Cement-polyphenyl granule foamed heat preservation board and preparation method thereof
A technology for foaming thermal insulation boards and polystyrene particles is applied in the field of building wall panels, which can solve the problems of affecting the compressive strength of thermal insulation boards, poor sound insulation effect, and high thermal insulation coefficient, and achieve the advantages of low cost, convenient operation and molding, and reduced structural cost. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] Cement, polystyrene particle foam insulation board, its specific preparation method is as follows:
[0018] Take 155 kg of Portland cement, 1.8 kg of flame-retardant polystyrene particles, 1 kg of polypropylene fiber, and 2.5 kg of calcium stearate, mix and stir evenly, then add 3 kg of styrene-acrylic emulsion, 2 kg of silicone waterproofing agent and Continue stirring with 110kg of warm water at 55°C for 20-30 minutes. After stirring into a slurry, add 6.3kg of hydrogen peroxide in accordance with the stated weight and then pour it into a mold for rise. Foaming and hair in place for 25 minutes, wait for 6 After 1 hour, it was demoulded and cured for 13 days to obtain a cement and polystyrene particle foam insulation board. The length of polypropylene fiber is 9-11mm.
[0019] The cement and polystyrene granule foam insulation board prepared in this example have a self-weight of 130 kilograms per cubic meter, a thermal insulation coefficient of 0.04, and a sound insul...
Embodiment 2
[0021] Cement, polystyrene particle foam insulation board, its specific preparation method is as follows:
[0022] Take 150 kg of Portland cement, 2 kg of flame-retardant polystyrene particles, 1.2 kg of polypropylene fiber, and 3 kg of calcium stearate, mix and stir evenly, and then add 3.5 kg of styrene-acrylic emulsion and 2.5 kg of silicone waterproofing agent in accordance with the stated parts by weight. kg and 120kg of warm water at 60°C and continue to stir for 20-30 minutes. After stirring into a slurry, add 6.5kg of hydrogen peroxide in accordance with the stated weight and then pour it into a mold for rising. Foaming and hair in place for 20 minutes. After waiting for 7 hours, demoulding and curing for 15 days, the foamed insulation board made of cement and polystyrene particles was obtained. The length of polypropylene fiber is 8-9mm.
[0023] The cement and polystyrene granule foam insulation board made in this embodiment have a self-weight of 133 kilograms per c...
Embodiment 3
[0025] Cement, polystyrene particle foam insulation board, its specific preparation method is as follows:
[0026] Take 160 kg of Portland cement, 1.5 kg of flame-retardant polystyrene particles, 0.8 kg of polypropylene fiber, and 2 kg of calcium stearate, mix and stir evenly, and then add 2.5 kg of styrene-acrylic emulsion and 1.5 kg of silicone water repellent that meet the stated parts by weight. kg and 100kg of warm water at 50°C and continue to stir for 20-30 minutes. After stirring into a slurry, add 6kg of hydrogen peroxide in accordance with the stated weight and then pour it into the mold for rise. Foaming and hair in place for 30 minutes, wait After 5 hours, the mold was demoulded and cured for 10 days to obtain a cement and polystyrene particle foam insulation board. The length of polypropylene fiber is 10-12mm.
[0027] The cement and polystyrene granule foam insulation board made in this example have a self-weight of 137 kilograms per cubic meter, a thermal insul...
PUM
Property | Measurement | Unit |
---|---|---|
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap