Composition for environmentally friendly door and window materials excellent in heat resistance and colorability

A composition and door and window technology, which is applied in the field of environment-friendly door and window materials and door and window materials using the composition, can solve the problems of building material distortion, reduced weather resistance of pigments, discoloration, etc., and achieve excellent physical properties and mechanical physical properties. The effect of high properties and good extrusion processability

Inactive Publication Date: 2016-04-20
KOREA KUMHO PETROCHEMICAL CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of coloring with a color with good light absorption, problems such as distortion, deformation, and discoloration of building materials will occur when the atmospheric temperature rises
Also, the weather resistance of pigments used to express various colors is lowered, so that there is a problem of discoloration when exposed to external weather

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for environmentally friendly door and window materials excellent in heat resistance and colorability
  • Composition for environmentally friendly door and window materials excellent in heat resistance and colorability
  • Composition for environmentally friendly door and window materials excellent in heat resistance and colorability

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] Preparation of SAN

[0051] After heating the temperature of the bulk polymerization reaction tank to 150°C, 66 parts by weight of styrene, 44 parts by weight of acrylonitrile, 10 parts by weight of toluene, and 0.1 parts by weight of tert-dodecyl sulfide as a molecular weight regulator were added. The alcohol is first miscible on the line and continuously added to the polymerization tank for polymerization. When the conversion rate reached 70%, the polymer material was transferred into the box, heated to 220°C, and transferred to the devolatilizer, and the unreacted monomer and toluene were removed by vacuum at 720mmHg. The product thus obtained is a SAN copolymer resin with a weight average molecular weight of 180,000 and a ratio of styrene and acrylonitrile of 66:34.

[0052] PMI-SAN preparation

[0053] Mix 20 parts by weight of phenylmaleimide (PMI) and 20 parts by weight of acrylonitrile (AN) in a separate box, and mix 50 parts by weight of α-methylstyrene (AMS) and ...

Embodiment 1～6

[0055] As shown in Table 1, adjust the mixing ratio of SAN copolymer resin, PMI-based SAN resin and AABS resin, and add 0.3 parts by weight of antioxidant (Songnox 6260 from SONGWON Industry) and 0.3 parts by weight of UV absorber (Ciba Fine TINUVIN-P from Ciba Special Chemicals) and 4 parts by weight of titanium dioxide are uniformly mixed, and then the prepared resin is pelletized. After that, the pelletized synthetic resin composition was extruded under the extrusion conditions described below to prepare door and window profiles. The physical properties of the test pieces prepared under the same conditions are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a composition for environmentally friendly door and window materials and door and window materials made of the composition, and concretely relates to a composition for environmentally friendly door and window materials and with excellent heat resistance and dyeing properties and door and window materials made of the composition. The composition comprises, by weight, 30-60% of acrylic rubber grafting resins, 30-60% of styrene-vinyl cyanide copolymers, and 1-18% of quadripolymers composed of N-substituted maleimide monomers, alpha-alkyl styrene monomers, vinyl cyanide monomers and aromatic ethene monomers.

Description

Technical field [0001] The present invention relates to a composition for environmentally friendly door and window materials and a door and window material using the composition, and more specifically to a composition for environmentally friendly door and window materials with excellent heat resistance and colorability, and a door and window material using the composition . Background technique [0002] Polyvinyl chloride (PVC) resin is widely used as building materials such as window frames and windows. However, PVC resin contains environmentally hazardous substances such as large amounts of dioxins generated during combustion or extrusion processing. In addition, PVC resin uses heavy metal ions such as cadmium stearate (Cd-St) and lead stearate (Pb-St) as heat stabilizers, and such heavy metal ions play a role in disturbing human hormones and are thus restricted. Moreover, even if the PVC resin uses a heat stabilizer, it has the problem of discoloration during the process of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/12C08L51/00E06B1/26E06B3/20C08F265/04C08F279/04
Inventor 李济哲崔璋铉
Owner KOREA KUMHO PETROCHEMICAL CO LTD