Colloid acid system for acid fracturing of carbonate reservoir and preparation method thereof

A technology of carbonate rock storage and jelly acid, which is applied in the direction of drilling compositions, chemical instruments and methods, etc. It can solve the problems of fast reaction speed of acid rock, short retention time of high viscosity process, inability to effectively reduce formation condition filtration loss, etc. question

Active Publication Date: 2013-10-30
PETROCHINA CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] 1) Under the temperature conditions of deep wells and ultra-deep wells, the reaction speed of acid rock is fast, which is not conducive to the deep penetration of acid liquid;
[0013] 2) The viscosity of the acid solution is limited, which is not enough to effectively reduce the fluid loss of the acid solution
In particular, the acid liquid has poor high-temperature shear resistance, and the retention time of the high-viscosity process is short, which cannot effectively reduce the filtration loss under formation conditions.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colloid acid system for acid fracturing of carbonate reservoir and preparation method thereof
  • Colloid acid system for acid fracturing of carbonate reservoir and preparation method thereof
  • Colloid acid system for acid fracturing of carbonate reservoir and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] amino acid preparation

[0031] ①Under high-speed stirring, slowly and evenly add the powdered CYY-160 gelling agent into the acid solution. Since the gelling agent is a high-molecular polymer, pay attention to avoid forming lumps (fish eyes), and stir for 2 hours (200ml is a batch);

[0032] ②Let the acid stand for at least 16-24 hours for hydration;

[0033] ③ Add 1% CYY-1 cross-linking agent or first add 1% cross-linking retarder CYY-3 and then add 1% CYY-1 cross-linking agent.

Embodiment 2

[0035] Preparation of finished acid: 20% HCl + 0.8% CYY-160 + 1% CYY-1 cross-linking agent + 1% CYY-3 cross-linking retarder.

[0036] The 6300 reciprocating capillary viscometer of Chandler Company was used to measure the rheological properties of finished acid. The detection principle is: normal temperature -90 ℃ shear rate 40s -1 ;90℃-140℃ shear rate 170s -1 .

[0037] 90℃-140℃, the shear rate is 170s -1 test results:

[0038] Table 2-2-9 Viscosity temperature data of formula 190℃-140℃

[0039]

Embodiment 3

[0041] Preparation of finished acid: 20% HCl + 0.8% CYY-160 + 1% CYY-1 cross-linking agent + 1% CYY-3 cross-linking retarder.

[0042] The reaction rates of ordinary hydrochloric acid and jelly acid were measured with a rotary rock instrument.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a colloid acid system for the acid fracturing of a carbonate reservoir and a preparation method thereof. The colloid acid system is characterized by being prepared by adding 0.8% of CYY-160, 1% of CYY-1 cross-linking agent and 1% of CYY-3 cross-linking retarder in HCl with the mass concentration of 20% in terms of the weight of HCl with the mass concentration of 20% as 100%, wherein the CYY-160 is a copolymer of 2-sulfoacrylamide-methylpropanesulfonic acid and N,N-dimethacrylamide; the CYY-1 is a compound of zirconium acetate, zirconium lactate and zirconium oxide; the CYY-3 is one of citric acid and lactic acid; and under a condition of 90 DEG C, the viscosity of a basic acid of the colloid acid system is more than 1000 mPa.s, the retardant rate is more than 85%, and the viscosity of gel breaking liquid is less than 15 mPa.s.

Description

technical field [0001] The invention relates to an acid liquid system applied to acid fracturing reformation of carbonatite reservoirs and its preparation. Background technique [0002] The deep acid fracturing technologies used in deep acid fracturing of carbonate reservoirs can be summarized into the following technical series. [0003] 1) Gelled acid (thickened acid) acid fracturing technology [0004] The optimal viscosity of thickening acid in the ground is generally around 25mPa.S-30mPa.S, and the flowback viscosity of residual acid is generally between 5mPa.S-14mPa.S, which is easy to flow back and can carry the residual acid in formation fractures after reaction. solid particles. [0005] 2) Slow acid process technology [0006] Chemical retarded acid is a conventional acid added with surfactant. This system has a large fluid loss and is mainly suitable for medium and low temperature dolomite reservoirs. Due to the poor control of fluid loss, this technology is c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/74
Inventor 袁飞王斌成一张健强
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com