Red-hardness high alloy steel material for pump valves and preparation method thereof

A high-hardness, alloy steel technology, applied in the direction of improving process efficiency, can solve problems such as harshness and high requirements, and achieve the effect of improving yield, good red hardness, and reducing inclusion oxides

Inactive Publication Date: 2014-03-19
TONGLING SIDE TECH
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002]Pumps and valves work in various and harsh environments, and have high requirements for materials. At present, there are many kinds of alloy steels used for pumps and valves, and the technology has made great progress, but There are still many problems, such as wear resistance, hardness, antirust performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., which cannot meet the production requirements in many occasions, and further improvement is needed to increase production efficiency. , reduce costs, improve safety, provide guarantee for the development of high-precision technology, and provide impetus for social development, the task is still very arduous

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A red hardness high-alloy steel material for pump valves, which contains chemical element components and mass percentages: carbon 0.2-0.4, silicon 0.6-0.9, manganese 1.7-1.9, molybdenum 2.1-2.4, chromium 1.6-1.8, vanadium 0.02-0.04, nickel 0.02-0.05, niobium 0.1-0.15, Ta0.04-0.06, S≤0.04, P≤0.04, and the balance is iron.

[0014] The production method of the red hardness high alloy steel material for the pump valve is as follows:

[0015] (1) Prepare pig iron and scrap iron as the source of iron matrix in a ratio of 1:1.5, put pig iron into the furnace for melting, perform desulfurization, deoxidation, use refining agent for one-time refining, add alloy components for alloying, and then add scrap iron to melt , adding refining agent for secondary refining, testing and adjusting the content of chemical elements to pass, casting, post-casting heat treatment, etc.;

[0016] (2) The order of batches of alloying elements put into the furnace during the alloying process is: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to view more

Abstract

A red-hardness high alloy steel material for pump valves comprises the following chemical element components by mass percent: 0.2-0.4% of carbon, 0.6-0.9% of silicon, 1.7-1.9% of manganese, 2.1-2.4% of molybdenum,1.6-1.8% of chromium, 0.02-0.04% of vanadium, 0.02-0.05% of nickel, 0.1-0.15% of niobium, 0.04-0.06% of Ta, not more than 0.04% of S, not more than 0.04% of P, and the balance of iron. The alloy steel of the invention not only has high hardness and good red hardness, but also has good toughness and good wear resistance. The method of the invention partly adopts scrap iron as a raw material; secondary refining is performed; and the comprehensive mechanical properties are improved. The alloy steel of the invention is suitable for high-wear rate parts used at high temperature, such as pump shafts, pipelines, valves and the like. The method of the invention adopts a refining agent in the casting production, which significantly improves the yield, especially reduces the degree of porosity in casting by 1-2 degrees, and controls the oxide inclusion level at about grade two.

Description

technical field [0001] The invention relates to the field of metal material preparation, in particular to a red hardness high alloy steel material for pump valves and a preparation method thereof. Background technique [0002] The working environment of pump valves is diverse and harsh, and the requirements for materials are very high. At present, there are many kinds of alloy steel used in pump valves, and the technology has made great progress, but there are still many problems, such as wear resistance, hardness, rust resistance Performance, corrosion resistance, high and low temperature resistance, brittleness, toughness, etc., cannot meet the production requirements in many occasions, and further improvement is needed to improve production efficiency, reduce costs, and improve safety. Guaranteeing and providing impetus for social development are still arduous tasks. Contents of the invention [0003] The object of the present invention is to provide a red hardness hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/58C22C33/04C21D6/00
CPCY02P10/20
Inventor 孔华英
Owner TONGLING SIDE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap