Fire-resistant rubber

A technology of refractory rubber and neoprene, which is applied in the field of refractory rubber to achieve the effect of good fire resistance and reduced loss

Inactive Publication Date: 2014-03-26
山东中一橡胶有限公司
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of chloroprene rubber are electrical insulation performance, poor cold resistance, and raw rubber is unstable during storage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] Neoprene 90 EPDM 120

[0057] Nano Zinc Oxide 8 Stearic Acid 3

[0058] Magnesium hydroxide 20 Aluminum phosphate 4

[0059] Magnesium silicate 8 Sodium silicate 6

[0060] Mica powder 10 Silicon carbide 7

[0061] Antiaging agent 4 Calcium carbonate 6

[0062] Hydroxy silicone oil 4 Hydrogen silicone oil 3

[0063] Silica 3 Dimethicone 2

[0064]Dibutyl phthalate 1 N-tert-butyl-2-benzothiazole sulfenamide 2

[0065] 2-thiol imidazoline 1.

[0066] The anti-aging agent is N-phenyl-α-aniline and N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 2:1.

[0067] Fire resistance test:

[0068] It can play a very good flame retardant effect, and it is not easy to burn in case of fire, but it cannot form a hard shell, and the surface still has a certain degree of ceramicization, which can also play a very good protective role. It can reach the UL94V0 flame retardant level (UL94V0 is the American flame retardant material standard).

Embodiment 2

[0079] Neoprene 100 EPDM 110

[0080] Nano Zinc Oxide 8 Stearic Acid 2

[0081] Magnesium hydroxide 20 Aluminum phosphate 3

[0082] Magnesium silicate 8 Sodium silicate 6

[0083] Mica powder 9 Silicon carbide 6

[0084] Antiaging agent 4 Calcium carbonate 6

[0085] Hydroxy silicone oil 4 Hydrogen silicone oil 2

[0086] Silica 3 Simethicone 1.5

[0087] Dibutyl phthalate 1 N-tert-butyl-2-benzothiazole sulfenamide 1.5

[0088] 2-thiol imidazoline 1.

[0089] The anti-aging agent is N-phenyl-α-aniline and N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 2:1.

Embodiment 3

[0091] Neoprene 60 EPDM 70

[0092] Nano Zinc Oxide 4 Stearic Acid 1

[0093] Magnesium hydroxide 10 Aluminum phosphate 2

[0094] Magnesium silicate 2 Sodium silicate 2

[0095] Mica powder 4 Silicon carbide 3

[0096] Antiaging agent 1 Calcium carbonate 2

[0097] Hydroxy silicone oil 1 Hydrogen silicone oil 1

[0098] Silica 1 Simethicone 1

[0099] Dibutyl phthalate 1 N-tert-butyl-2-benzothiazole sulfenamide 1

[0100] 2-thiol imidazoline 1.

[0101] The anti-aging agent is N-phenyl-α-aniline and N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 1:1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of rubber, and particularly relates to a fire-resistant rubber. The fire-resistant rubber comprises the following components in parts by weight: 50-160 parts of neoprene, 60-150 parts of ethylene-propylene-diene rubber, 4-12 parts of nano zinc oxide, 1-5 parts of stearic acid, 10-25 parts of magnesium hydroxide, 2-6 parts of aluminium phosphate, 2-12 parts of magnesium silicate, 2-10 parts of sodium silicate, 4-18 parts of mica powder, 2-12 parts of silicon carbide, 1-5 parts of an antiager, 1-10 parts of calcium carbonate, 1-7 parts of hydroxyl silicone oil, 1-6 parts of hydrosilicone oil, 1-5 parts of white carbon black, 1-5 parts of simethicone, 1-5 parts of dibutlyl phthalate, 1-5 parts of N-tert-butylbenzothiazole-2-sulphenamide and 1-5 parts of 2-imidazolidinethione. The invention has the benefits that the fire-resistant rubber prepared by the formula has good refractability and can play a certain protective role in a big fire to reduce loss caused to people by the big fire.

Description

technical field [0001] The invention belongs to the field of rubber, and in particular relates to a fire-resistant rubber. Background technique [0002] Usually silicone rubber itself is not fire resistant. However, in the current fire accidents, wires and cables are not fire-resistant and easy to burn in case of fire. This field lacks a kind of fire-resistant silicone rubber, which is required to play a certain protective role in the fire, and can reduce the electricity brought to people in the fire. Loss, reduce the harm of electricity. Refractory rubber is made of chloroprene as the main raw material through homopolymerization or copolymerization of a small amount of other monomers. Such as rubber products with high tensile strength, excellent heat resistance, light resistance, aging resistance, and oil resistance are better than natural rubber, styrene-butadiene rubber, and butadiene rubber. It has strong flame resistance and excellent flame retardancy resistance, hi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L11/00C08L23/16C08L83/06C08L83/05C08L83/04C08K13/02C08K3/22C08K5/09C08K3/32C08K3/34C08K3/26C08K3/36C08K5/12C08K5/47C08K5/37
Inventor 郭永县裴升明王江涛隋效营李洪飞郑海菲
Owner 山东中一橡胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com