Carboxyl containing organic matter assisted preparation method for metal and high-dispersion metal catalyst
A metal catalyst, high dispersion technology, applied in metal/metal oxide/metal hydroxide catalysts, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of complex catalyst preparation process and high viscosity
Active Publication Date: 2013-06-26
SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY
View PDF6 Cites 24 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, using this sol-gel method, the preparation process of the catalyst is too complicated
Moreover, due to the relatively high viscosity of the sol precursor after chelation of citric acid and metal cations, it cannot completely diffuse into the pores of the carrier core, resulting in the prepared metal can only be loaded on the surface of the carrier, forming a core-shell structure ,like figure 1 shown
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
preparation example
[0021] Preparation of metals, alloys / composite oxides: select one or more of the above-mentioned ones containing metals, noble metals and alloys (such as Cu, Ag, Au, Ni, Pt, Pd, Co, Rh, Ir, Fe, Ru) precursor salts and one or more salt precursors containing K, Ca, Ti, V, Cr, Mn, Zn, Zr, Al, Y, Mo and La, Ce and other lanthanide rare earth elements The body needs to be physically mixed according to different molar ratios. After uniform solid phase grinding at room temperature, it can be mixed with organic acids containing carboxyl groups (such as formic acid, acetic acid, propionic acid, oxalic acid, citric acid, glycine, EDTA, or amino acids, etc. ) or glucose (cellulose) is physically mixed according to the molar ratio of 1 / 1 to 1 / 3, and the pH range is adjusted to 1.0-7.0 by using ammonia water. The powdery precursor formed after drying at 120 ° C for 10 h, in an inert atmosphere (such as argon or nitrogen) conditions, calcined at a temperature range of 300-500°C (Cu, Ag, Au ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
A carboxyl containing organic matter assisted preparation method for metal and high-dispersion metal catalyst relates to a preparation method for high-dispersion supported nanometer metal catalyst, and includes the steps of preparing metal and corresponding alloy, preparing metal, alloy / composite oxide, and preparing high-dispersion metal, alloy / carrier supported metal catalyst. The whole preparation process does not generate waste water, and is environment-friendly. When metal salt and an organic acid chelate precursor containing carboxyl is resolved under the condition of inert atmosphere, reducing gases are released slowly, such as CH4, CO and H2, the reducing gases can reduce metal cations in a chelate as in-situ reducing agent to directly obtain pure metal and alloy, an extra reducing process is not needed, and energy is saved. High-dispersion metal Co / SiO2 catalyst prepared through the method is applied to Fischer-Tropsch synthesis reaction, and the reactivity of the high-dispersion metal Co / SiO2 catalyst prepared through the method is four times as high as that of the high-dispersion metal Co / SiO2 reducing catalyst prepared through a traditional dipping method.
Description
technical field [0001] The invention relates to a method for preparing a highly dispersed supported nanometer metal catalyst, in particular to a method for assisting the preparation of a metal and a highly dispersed metal catalyst by a carboxyl group-containing organic substance. Background technique [0002] A new sol-gel method involving citric acid is reported for the first time in the existing literature to directly prepare metal Cu / ZnO catalysts and highly dispersed metal Co / SiO 2 Supported catalysts without the need for additional reducing conditions. The prepared metal Cu / ZnO and Co / SiO 2 The catalyst is directly used in low-temperature methanol synthesis and Fiercher synthesis reactions. (Literature: 1.Study on the preparation of Cu / ZnO catalyst by sol-gel auto-combustion method and its application for low-temperature methanol synthesis. L. Shi , K. Tao, R.Q. Yang, F.Z. Meng, C. Xing, N. Tsubaki, Applied Catalysis A: General 401 (2011) 46-55; 2. Surface impregnati...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/22B01J37/16B01J23/75
Inventor 石磊椿范立肖林久
Owner SHENYANG INSTITUTE OF CHEMICAL TECHNOLOGY