Black high-build quick-drying antirust oil applicable to diesel engines of ships and warships and preparation method thereof

A technology of diesel engine and anti-rust oil, applied in the petroleum industry, base materials, lubricating compositions, etc., can solve the problems of poor anti-corrosion performance, difficult removal, rework and rust removal, etc., and achieve strong anti-corrosion ability, good adhesion, Easy-to-source effects

Active Publication Date: 2014-01-29
广西高城新材料科技有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the commercially available special anti-rust oil is sprayed or brushed on the oil film of large marine shafting diesel engine parts, which is difficult to remove after natural draining or has poor anti-corrosion performance. After the surface mechanical finishing treatment of various large-scale shafting products used in ships, due to the stay in the workshop, warehouse or short-ter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Black high-build quick-drying antirust oil applicable to diesel engines of ships and warships and preparation method thereof
  • Black high-build quick-drying antirust oil applicable to diesel engines of ships and warships and preparation method thereof
  • Black high-build quick-drying antirust oil applicable to diesel engines of ships and warships and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of the black thick paste quick-drying antirust oil that is applicable to marine diesel engine, comprises the following steps:

[0032] (1) Add 30% alkaline barium dinonyl sulfonate T705, 20% zinc naphthenate T704, 15% dodecenylsuccinic acid T746, 15% ortho Dibutyl phthalate, 3% benzotriazole T706, mix and heat to 65-75°C, stir until the material is completely dissolved; then when the temperature of the mixed material drops to 45-55°C, add 15 % emulsifier S-80 (purchased from Guangzhou Jieying Chemical Co., Ltd.; the same below), 1% 2,6-di-tert-butyl-p-cresol T501, 1% simethicone JC-201, mixed and stirred for 20 ~ 30 minutes until the materials are completely dissolved and uniform, and the multi-effect composite anti-rust agent is obtained; the percentages mentioned are the percentages of each component in the total weight of the raw materials of the multi-effect composite anti-rust agent.

[0033] (2) Pour the weighed 8% 150SN neutral base ...

Embodiment 2

[0038] A kind of preparation method of the black thick paste quick-drying antirust oil that is applicable to marine diesel engine, comprises the following steps:

[0039] (1) Same as step (1) of Example 1.

[0040] (2) Pour the weighed 6% 150SN neutral base mineral oil into the reaction kettle with steam heating and sealing device, add 8% barium petroleum sulfonate T701, 4% refined lanolin magnesium soap, 28% No. 10 petroleum asphalt, 6% No. 56 semi-refined paraffin, 8% No. 2 industrial vaseline, heat to 110-120 ° C, stir until the mixture is completely dissolved;

[0041] (3) After the temperature in the reactor drops to 45-55°C, add 10% multi-effect composite anti-rust agent and 0.5% tricresyl phosphate T306 under continuous stirring, and stir for 20 minutes;

[0042] (4) Finally, slowly add 25.5% No. 120 solvent oil and 4% acetone under continuous stirring, stir until the materials are evenly dissolved, filter out mechanical impurities with a mesh screen, and obtain a blac...

Embodiment 3

[0045] A kind of preparation method of the black thick paste quick-drying antirust oil that is applicable to marine diesel engine, comprises the following steps:

[0046] (1) Same as step (1) of Example 1.

[0047] (2) Pour the weighed 9% 150SN neutral base mineral oil into a reaction kettle with a steam heating and sealing device, and add 4.5% barium petroleum sulfonate T701, 4.5% refined lanolin magnesium soap, 27% No. 10 petroleum asphalt, 8% No. 56 semi-refined paraffin, 6% No. 2 industrial vaseline, heat to 110-120 ° C, stir until the mixture is completely dissolved;

[0048] (3) After the temperature in the reactor drops to 45-55°C, add 10% multi-effect composite anti-rust agent and 0.5% tricresyl phosphate T306 under continuous stirring, and stir for 20 minutes;

[0049] (4) Finally, under continuous stirring, slowly add 27% No. 120 solvent oil and 3.5% acetone, stir until the materials are evenly dissolved, filter out mechanical impurities with a mesh screen, and obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses black high-build quick-drying antirust oil applicable to diesel engines of ships and warships and a preparation method thereof. The black high-build quick-drying antirust oil applicable to diesel engines of ships and warships is prepared from 150SN neutral basic mineral oil, No.120 solvent oil, acetone, tricresyl phosphate, barium petroleum sulfonate, refined lanolin magnesium soap, a multi-effect compound antirust agent, No.10 petroleum asphalt, No.56 semi-refined paraffin wax and No.2 industrial Vaseline. The black high-build quick-drying antirust oil can form a semi-hard membrane-like protective coating with strong compactness, good adhesive force and naturally quick-drying property on the surface of a material, is resistant to atmospheric corrosion and has excellent moisture resistance and salt mist resistance, and the rustproof life can be more than three years; the antirust effect is good, and the antirust quality technical requirement of a user on products in processes of production, manufacturing, transportation, storage and the like can be completely met.

Description

technical field [0001] The invention belongs to the field of metal anti-corrosion and surface technology, and in particular relates to a black thick paste quick-drying anti-rust oil suitable for marine diesel engines and a preparation method thereof. Background technique [0002] In the process of production, manufacturing, storage and transportation of large-scale shafting diesel engine parts of ships, external oil seal anti-rust treatment is required until the parts of large-scale shafting diesel engines of ships are guaranteed to be rust-free, unsealed and cleaned before installation Only then can it be assembled and used. Due to the high cost of large-scale marine shafting diesel engine parts, high machining accuracy is required in the manufacturing process, especially the product needs to go through multiple links such as manufacturing, processing, storage, and transportation. The cycle is long, and the product weight and volume are large. Loading and unloading is more...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/04C10M111/06C10N30/12C10N30/08C10N40/00
Inventor 李荣福曾伟筠李诗菁
Owner 广西高城新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap