Welding wire made of Cr28 Ni48 W5 nickel base alloy
A nickel-based alloy and welding wire technology, applied in the field of alloys, can solve problems such as difficult deformation, poor processing plasticity, and low yield, and achieve the effects of improving plasticity, increasing fluidity, and improving oxidation resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0029] Example 1
[0030] In the nickel-based alloy welding wire of this embodiment, the alloy composition and mass percentage are C: 0.41%, Mn: 1.02%, Si: 0.57%, P: 0.02%, S: 0.02%, Cr: 28.32%, Ni: 49.58 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.81%, and the rest is iron.
[0031] The specific steps of the method for preparing the nickel-based alloy welding wire of this embodiment are as follows:
[0032] A. For alloy smelting, batching is carried out according to the composition and mass percentage of the alloy, and the raw materials after surface derusting and oil contamination are put into a vacuum induction furnace. After the charging is completed, vacuum is started until the pressure reaches 0.67Pa, and then electric heating is started. , The temperature is controlled at about 1600℃, and the vacuum degree is controlled at 0.1~1Pa. After the charge is melted, add an appropriate amount of massive graphite or other high-carbon materials for carbon-oxygen reaction. Afte...
Example Embodiment
[0039] Example 2
[0040] In the nickel-based alloy welding wire of this embodiment, the alloy composition and mass percentage are C: 0.45%, Mn: 1.18%, Si: 0.15%, P: 0.02%, S: 0.02%, Cr: 29.51%, Ni: 50.32 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.15%, and the rest is iron.
[0041] The preparation method of the nickel-based alloy welding wire of this embodiment is the same as that of the first embodiment.
Example Embodiment
[0042] Example 3
[0043] In the nickel-based alloy welding wire of this embodiment, the alloy composition and mass percentage are C: 0.42%, Mn: 1.12%, Si: 0.50%, P: 0.02%, S: 0.02%, Cr: 29.22%, Ni: 50.06 %, Co: 0.08%, Mo: 0.09%, Ti: 0.08%, Al: 0.07%, W: 4.53%, and the rest is iron.
[0044] The preparation method of the nickel-based alloy welding wire of this embodiment is the same as that of the first embodiment.
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap