Chrome-free tanning method of alligator skin
A chrome-free tanning technology for crocodile skin, which is applied in the field of chrome-free tanning of crocodile skin, can solve the problem of destroying the glossiness of the grain surface of crocodile skin, the square concave-convex texture, the difficulty in combining organic phosphonium salt tanning agents with crocodile skin, and the grain surface of crocodile skin. Abrasion and other problems, to achieve good tanning effect, good gloss, pure white color effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1
[0026] This embodiment is implemented in a rotating drum, and the process steps are as follows:
[0027] (1) The preservatively treated crocodile skin is subjected to meat removal, water immersion, scale removal, liming, non-ammonium salt deliming, bleaching, softening, and acid pickling to obtain the crocodile skin blank according to the conventional process. When the pickling treatment is completed, soak The pH of the acid is 2.4;
[0028] (2) Add 100kg of water and 6kg of sodium chloride into the drum, rotate the drum to dissolve the sodium chloride completely, then add 100kg of pickled crocodile skin obtained in step (1), rotate the drum for 5 minutes, and then rotate the drum Add NaHCO with a concentration of 50g / L in 2 times (15min interval) under the condition of 3 Adjust the pH value of the mixed liquid in the drum to 3.5 with the aqueous solution;
[0029] (3) Add organic phosphine salt tanning agent FCC 3.5 kg, monoethanolamine 0.5 kg, and glutaraldehyde ...
Example Embodiment
[0034] Example 2
[0035] This embodiment is implemented in the scribe groove, and the process steps are as follows:
[0036] (1) The preservatively treated crocodile skin is subjected to meat removal, water immersion, scale removal, liming, non-ammonium salt deliming, bleaching, softening, and acid pickling to obtain the crocodile skin blank according to the conventional process. When the pickling treatment is completed, soak The pH of the acid is 2.0;
[0037] (2) Add 300kg of water and 12kg of sodium chloride into the scoring slot, move the scoring board of the scoring slot to completely dissolve the sodium chloride, and then add 100kg of pickled crocodile skin obtained in step (1), rotate for 10 minutes, and then scratch Add NaHCO with a concentration of 100g / L in 2 times (15min interval) under the condition of moving the paddle 3 Adjust the pH value of the mixed solution in the groove to 3.7 with the aqueous solution;
[0038] (3) Add 4.0 kg of organic phosphine salt tanning age...
Example Embodiment
[0043] Example 3
[0044] This embodiment is implemented in a rotating drum, and the process steps are as follows:
[0045] (1) The preservatively treated crocodile skin is subjected to meat removal, water immersion, scale removal, liming, non-ammonium salt deliming, bleaching, softening, and acid pickling to obtain the crocodile skin blank according to the conventional process. When the pickling treatment is completed, soak The pH of the acid is 1.6;
[0046] (2) Add 120kg of water and 8kg of sodium chloride into the drum, rotate the drum to completely dissolve the sodium chloride, then add 100kg of the soaked crocodile skin obtained in step (1), rotate the drum for 10 minutes, and then rotate the drum Add NaHCO with a concentration of 100g / L in 3 times (15min interval) under the condition of 3 Adjust the pH value of the mixed liquid in the drum to 3.4 with the aqueous solution;
[0047] (3) Add 4.0 kg of organic phosphine salt tanning agent PCC, 1.0 kg of isopropanolamine, and 0.4 ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap