A kind of ZSM-48 molecular sieve with low silicon-aluminum ratio and preparation method thereof

A low-silicon-aluminum ratio and molecular sieve technology, applied in the direction of crystalline aluminosilicate zeolite, etc., can solve the problems of shortening the crystallization time, achieve the effects of reducing the silicon-aluminum ratio, increasing the acid content, and good application prospects

Active Publication Date: 2015-10-21
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the more expensive template agent hexamethylenediamine chloride is used in this patent, its effect is indeed very significant. The silicon-aluminum ratio of the feed is reduced to 100, the silicon-aluminum ratio of the product reaches about 100, and the crystallization time is also shortened. reduced to 48 hours

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ZSM-48 molecular sieve with low silicon-aluminum ratio and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) Weigh sodium hydroxide and sodium aluminate (Al 2 o 3 , 43wt%; Na 2 O, 38wt%) was dissolved in deionized water, and then the templating agent R (12-crown-4, content >97%) was added while stirring at a water bath temperature of 60°C, and after stirring for 0.5 hours, white carbon black was added, After stirring for 1 hour, add seed crystal S, continue stirring for 2 hours, and then move to a closed stainless steel reaction kettle.

[0021] (2) Crystallized at 160°C for 6 days, the obtained crystallized product was analyzed as ZSM-48 molecular sieve by XRD analysis, the specific raw material ratio and product properties are shown in Table 1.

Embodiment 2

[0023] (1) Same as step (1) of Example 1.

[0024] (2) Crystallized at 158°C for 8 days, the obtained crystallized product was analyzed as ZSM-48 molecular sieve by XRD analysis, the specific raw material ratio and product properties are shown in Table 1.

Embodiment 3

[0026] (1) Same as step (1) of Example 1, the temperature of the water bath is 80°C.

[0027] (2) Crystallize at 160°C for 5 days, and the obtained crystallized product is ZSM-48 molecular sieve by XRD analysis. The specific raw material ratio and product properties are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a ZSM-48 molecular sieve with a low silica-alumina ratio and a preparation method thereof. The molecular sieve has the following properties: the molar ratio of silica to alumina is 25-50; the specific surface is 250-400 m2 / g; the pore volume is 0.25-0.35 cm3 / g; the average pore size is 3-5 nm. The preparation method comprises the following steps: (1) well mixing a seed crystal S, a template R, a silicon source, an aluminium source, sodium hydroxide and water to prepare a reaction mixture, wherein the composition of the reaction mixture is as follows: on a basis of oxide, the molar ratio of R to SiO2 is 0.05-0.2, the molar ratio of SiO2 to Al2O3 is 30-50, the molar ratio of Na2O to SiO2 is 0.06-0.1, the molar ratio of H2O to SiO2 is 15-23, the mass ratio of S to SiO2 is 0.05-0.5, S is the ZSM-48 molecular sieve, and R is 12-crown ether-4; (2) performing hydrothermal crystallization of the reaction mixture prepared in step (1) at 150-170 DEG C for 4-8 days, performing filtration, washing, drying, and roasting of the crystallization product to obtain the ZSM-48 molecular sieve with a low silica-alumina ratio. The ZSM-48 molecular sieve prepared by the method of the invention has a low silica-alumina ratio, and has good application prospects in technical fields of isodewaxing and the like.

Description

technical field [0001] The invention relates to a preparation method of a molecular sieve, in particular to a ZSM-48 molecular sieve with a low silicon-aluminum ratio and a preparation method thereof. Background technique [0002] In 1983, the patent USP4397827 reported the synthesis of ZSM-48 molecular sieve for the first time. ZSM-48 molecular sieve is a molecular sieve with ten-membered ring channel structure, and the pore size is 0.53nm×0.56nm. The pure silicon ZSM-48 molecular sieve has attracted wide attention for its good selectivity of low-carbon olefins in the reaction of synthesis gas to olefins. [0003] At present, the research focus of ZSM-48 molecular sieve is still on its synthesis process. The synthesis process of this molecular sieve has the following characteristics: (1) The silicon-aluminum ratio of the synthesized molecular sieve is high. The ratio is greater than 100; (2) If a low-cost template is used, although the cost of synthesizing molecular sieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/04
Inventor 秦波尹泽群张喜文刘全杰张志智
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products