High-quality flax staple fiber processing method

A processing method and short fiber technology, applied in fiber treatment, plant fiber, textiles and papermaking, etc., can solve the problems of insufficient spinnability of flax short fiber, failure to meet technical requirements, serious fiber damage, etc. Improve spinnability, improve market competitiveness, and reduce damage to fiber strength

Inactive Publication Date: 2014-09-03
QIQIHAR UNIVERSITY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention method with the application number 97104800.2 is characterized in that it uses a strong alkali to process the fibers, which not only seriously damages the fibers, makes the hand feel rough and hard, but also seriously pollutes the waste water, and the spinnability of the flax short fibers is not improved well enough, and the splitting degree of the finished product is not good enough. It is 1100-1300 Nm, which cannot meet the technical requirements of yarns for weft-knitting single jersey on circular knitting machines

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Process flow of the present invention:

[0019] (1) Pretreatment: bath ratio 1:20, fatty alcohol polyoxyalkyl ether 1.5 g / L, room temperature, time 1 h;

[0020] (2) Scouring: liquor ratio 1:20, temperature 98°C, time 40 min, sodium bicarbonate 4.5g / L, sodium sulfite 3.0 g / L, iminodisuccinic acid 3.5 g / L, urea 5.0g / L;

[0021] (3) Hot water washing: 80-90°C;

[0022] (4) Washing in cold water: 20-30°C;

[0023] (5) Dehydration;

[0024] (6) Drying: 100~105℃ to constant weight;

Embodiment 2

[0026] Process flow of the present invention:

[0027] (1) Pretreatment: bath ratio 1:20, fatty alcohol polyoxyalkyl ether 1.5 g / L, room temperature, time 1 h;

[0028] (2) Scouring: liquor ratio 1:20, temperature 98°C, time 45 min, sodium bicarbonate 5.0 g / L, sodium sulfite 1.5 g / L, iminodisuccinic acid 1.5 g / L, urea 7.0 g / L;

[0029] (3) Hot water washing: 80-90°C;

[0030] (4) Washing in cold water: 20-30°C;

[0031] (5) Dehydration;

[0032] (6) Drying: 100~105℃ to constant weight;

Embodiment 3

[0034] Process flow of the present invention:

[0035] (1) Pretreatment: bath ratio 1:20, fatty alcohol polyoxyalkyl ether 1.7 g / L, room temperature, time 1 h;

[0036] (2) Scouring: liquor ratio 1:20, temperature 98°C, time 45 min, sodium bicarbonate 4.5g / L, sodium sulfite 2.0 g / L, iminodisuccinic acid 2.0 g / L, urea 6.5 g / L;

[0037] (3) Hot water washing: 80-90°C;

[0038] (4) Washing in cold water: 20-30°C;

[0039] (5) Dehydration;

[0040] (6) Drying: 100~105℃ to constant weight;

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-quality flax staple fiber processing method. The high-quality flax staple fiber processing method adopts flax staple fibers as the raw materials and comprises the steps of pretreatment, boiling off, hot water washing, cold water washing, dehydration and drying. The method has the advantages that a weak base and an environment-friendly auxiliary are adopted to remove most of impurities such as pectin, lignin and the like, the selected auxiliary is non-toxic, tasteless, low in cost, good in impurity removal effect, and excellent in biodegradablity without causing wastewater pollution, and the damage to the strength of the fibers caused by a strong base, high temperature and high pressure in the traditional process is solved, and furthermore, the processing procedure is shortened. The processing method is capable of obviously improving the split degree and the uniformity of the flax staple fibers, enhancing the whiteness and the flexibility thereof and improving the spinnability. The split degree of the processed flax staple fiber finished product can achieve 1800 Nm, the average length thereof is 65mm, the breaking force thereof is 112-122cN, and the elongation thereof is 4.6-5.0%; therefore, the technical requirements of the production of flax yarns for circular machine weft knitted single jersey are well met.

Description

technical field [0001] The invention relates to a processing method of high-quality flax short fiber, which belongs to the technical field of textile technology. Background technique [0002] Linen fabric is hygroscopic, breathable, antibacterial, deodorant, comfortable to wear and has health care functions. Because flax short fiber contains more lignin and pectin impurities, its splitting degree and softness are far lower than that of long flax, so the scope of use is limited to weaving middle and low-grade products. And because of its high crystallinity and high rigidity, traditional linen yarn can only be used for weaving on weaving and knitting flat knitting machines. According to investigation, adopt this processing method, be made of flax staple fiber and be suitable for knitting circular machine weft knitting single jersey yarn and there is no report at present in domestic and foreign data. The invention method with the application number 97104800.2 is characterized...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/53D06M11/76D06M11/54D06M13/432D06M13/325D06B21/00D06M101/06
Inventor 高洁赵欣姜楠唐文清王高扬马中华郝成成
Owner QIQIHAR UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products