0.03-0.06Mpa;
[0020] ⑤ The ingot should ...
specific Embodiment approach 2
[0022] Specific embodiment two, an aluminum alloy lightweight material, characterized in that the weight percentage of the composition is: Mg: 2.2%, Zn: 3.9%, Mn: 0.5%, Cr: 0.3%, Cu: 0.4%, Ti: 0.15%, Si≤0.25%, Fe≤0.4%, single impurity≤0.05%, total impurity≤0.15%, the balance is aluminum.
[0023] A method for preparing an aluminum alloy lightweight material, comprising the steps of:
[0024] ①At a temperature of 720-740°C, put each raw material into the flame furnace for melting according to the formula;
[0025] ②At a temperature of at least 720°C, inject common refining agents with argon gas and refine for 10-20 minutes;
[0026] ③After melt refining and removing scum on the surface, sprinkle sodium modifier evenly, then stir it into the melt, and let it stand for 10-20 minutes;
[0027] ④Semi-continuous direct water-cooled casting, casting temperature: 715-730°C, casting speed: 20-40mm / min, cooling water pressure: 0.03-0.06Mpa;
[0028] ⑤ The ingot should be homogenized ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com