A kind of semi-worsted color spinning knitting yarn and its production process

A technology of knitting yarn and semi-worsted spinning is applied in the field of semi-worsted dyed knitting yarn and its production technology, which can solve the problems of too many short fibers, high price, and little use, etc., and achieve smooth yarn, soft hand feeling and good quality. The effect of moisture absorption and thermal insulation

Inactive Publication Date: 2016-08-24
NANTONG TEXTILE VOCATIONAL TECH COLLEGE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high price, it is not used much for the production of non-woven fabrics, and the price of 70 public count sheep cashmere is relatively cheap, and it contains more short fibers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] A semi-worsted yarn-dyed knitting yarn. The semi-worsted yarn-dyed knitting yarn is composed of the following components in parts by weight: 34 parts of viscose, 23 parts of nylon, 20 parts of cotton, 15 parts of wool, 3 parts of cashmere, rabbit Velvet 5 parts.

[0023] Among them, the viscose is viscose staple fiber, the specification is 1.67D*38mm, the nylon specification is 1.67D*38mm, the cotton is combed cotton, the length of combed cotton is 28mm, the wool is 70 male cashmere, the length is 45mm , the cashmere is white cashmere with a length of 28mm, and the length of rabbit hair is 28mm.

[0024] The production process of semi-worsted yarn-dyed knitting includes the following steps: 1) Dyeing; 2) Blending; 3) Carding, the sliver weight is 21.00g / 5m; 4) Drawing, the sliver speed is 340r / min ;5) Roving, the spindle speed is 1000r / min; 6) Spun yarn, the spindle speed is 15000r / min; 7) Winding; 8) Doubling; 9) Two-for-one twisting.

[0025] Among them, in step 2) ...

specific Embodiment 2

[0026] A semi-worsted yarn-dyed knitting yarn. The semi-worsted yarn-dyed knitting yarn is composed of the following components in parts by weight: 32 parts of viscose, 26 parts of nylon, 15 parts of cotton, 15 parts of wool, 5 parts of cashmere, rabbit 7 parts of cashmere.

[0027] Among them, the viscose is viscose staple fiber, the specification is 1.67D*38mm, the nylon specification is 1.67D*38mm, the cotton is combed cotton, the length of combed cotton is 28mm, the wool is 70 male cashmere, the length is 50mm , the cashmere is white cashmere with a length of 30mm, and the length of rabbit hair is 30mm.

[0028] The production process of semi-worsted yarn-dyed knitting includes the following steps: 1) Dyeing; 2) Blending; 3) Carding, the sliver weight is 21.00g / 5m; 4) Drawing, the sliver speed is 340r / min ;5) Roving, the spindle speed is 1000r / min; 6) Spun yarn, the spindle speed is 15000r / min; 7) Winding; 8) Doubling; 9) Two-for-one twisting.

[0029] Among them, in ste...

specific Embodiment 3

[0030] A semi-worsted yarn-dyed knitting yarn. The semi-worsted yarn-dyed knitting yarn is composed of the following components in parts by weight: 33 parts of viscose, 20 parts of nylon, 18 parts of cotton, 18 parts of wool, 7 parts of cashmere, rabbit Cashmere 4 parts.

[0031] Among them, the viscose is viscose staple fiber, the specification is 1.67D*38mm, the nylon specification is 1.67D*38mm, the cotton is combed cotton, the length of combed cotton is 28mcm, the wool is 70 male cashmere, the length is 54mm , the cashmere is white cashmere with a length of 29mm, and the length of rabbit hair is 29mm.

[0032] The production process of semi-worsted yarn-dyed knitting includes the following steps: 1) Dyeing; 2) Blending; 3) Carding, the sliver weight is 21.00g / 5m; 4) Drawing, the sliver speed is 340r / min ;5) Roving, the spindle speed is 1000r / min; 6) Spun yarn, the spindle speed is 15000r / min; 7) Winding; 8) Doubling; 9) Two-for-one twisting.

[0033] Among them, in step ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a semi-worsted yarn-dyed knitting yarn, which is composed of the following components in parts by weight: 30-36 parts of viscose, 20-26 parts of nylon, and 15-21 parts of cotton 15-21 parts of wool, 3-7 parts of cashmere, 3-7 parts of rabbit hair. The production process of semi-worsted yarn-dyed knitting yarn includes the following steps: 1) dyeing; 2) wool; 3) carding; 4) drawing; 5) roving; 6) spun yarn; line; 9) double twisting. The present invention is a semi-worsted yarn-dyed knitting yarn blended from six kinds of raw materials. The yarn is smooth, has good hygroscopicity and warmth-retaining performance, good elongation, good luster, and soft hand feeling. Its production process is pre-spun It is a wool spinning process, and the post-spinning is a cotton spinning process.

Description

technical field [0001] The invention relates to a yarn and a production process, in particular to a semi-worsted yarn-dyed knitting yarn and a production process thereof. Background technique [0002] The dry strength of viscose fiber is lower than that of cotton, and its wet strength is only about 50% of the dry strength. The elastic recovery ability is poor, it is not wear-resistant, not light-resistant, alkali-resistant and acid-resistant; but viscose fiber has good hygroscopicity and is easy to dye. The fabric is comfortable to wear. Blending it with synthetic fibers can improve the wearability of the fabric. [0003] Nylon has better resilience, fatigue resistance and thermal stability at a lower melting point, and also has better elongation. [0004] The yarn spun from combed cotton is finer and of better quality, and the fabrics made of combed cotton have a higher quality level in terms of texture, washability and durability. [0005] Wool is an important raw mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D02G3/04D01H13/30
Inventor 蔡永东
Owner NANTONG TEXTILE VOCATIONAL TECH COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com