A stainless steel, high-brightness technology, applied in the direction of lubricating compositions, additives, petroleum industry, etc., can solve problems such as insufficient lubrication, loss of lubricating effect of lubricants, affecting mechanical properties of wires, etc., achieves stable and uniform hardness and strength, and improves affinity and lubricity, value-enhancing and profit-enhancing effects

Active Publication Date: 2014-06-18
GUANGDONG YATAI NEW MATERIAL TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the lubricants for stainless steel wire drawing are single wire drawing powder and liquid wire drawing oil, mainly graphite and calcium soap lubricants. In graphite lubricants, minerals are used as the medium. When drawing, the oil is exhausted. The lubricant loses its lubricating effect, forms foam and agglomerates, and has poor stability. The surface of the drawn wire is not bright, and it will cause varying degrees of damage to the wire drawing die, reducing the service life of the die. The temperature is very high and the degree of lubrication is not enough, which greatly affects the mechanical properties of the wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Aqueous graphite was purchased from Qingdao Runba Graphite Products Co., Ltd.

[0013] Water intake: 60g graphite, 24g linear alkylbenzene sulfonate sodium 24g, sodium lauryl sulfate 15g, α-olefin sulfonate 12g, fatty alcohol polyoxyethylene ether sodium sulfate 15g, alkyl alcohol amide 6g and alkyl glycoside 12g.

[0014] The above-mentioned components are mixed and stirred uniformly to obtain a new type of high-brightness environmentally friendly stainless steel wire drawing lubricant.

[0015] The matte stainless steel wire with a diameter of φ0.90~6.00mm and a tensile strength of 700MPa~1500MPa has a single-pass drawing reduction rate of 7%-23%, and the temperature of the inner surface of the mold reaches 400-600 degrees during drawing. , The new high-brightness environmentally friendly stainless steel wire drawing lubricant prepared in this embodiment can greatly reduce the temperature of the mold surface, and the temperature of the mold surface can be reduced to 60°C. T...

Embodiment 2

[0019] Aqueous graphite was purchased from Qingdao Runba Graphite Products Co., Ltd.

[0020] Water intake agent graphite 85g, linear alkyl benzene sulfonate 30g, sodium lauryl sulfate 20g, alpha-olefin sulfonate 13g, fatty alcohol polyoxyethylene ether sodium sulfate 17g, alkyl alcohol amide 8g and alkyl glycoside 18g.

[0021] The above-mentioned components are mixed and stirred uniformly to obtain a new type of high-brightness environmentally friendly stainless steel wire drawing lubricant.

[0022] The matte stainless steel wire with a diameter of φ0.90~6.00mm and a tensile strength of 700MPa~1500MPa has a single-pass drawing reduction rate of 7%-23%, and the temperature of the inner surface of the mold reaches 400-600 degrees during drawing. , The new high-brightness environmentally friendly stainless steel wire drawing lubricant prepared by this embodiment can greatly reduce the temperature of the mold surface, the temperature of the mold surface can be reduced to 40 ℃, the wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel high-brightness environment-friendly stainless steel wire drawing lubricant. The novel high-brightness environment-friendly stainless steel wire drawing lubricant comprises the following components calculated based on 100 percent of total mass fraction: 60 to 85 percent of water graphite and 15 to 40 percent of composition, the composition comprises the following components according to the total mass fraction of 100 percent: 24 to 30 percent of sodium n-alkyl benzene sulfonate, 15 to 20 percent of lauryl sodium sulfate, 12 to 13 percent of AOS, 15 to 17 percent of fatty alcohol polyoxyethylene lauryl ether sulfate sodium, 6 to 8 percent of alkyl alcohol amine and 12 to 18 percent of alkyl glycoside. The high-brightness environment-friendly stainless steel wire drawing lubricant is high-temperature-resisting, friction-resisting, antioxidant, self-lubricating, good in ventilation and free from smoke and toxicity and can improve the appetency and lubrication performance for the metal surface, the surface brightness of a drawn product is high, the fineness is good, no electrolysis is needed, the environmental pollution can be reduced, the hardness and strength of a stainless steel wire can be stable and uniform, and the stainless steel wire can be used as a bus blank for a subsequent top-grade deep processing product.

Description

Technical field [0001] The invention relates to a lubricant, in particular to a new type of high-brightness environment-friendly stainless steel wire drawing lubricant. Background technique [0002] At present, the lubricant for drawing stainless steel wire is a single drawing powder and liquid drawing oil, mainly graphite and calcium soap lubricants. In the graphite lubricant, minerals are used as the medium. The oil is exhausted during drawing. The lubricant loses its lubricating effect, forms foam and agglomerates, has poor stability, and the drawn wire surface is not bright, and it will cause varying degrees of damage to the drawing die, reducing the service life of the die. The temperature is high and the lubricity is not enough, which greatly affects the mechanical properties of the wire. Summary of the invention [0003] The purpose of the present invention is to provide a new type of high-brightness environmentally friendly stainless steel wire drawing lubricant with high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M161/00C10M129/20C10N40/24C10N30/06
Inventor 朱增余罗国伟吕汪华翟秀凤朱丹丹
Owner GUANGDONG YATAI NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap