Auxiliary heat stabilizer for PVC (Polyvinyl Chloride) machining
A technology that assists heat stabilizers and stabilizers, applied in the field of stabilizers, can solve problems such as poor synergistic effects, poor initial stability, and cost increases, and achieve the effect of solving stabilizer defects and poor stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0012] Example 1: Take equimolar glycerin with a pure calcium content higher than 60% calcium oxide, a pure zinc content of not less than 50% zinc oxide, and a purity of more than 90% in a formic acid environment, and heat it to 180 ° C for 200 minutes. When it becomes colorless and transparent, cool down to 120°C, add 6-amino-2-mercapto-pyrimidin-4-ol in a total amount equal to glycerin at a rate of 1 ml per second, and keep warm at 80°C for 60 minutes after dropping , filtered, dried, and crushed to obtain a stabilizer.
Embodiment 2
[0013] Example 2: Take equimolar glycerin with a pure calcium content higher than 60% calcium oxide, a pure zinc content of not less than 50% zinc oxide, and a purity of more than 90% in an acetic acid environment, and heat it to 180 ° C for 200 minutes. When it becomes colorless and transparent, cool down to 120°C, add 6-amino-2-mercapto-pyrimidin-4-ol in a total amount equal to glycerin at a rate of 1 ml per second, and keep warm at 80°C for 60 minutes after dropping , filtered, dried, and crushed to obtain a stabilizer.
Embodiment 3
[0014] Example 3: Take equimolar glycerol with a pure calcium content higher than 60% calcium oxide, a pure zinc content of not less than 50% zinc oxide, and a purity of more than 90% in a propionic acid environment, and heat it to 180 ° C for 200 minutes. When the system becomes colorless and transparent, cool down to 120°C, add 6-amino-2-mercapto-pyrimidin-4-ol in an amount equal to glycerin at a rate of 1 ml per second, and keep warm at 80°C for 60 minutes, filtered, dried, and crushed to obtain a stabilizer.
[0015] The stabilizer of embodiment 1-2 gained is used for PVC processing, and the photo of PVC product is as figure 1 shown.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap