Modified compounded rubber sealing gasket material and preparation method thereof

A technology of mixed rubber and sealing gasket, which is applied in the field of modified mixed rubber sealing gasket material and its preparation, which can solve the problems of low strength, unsatisfactory sealing effect, poor wear resistance, etc., achieve high performance such as aging resistance, and improve process performance , long service life effect

Inactive Publication Date: 2014-03-05
TONGLING SIDE TECH
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance, and low strength, which are far from meeting the actual requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified compounded rubber sealing gasket material and preparation method thereof
  • Modified compounded rubber sealing gasket material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The present invention will be described in detail below through specific examples.

[0010] A modified mixed rubber sealing gasket material, which is made of the following raw materials in parts by weight (kg): tetrapropylene fluorine rubber 70, silicon rubber 18, calcium hydroxide 1, magnesium oxide 2, N550 carbon black 28, sulfur 1, accelerator Agent DM1, zinc oxide 2, potassium citrate 2, decabromodiphenylethane 1, acrylonitrile 1, methyl methacrylate 3, 3-aminopropyltrimethoxysilane 1, crosslinking agent TAC0.5, nano Celestite powder 16, modified attapulgite 10;

[0011] The modified attapulgite is made of the following raw materials in parts by weight (kg): attapulgite 20, toluene diisocyanate 3, trimethylolpropane triacrylate 2, medical stone 30, ascorbic acid 1, jade 2, Polyisobutylene 2, aluminate coupling agent DL-4111, Zanthoxylum bungeanum seed oil 1; the preparation method is to mix attapulgite, medical stone, and jade into a calciner and calcinate at 700-7...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified compounded rubber sealing gasket material. The modified compounded rubber sealing gasket material is characterized by being prepared from the following raw materials in parts by weight: 70-75 parts of tetrafluoroethylene-propylene rubber, 18-23 parts of silicone rubber, 1-2 parts of calcium hydroxide, 2-4 parts of magnesium oxide, 28-32 parts of N550 carbon black, 1-2 parts of sulphur, 1-2 parts of accelerant DM, 2-3 parts of zinc oxide, 2-4 parts of potassium citrate, 1-2 parts of 2,2',3,3',4,4',5,5',6,6'-decabromobibenzyl, 1-2 parts of acrylonitrile, 3-5 parts of methyl methacrylate, 1-2 parts of 3-aminopropyltrimethoxysilane, 0.5-1 part of crosslinking agent TAC, 16-20 parts of nanometer celestite powder and 10-12 parts of modified attapulgite. The processing property of the rubber material is improved by adding the modified attapulgite; the toxic and side effects and the pollution to environments of the rubber material are reduced by using an environmentally-friendly compounding agent; the modified compounded rubber sealing gasket material has good combination property and is long in service life; the mechanical property, the oil resistance, the ageing resistance and the like of the modified compounded rubber sealing gasket material are improved.

Description

technical field [0001] The invention relates to the field of processing rubber composite materials, in particular to a modified mixed rubber gasket material and a preparation method thereof. Background technique [0002] Gasket is a material used for sealing inside machinery, equipment, pipelines, etc. The gaskets currently used are mostly rubber gaskets, which are characterized by high temperature resistance, ozone resistance, natural aging resistance, vacuum resistance, fuel oil resistance, lubricating oil resistance, strong oxidant resistance, chemical resistance and good electrical insulation performance. Widely used in defense industry and civilian industry. However, the existing rubber gaskets have defects such as unsatisfactory sealing effect, poor wear resistance and low strength, which are far from meeting the actual requirements. Therefore researching and developing a kind of high-performance rubber gasket has become the task of top priority. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/18C08L83/04C08K13/06C08K9/00C08K9/02C08K3/34C08K5/103C08K3/22C08K5/098C08K5/1535
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com