A method for enriching and recovering cadmium from lead smelting system

A lead smelting and enrichment technology, applied in the direction of improving process efficiency, can solve the problems of high production cost, difficult enrichment and separation, unreasonable economy, etc., and achieves short enrichment and separation process, efficient enrichment and separation, and economic benefits. significant effect

Active Publication Date: 2016-04-20
HENAN YUGUANG GOLD & LEAD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen that when recovering cadmium from the lead smelting system, the traditional process is long, the cadmium is seriously dispersed, the enrichment and separation are difficult, the heavy metal pollution is large, a large number of chemical reagents are used, the production cost is high, and the metal recovery rate is low.
[0004] At present, bottom-blowing furnace oxidation-blast furnace (reduction furnace) reduction lead smelting process is widely used in China. Most of the cadmium-containing materials produced by high-temperature smelting are rich in lead and zinc. Some companies sell this part of cadmium-containing materials to zinc smelters to recover cadmium. , when this kind of high-cadmium-containing lead-zinc soot is sold, neither cadmium nor zinc is priced, only the price of lead is calculated, which makes this method of recycling cadmium poor in economic benefits, economically unreasonable, and loses a certain amount of lead metal , zinc smelters also bear the risk of heavy metal lead pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for enriching and recovering cadmium from lead smelting system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Example 1: After 10 tons of lead concentrate is mixed with 0.5-1 tons of quartz, 0.5-1 tons of stones and 1-2 tons of low-cadmium smoke, it is added to the bottom blowing furnace, and the bottom of the furnace is blown into the furnace with an oxygen lance at a pressure of 0.6-1.0 Oxygen and nitrogen in MPa, the amount of oxygen blown into it is 1200m 3 , the amount of nitrogen is 0.3 times that of oxygen, and the temperature in the furnace is kept at 1100°C. After the reaction, high-lead slag, crude lead, and high-temperature SO2 flue gas dust are produced. After 280-350°C, 1 ton of ESP soot containing 20% ​​cadmium is obtained after passing through the electrostatic precipitator; the obtained 1 ton of ESP soot containing 20% ​​cadmium is added to water for leaching, and the leaching conditions : The liquid-solid ratio is 4:1, the temperature is about 30°C, and the time is 2 hours. After the leaching is completed, 0.7 tons of leaching residue and 4m of leaching soluti...

Embodiment 2

[0041] Example 2: Example 1: After 10 tons of lead concentrate is mixed with 0.5-1 tons of quartz, 0.5-1 tons of stones and 1-2 tons of low-cadmium smoke, it is added to the bottom blowing furnace, and the bottom of the furnace is blown into the pressure by an oxygen lance. Oxygen and nitrogen at 1MPa, the amount of oxygen blown into it is 1000m 3 , the amount of nitrogen is 0.4 times that of oxygen, and the temperature in the furnace is kept at 1100°C. After the reaction, high-lead slag, crude lead, and high-temperature SO2 flue gas dust are produced. After 300°C, 1 ton of ESP soot containing 20% ​​cadmium is obtained after passing through the electrostatic precipitator; the obtained 1 ton of ESP soot containing 20% ​​cadmium is added to the concentration of 0.2-1% Leach in dilute sulfuric acid, leaching conditions: liquid-solid ratio 4:1, temperature around 30°C, time 2 hours. After the leaching is completed, 0.7 tons of leaching residue and 4m of leaching solution are obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the non-ferrous metal smelting industry, and in particular relates to a method for enriching and recovering cadmium from a lead smelting system. After the lead concentrate is matched with auxiliary materials and returned low-cadmium fume, it is added to the bottom blowing furnace for desulfurization and smelting lead. Cadmium is cyclically enriched in the form of cadmium sulfate in the electric dust collection soot; when the cadmium content in the electric dust collection soot reaches 5-28%, the cadmium is separated by leaching with water or dilute sulfuric acid, and the leaching solution is replaced with zinc powder to produce cadmium cotton, which is further produced Crude cadmium and refined cadmium are extracted; the solution after replacing cadmium is used as a raw material for the production of nano-zinc oxide, zinc sulfate monohydrate, and zinc sulfate heptahydrate to recover zinc; lead is enriched in the leaching residue during the leaching process, which is convenient to return to the lead system for smelting Recovery; this method adopts bottom blowing smelting technology, while smelting lead, efficiently enriches and transforms cadmium in raw materials into water-soluble cadmium salt, shortens the process flow, and provides conditions for direct enrichment, separation and recovery of lead and cadmium. The dispersion of lead during wet recovery of cadmium is avoided, and the production cost is reduced.

Description

technical field [0001] The invention belongs to the nonferrous metal smelting industry, in particular to a method for enriching and recovering cadmium from a lead smelting system. Background technique [0002] At present, cadmium metal is mainly recovered comprehensively from the zinc smelting system. The main recovery process is: the zinc sulfide concentrate is roasted, so that zinc and cadmium enter the calcine in the form of oxide and sulfate, and when the calcine is acid leached, the zinc and Cadmium enters the solution in the form of sulfate. Harmful metals in the solution need to be removed before zinc electrowinning. The main method for removing cadmium is to add zinc powder for replacement, and produce copper and cadmium replacement slag; then use dilute sulfuric acid or zinc electrowinning solution for oxidative leaching Copper cadmium replacement slag, the output copper cadmium slag leaching solution is replaced twice with zinc powder to remove cadmium, the first s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B17/00C22B7/02C22B13/02
CPCY02P10/20
Inventor 李卫锋狄聚才蒋丽华王光明李武科王成伟王海涛杨明
Owner HENAN YUGUANG GOLD & LEAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com