A kind of cold mix type epoxy asphalt repair material and preparation method thereof

A technology of epoxy asphalt and repair materials, which is applied in building insulation materials, building components, buildings, etc., and can solve the problems of harmful asphalt fumes, difficult transportation, and high energy consumption in production

Inactive Publication Date: 2018-03-06
HUBEI UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Moreover, the epoxy asphalt aggregate that has been mixed must be transported from the mixing station to the construction site under the condition of heat preservation. Transportation is difficult. On the other hand, during the heating process of epoxy asphalt, asphalt fumes harmful to human body will be produced, which will have a great impact on the body of the constructor and the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cold mix type epoxy asphalt repair material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] The present invention provides a kind of preparation method of cold mix type epoxy asphalt repair material described in above-mentioned technical scheme, comprises the following steps:

[0057] a) Mix the asphalt described in the above technical solution with asphalt thinner, epoxy asphalt compatibilizer, and epoxy resin curing agent to obtain part A of the cold-mix epoxy asphalt repair material;

[0058] b) Mix the epoxy resin and epoxy diluent described in the above technical solution to obtain part B of the cold-mix epoxy asphalt repair material;

[0059] c) Mix part A of the cold-mix epoxy asphalt repair material with part B of the cold-mix epoxy asphalt repair material at room temperature to obtain a cold-mix epoxy asphalt repair material. The weight ratio of the B part is (0.5-5):1;

[0060] The steps a) and b) are not restricted in chronological order.

[0061] The present invention mixes the asphalt described in the above technical proposal with an asphalt dil...

Embodiment 1

[0083] Add 30g of asphalt, 10g of asphalt thinner xylene, 17g of epoxy asphalt compatibilizer epoxy octyl stearate and 10g of epoxy curing agent polyamide 650 into an ordinary reaction kettle at 80°C, and stir for 60min to obtain a cold mix type Part A of the epoxy bituminous repair material;

[0084] Add 8g of epoxy diluent 632 and 20g of epoxy resin into a reaction kettle at 80°C and stir for 45min to obtain part B of the cold-mix epoxy asphalt repair material;

[0085] Then the A part of the obtained cold-mix type epoxy asphalt repair material and the B part of the cold-mix type epoxy asphalt repair material are added in the normal temperature reaction kettle, stirred for 20min, and the mixed material obtained after mixing is cooled to room temperature to obtain Cold mix epoxy asphalt repair material.

[0086] The present invention carries out performance test to the cold mix type epoxy asphalt repair material that obtains, and test result is as table 1 and figure 1 Shown...

Embodiment 2

[0088] Add 30g of asphalt, 12g of asphalt diluent carbon tetrachloride, 15g of epoxy asphalt compatibilizer epoxy heptyl stearate and 12g of epoxy curing agent polyamide 650 into a common reactor at 50°C and stir for 100min to obtain Part A of cold-mix epoxy asphalt repair materials;

[0089] Add 8g of dodecyl glycidyl ether and 20g of epoxy resin into a reaction kettle at 80°C and stir for 45min to obtain part B of the cold-mix epoxy asphalt repair material;

[0090] Then add part A of the cold-mix epoxy asphalt repair material and part B of the cold-mix epoxy asphalt repair material into a normal temperature reaction kettle and stir for 20 minutes. After mixing evenly, the obtained mixture is cooled to room temperature to obtain a cold mix Epoxy asphalt repair material.

[0091] The present invention carries out the performance test of the cold mix type epoxy asphalt repair material obtained, and the test results are as shown in table 1, and table 1 is the cold mix type epo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a cold-mix epoxy asphalt repair material and a preparation method thereof. A cold-mix type epoxy asphalt repair material includes part A and part B; in parts by weight, the part A includes the following components: 100 parts of asphalt; 5 parts to 50 parts of asphalt thinner; 10 parts to 50 parts epoxy asphalt compatibilizer; 5 to 50 parts of epoxy resin curing agent; in parts by weight, the B part includes the following components: 40 to 100 parts of epoxy resin; 5 to 50 parts of Epoxy diluent; the weight ratio of part A to part B is (0.5-5):1. The cold-mix epoxy asphalt repair material provided by the invention has better construction fluidity at room temperature, and is easier to penetrate into cracks on the road surface for repair; and it can be stirred and used at normal temperature without heating and heat preservation for transportation.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a cold-mix epoxy asphalt repair material that can be stirred and used at normal temperature without heating and heat preservation transportation and a preparation method thereof. Background technique [0002] Epoxy asphalt is developed on the basis of ordinary asphalt. It has excellent high temperature stability, low temperature crack resistance, super fatigue resistance and excellent durability. The Marshall stability of the mixture obtained with stone can be More than 40KN, while the stability of ordinary asphalt concrete is only 8KN ~ 12KN, the difference is 4 to 5 times; the splitting strength can reach 4MPa, which is much higher than ordinary asphalt mixture, and the fatigue life is almost 10 times that of ordinary asphalt concrete ~ 30 times. Based on the excellent performance of epoxy asphalt, it is widely used in steel bridge deck pavement, tunnel pavement pav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L63/00C08K5/1515C04B26/26E01C7/20
Inventor 周威蒋涛王东怡田科曹志龙敖成鸿
Owner HUBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap