Automatic adhering wrapping explosion-prevention polymer sealing rubber powder for improving vehicle tire performances

A technology for automobile tires and polymers, applied in the direction of non-polymer adhesive additives, adhesives, adhesive types, etc. Problems such as poor force, polymer self-sealing hot melt adhesive powder layer falling off, etc., to achieve the effect of reducing hardness, improving operability, and increasing stickiness

Inactive Publication Date: 2014-05-21
LUOYANG JUNTENG ENERGY TECH
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing polymer self-sealing hot-melt adhesive powder is difficult to meet this requirement, mostly due to the poor adhesion of the polymer self-sealing hot-melt adhesive powder and the unreliable adhesion to the inner wall surface of the automobile wheel tire, causing the polymer self-sealing hot-melt adhesive powder layer to fall off or off-edge defects, it is difficult to achieve the function and effect of the upgraded car tires without deflation
[0007] In order to solve the above-mentioned problems, relevant manufacturers and research institutes have worked hard to find a solution, but for a long time no suitable polymer automatic adhesive explosion-proof sealing powder has been found.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Proportion and composition of polymer self-adhering explosion-proof sealant powder (based on weight percentage): 50% thermoplastic elastomer, 40% tackifier, 5% plasticizer, 1% anti-aging agent, 3% filler , 1% blowing agent; Take thermoplastic elastomer SEBS700g, thermoplastic elastomer SEPS300g; Tackifier: terpene phenolic resin 600g, rosin glyceride 200g; Plasticizer: aromatic hydrocarbon oil 50g, dioctyl phthalate ( DOP) 50g; anti-aging agent: 101010g, anti-aging agent RD10g; filler: nano-calcium carbonate 60g; foaming agent: a mixture of AC and zinc oxide 20g.

Embodiment 2

[0034] Proportion and composition of polymer self-adhering explosion-proof sealant powder (based on weight percentage): 40% thermoplastic elastomer, 50% tackifier, 3% plasticizer, 1% anti-aging agent, 4% filler , 2% foaming agent; weigh thermoplastic elastomer SEBS600g, SEPS200g; tackifier: terpene phenolic resin 500g, coumarone resin 500g; plasticizer: aromatic oil 30g, dioctyl phthalate (DOP) 30g; antiaging agent 1076, 10g, antiaging agent RD, 10g; filler: 50g of quartz powder, 30g of nano calcium carbonate; foaming agent: 40g of mixture of AC and zinc stearate.

Embodiment 3

[0036] Proportion and composition of polymer self-adhering explosion-proof sealant powder (based on weight percentage): 41% thermoplastic elastomer, 45% tackifier, 5% plasticizer, 1% anti-aging agent, 5% filler , 3% foaming agent; weigh thermoplastic elastomer SEBS500g, SEPS320g; tackifier: coumarone resin 400g, rosin glyceride 500g; plasticizer: aromatic hydrocarbon oil 50g, dioctyl phthalate (DOP) 50g Antiaging agent: Antiaging agent 1010, 10g, Antiaging agent RD, 10g; Filling agent: Nano-calcium carbonate 50g, Quartz powder 50g; Foaming agent: AC, zinc oxide, zinc stearate mixture 60g.

[0037] The synthesis sequence of the polymer automatic adhesive coating explosion-proof sealing rubber powder proposed by the present invention is as follows: use material crushing equipment to crush the solid material into <150 mesh particles; use continuous mixing equipment to uniformly mix the crushed solid material and liquid material , after mixing evenly, measure and pack into bags. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to automatic adhering wrapping explosion-prevention polymer sealing rubber powder for improving vehicle tire performances. The automatic adhering wrapping explosion-prevention polymer sealing rubber powder comprises, by weight, 40-50% of a thermoplastic elastomer, 40-50% of a tackifier, 5-8% of a plasticizer, 0.5-1.5% of an anti-aging agent, 3-5% of a filler, and 1-3% of a foaming agent. With the technical scheme, the ordinary vehicle tire can be upgraded to the vehicle tire with characteristics of high-temperature resistance, low-temperature resistance, bullet resistance, leakage resistance and puncture resistance.

Description

technical field [0001] The invention relates to a polymer rubber powder, in particular to a polymer self-adhering explosion-proof sealing rubber powder for improving the performance of automobile tires. Background technique [0002] At present, there are two types of car wheels used in vehicles, one with inner tubes and the other without tubes. At present, almost all of the passenger vehicles use tubeless wheels. The country requires gradual promotion and use of heavy-duty vehicles. Tubeless car wheels. Tubeless car wheels have the advantages of good heat dissipation, softness, sealing and ride comfort, and long intervals between inflation and use. The high-pressure gas in the tire of the car tire will leak outwards or blow out at the punctured part; If there are two situations of tire or rapid leakage, the risk of automobile accidents is high, and the probability of car crashes and fatalities is high. [0003] Since the main technology in the market in the eighties of la...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J153/02C09J161/06C09J193/04C09J145/02C09J11/06C09J11/04
Inventor 周仁福王自新刘宽亮史惠娟周强
Owner LUOYANG JUNTENG ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com