Firing technology of insect wing crafts with skin texture characteristics

A technology of crafts and insects, which is applied in the field of firing crafts of insect wings with translucent covering texture, to achieve the effect of rich artistic expression

Active Publication Date: 2013-11-27
郑剑峰
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the different glaze changes of high-temperature glazes during the firing process, the superimposed effect of glazes is used, especially the light-colored or transparent-effect colored glazes are placed on the dark-colored high-temperature glazes, which form during the high-temperature firing process. There is no report on the glazing method of the special mixed glaze change effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The firing process of the "Zen Realm" ceramic cup is as follows:

[0015] Take an existing commercially available low-temperature teacup pottery body with a diameter of about 6cm. The embryo body is fired at a low temperature of 450-550°C; the head, body and feet of the insect are outlined on the pottery body with a dark copper-colored high-temperature glaze; The light-colored bean green high-temperature glaze is used to draw the wings of insects, and the glaze and the dark glaze form partial overlapping coverage. At the same time of drawing, according to the design requirements of the work, the thick characteristics of the glaze are used to create texture effects; according to the high-temperature crystallization The formation and transformation of the phase and the characteristics of the embryo are fired between 1300 ° C and 1400 ° C until the single-color glaze and the mixed-color glaze have different glaze change effects, and the dark single-color glaze is covered wi...

Embodiment 2

[0017] The firing process of the "Zen Realm" ceramic cup is as follows:

[0018] Take an existing commercially available low-temperature teacup purple sand embryo with a diameter of about 7cm. The purple sand embryo is fired at a low temperature of 450-550°C; use a dark copper-colored high-temperature glaze to outline the head, body and feet of the insect on the purple sand embryo; The bean green high-temperature glaze is used to draw the wings of insects. The glaze and the dark glaze form a partial overlapping coverage. While drawing, according to the design requirements of the work, the thick characteristics of the glaze are used to create a texture effect; according to the high-temperature crystal phase The formation and transformation and the characteristics of the embryo are fired between 1000°C and 1300°C until the single-color glaze and the mixed-color glaze have different glaze transformation effects, and the dark single-color glaze is covered with a translucent glaze. ...

Embodiment 3

[0020] The firing process of the traditional Chinese painting insect Pu'er tea cup is as follows:

[0021] Take an existing commercially available low-temperature teacup with a diameter of about 8cm and manually draw the embryo. The hand-drawn embryo is fired at a low temperature of 450-550°C; the head, body and feet of the insect are outlined on the embryo with a dark copper-colored high-temperature glaze; The light-colored bean green high-temperature glaze is used to draw the wings of insects, and the glaze and the dark glaze form partial overlapping coverage. At the same time of drawing, according to the design requirements of the work, the thick characteristics of the glaze are used to create texture effects; according to the high-temperature crystallization The formation and transformation of the phase and the characteristics of the embryo are fired at 1300°C to 1500°C until the single-color glaze and the mixed-color glaze have different glaze change effects, and the dark ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a craft manufacture technology, and particularly relates to a firing technology of insect wing crafts with skin texture characteristics. The firing technology of insect wing crafts with skin texture characteristics comprises the following steps: drawing according to the design sequence on a low-temperature fired embryo body at 450-550 DEG C by using multiple kinds of high-temperature color glaze materials so as to form an effect of covering by multiple kinds of color glaze layers partially, and firing the drawn embryo body at a high temperature, wherein partial overlapped part is subjected to glaze change generated by firing mixed multiple kinds of glaze materials, so that the fired crafts present glaze change texture with a skin texture effect, especially the semi-transparent cover texture which is much approximate to the texture of insect wings, and the art expressive force of ceramic products is enriched greatly.

Description

technical field [0001] The invention relates to a handicraft manufacturing process, in particular to a firing process of a translucent covering texture insect wing handicraft with texture characteristics. Background technique [0002] Ceramic or purple sand surface decoration is an important part of beautifying its products, which directly affects the value and artistic effect of handicrafts. Applying the glaze to the surface of the ceramic embryo or purple sand embryo can make the rough surface of the embryo body smooth and flat, with low water absorption, easy to wash and keep clean. The chemical properties of the glaze are stable, and the glaze surface has a high hardness, which can make the surface of the craft product resistant to acid, alkali, and salt erosion, and is durable. According to the firing temperature of the glaze, it can be divided into high-temperature glaze and low-temperature glaze. [0003] Conventional glazing methods include dipping glaze, dipping ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B44C5/06
Inventor 姜岸李婷梅菊郑剑峰
Owner 郑剑峰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com