Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Multi-component copolymerized petroleum resin and its preparation method

A petroleum resin and multi-component copolymerization technology, applied in the field of multi-component copolymerized petroleum resin and its preparation, can solve the problems affecting the application and deep processing of petroleum resin, poor solubility and compatibility of thermally polymerized petroleum resin, and achieve good solubility and compatibility. Capacitive, low cost, simple process effect

Active Publication Date: 2015-09-09
TIANJIN DELAN WEICHENG BIOLOGICAL TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there are also some problems. At present, the thermally polymerized petroleum resin produced by the existing method has poor solubility and compatibility, especially insoluble in aliphatic hydrocarbon solvents, which directly affects the subsequent application and deep processing of this type of petroleum resin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of multi-component copolymerized petroleum resin, adding 200 g of inert solvent to the autoclave according to the ratio of parts by weight, the inert solvent of this embodiment uses toluene; 100 g of cyclopentadiene derivatives, the cyclopentadiene derivative Dicyclopentadiene and 100 g of aliphatic conjugated diene are used. In this embodiment, the aliphatic conjugated diene is butadiene and 100 g of aromatic olefin is used. In this example, styrene is used as the aromatic olefin, and 100 g of monoolefin is used. In this example, isobutylene is used as the monoolefin to form a mixed solution; the nitrogen is replaced twice, and the mixed solution is heated, and the temperature is slowly raised to 200 ° C. The pressure in the reactor is controlled at less than 3 MPa. React under this condition for 20 hours, and after the reaction is over, distill under reduced pressure to obtain a multi-component copolymerized petroleum resin.

[0029] The invention...

Embodiment 2

[0032] A preparation method of multi-component copolymerized petroleum resin, adding 600g of inert solvent to the high-pressure reactor according to the ratio of parts by weight, the inert solvent of this embodiment adopts No. 200 solvent oil, and 700g of cyclopentadiene derivatives The alkene derivatives are methyl dicyclopentadiene, 500g of aliphatic conjugated diene, the aliphatic conjugated diene in this embodiment is piperylene, 300g of aromatic olefin, the aromatic olefin in this embodiment is methyl styrene, mono 300g of olefin, the monoolefin in this example is isopentene, form a mixed liquid, replace with nitrogen 3 times, heat the mixed liquid, slowly raise the temperature to 280°C, control the pressure in the reactor to less than 3MPa, and react under this condition for 3 hours , After the reaction is over, it is distilled under reduced pressure to obtain a multi-component copolymerized petroleum resin.

[0033] The invention discloses a multi-component copolymerize...

Embodiment 3

[0035] A preparation method of multi-component copolymerized petroleum resin, adding 0.4Kg of an inert solvent to the autoclave according to the ratio of parts by weight, the inert solvent of this embodiment adopts a mixture of solvent D40 and nonane with a weight ratio of 1: 1, cyclopentadiene Derivatives 0.4Kg, the present embodiment cyclopentadiene derivatives adopt the mixture that the weight ratio between methyldicyclopentadiene and norbornene is 3: 1, the aliphatic conjugated diolefin 0.3Kg, the present embodiment aliphatic The conjugated diene uses a mixture of isoprene and piperylene in a weight ratio of 1:2, and the aromatic olefin is 0.16Kg. The aromatic olefin in this embodiment uses a weight ratio between α-methylstyrene and methylindene of 2: 1 mixture, 0.15Kg of monoolefin, the mixture of n-pentene and cyclopentene in weight ratio of 1: 1 is used as monoolefin in this embodiment to form a mixed solution, nitrogen replacement is performed 3 times, and the mixed sol...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for a multicomponent copolymer petroleum resin. The preparation method comprises: according to a weight part ratio, adding an inert solvent, a cyclopentadiene derivative, an aliphatic conjugated diolefin, an aromatic olefin and a monoolefine into a high pressure reaction still to form a mixture liquid, replacing with nitrogen for 2-3 times, heating the mixture liquid, slowly heating to 200-280 DEG C, controlling the reaction still pressure of less than 3 MPa, under the condition, reacting for 3-20 hours, after finishing the reaction, and carrying out reduced pressure distillation to obtain the multicomponent copolymer petroleum resin. The preparation method has simple process and low cost, allows the obtained resin to have good solubility and compatibility, and is the safe and reliable preparation method for the multicomponent copolymer petroleum resin.

Description

technical field [0001] The invention belongs to the field of petrochemical industry, in particular to a multi-component copolymerized petroleum resin and a preparation method thereof. Background technique [0002] Petroleum resin is a low-molecular-weight thermoplastic resin obtained by polymerization of by-products C5 and C9 in the process of petroleum cracking as the main raw material. Petroleum resins can be divided into C5 petroleum resins according to different sources of raw materials, that is, aliphatic petroleum resins, which mainly use piperylene in the C5 fraction obtained from olefin cracking as the main raw material; C9 petroleum resins, that is, aromatic petroleum resins, It is mainly based on the aromatic olefins in the C9 fraction as the main raw material; C5 / C9 petroleum resin is a mixed resin that is polymerized after mixing C5 raw materials and C9 raw materials. Dicyclopentadiene petroleum resin is a resin made from dicyclopentadiene in the C5 fraction as ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F240/00
Inventor 刘伟付红光
Owner TIANJIN DELAN WEICHENG BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com