Multifunctional water purification filling material

A water purification and multi-functional technology, applied in the field of multi-effect water purification fillers, can solve problems such as unfavorable human health and instability, and achieve the effect of strong stability and high stability

Active Publication Date: 2015-02-04
赵燕京
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is that after the water treatment material in the prior art is soaked for a long time, the pH value of the formed water exceeds the standard and becomes alkaline water or strong alkaline water, and the negative potential reaches above -250mv and is unstable. Harmful to human health, thereby providing a multifunctional water purification filler for forming healthy high-quality drinking water and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The multi-functional water-purifying filler provided in this embodiment, its components include 40g calcium-magnesium alloy balls and 60g tourmaline ceramic balls;

[0026] Wherein, the particle diameter of the tourmaline ceramic ball is 5 mm, which is prepared by the following method: respectively weigh 50 g of tourmaline powder with a particle diameter of 8000 mesh, 20 g of zeolite powder with a particle diameter of 320 mesh, and 15 g of zeolite powder with a particle diameter of 320 mesh. Purpose feldspar powder, 15g of pottery clay with a particle size of 320 mesh, mixed evenly, granulated and sintered at 1500°C to obtain the product;

[0027] The particle size of the calcium-magnesium alloy ball is 5 mm, which is prepared by the following method: Weigh the calcium and magnesium metal powders according to the molar ratio of 3:7 and mix them uniformly. , that is.

Embodiment 2

[0029] The multifunctional water-purifying filler provided in this embodiment, its components include: 60g calcium-magnesium alloy balls, 40g tourmaline ceramic balls, 40g medical stone, 25g wood fish stone, 10g black beryl, 15g tourmaline powder, 10g pottery clay, 15g loess, 25g antibacterial pottery, and described medical stone, wood fish stone, black beryl, tourmaline powder, pottery clay, loess, antibacterial pottery are all particle diameters and are 320 mesh powders;

[0030] Wherein, the particle diameter of the tourmaline ceramic ball is 3 mm, which is prepared by the following method: respectively weigh 50 g of tourmaline powder with a particle diameter of 8000 mesh, 20 g of zeolite powder with a particle diameter of 320 mesh, and 15 g of zeolite powder with a particle diameter of 320 mesh. Purpose feldspar powder, 15g of pottery clay with a particle size of 320 mesh, mixed evenly, granulated and sintered at 1700°C to obtain the product;

[0031] The particle size of ...

Embodiment 3

[0033] The multifunctional water-purifying filler provided in this embodiment includes: 50g calcium-magnesium alloy balls, 50g tourmaline ceramic balls, 50g medical stone, 20g wood fish stone, 15g black beryl, 10g tourmaline powder, 15g pottery clay, 10g loess, 20g antibacterial pottery, and described medical stone, wood fish stone, black beryl, tourmaline powder, pottery clay, loess, antibacterial pottery are all particle diameters and are 280 mesh powders;

[0034] Wherein, the particle diameter of the tourmaline ceramic ball is 5 mm, which is prepared by the following method: Weigh 60 g of tourmaline powder with a particle diameter of 8000 mesh, 15 g of zeolite powder with a particle diameter of 280 mesh, and 20 g of zeolite powder with a particle diameter of 350 mesh. Purpose feldspar powder, 10g of pottery clay with a particle size of 280 mesh, mixed evenly, granulated and sintered at 1600°C to obtain the product;

[0035] The particle size of the calcium-magnesium alloy ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a multifunctional water purification filling material, comprising a calcium-magnesium alloy ball and a tourmaline ceramic ball. The calcium-magnesium alloy ball has good stability, does not have considerable dissolved mineral matters after long-time soaking and generates a strong positive potential cloud in water to form a potential barrier, so the calcium-magnesium alloy ball absorbs hydroxide ions in water and enables hydrogen radical ions with positive potential to be left; at the same time, since the tourmaline energy ceramic ball can permanently release negative ions in water, the hydrogen radical ions in water are aggregated to form hydrogen in virtue of the negative ions released by the tourmaline energy ceramic ball, hydrogen runs out from water, and thus, hydroxide ions in water are stabilized and negatively ionized water is formed. Water treated by the multifunctional water purification filling material is rich in a plurality of mineral matters, has a pH value of 7.5 to 9.5, a small water molecule group and stable negative potential and meets standards of high-quality drinking water.

Description

technical field [0001] The invention relates to a multifunctional water purification filler, which belongs to the technical field of water purification. Background technique [0002] Water is the source of life, and water quality determines physique. With the development of science and technology and the progress of the times, the pollution of water sources is becoming more and more serious. However, with the acceleration of people's life rhythm and the improvement of life taste, health has become a problem that people pay more attention to. People's requirements for healthy water sources are increasing. The consumption of water sources with functional and health requirements is constantly increasing, and the tap water in cities is far from meeting the living and drinking standards of residents, and people's distrust of tap water is increasing year by year. In recent years, bottled water and bottled drinking water have developed rapidly, and functional water and beverages h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F1/66C02F1/46C02F1/68
Inventor 赵燕京
Owner 赵燕京