Biological enzyme wood and bamboo protective agent and its production and use method

A protective agent and biological enzyme technology, which is applied in the direction of wood impregnation, wood impregnation, wood processing appliances, etc., can solve the problems of insufficient resistance to loss, short drug effect period, corrosion inhibition of metal firmware, etc., and achieve good anti-mold and anti-corrosion effects. Simple production process and strong anti-degradation effect

Active Publication Date: 2017-01-04
ZHEJIANG FORESTRY UNIVERSITY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although chemical antifungal agents are effective, they are toxic to humans and the environment, and most countries have restricted or banned their use
Other fungicides such as boric acid and borax have low toxicity, but because of their poor loss resistance, the active ingredients are easy to lose, the efficacy period is short, and they will cause environmental pollution
Copper-containing protective agents and organic fungicide-type protective agents have gradually gained attention, and then found that copper-containing protective agents such as ammonia-soluble copper quaternary ammonium (ACQ), copper azole (CuAz) and copper dimethyl dithiocarbamate (CDDC) still exist Many problems, such as the potential harm of the metal component copper to the soil and aquatic environment; the inefficiency or ineffectiveness of the corrosion inhibition of metal firmware and the infringement of other bacteria such as mold; and the organic fungicide-type protective agent also has insufficient loss resistance and is easy to Water, photodegradation and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biological enzyme wood and bamboo protective agent and its production and use method
  • Biological enzyme wood and bamboo protective agent and its production and use method
  • Biological enzyme wood and bamboo protective agent and its production and use method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1 (contrasted with the corresponding raw material and weight ratio value of embodiment 1 in Table 1):

[0024] First, 0.05 parts of diammonium salt as an enzyme activator and 200 parts of potassium iodide as a fungicide substrate are dissolved in 9800 parts of phosphate-sodium phosphate buffer solution with a concentration of 0.1mol / L and a pH value of 4-6. Before use, add 0.05 part of sumac laccase with an activity of 0.5U / mg to the above mixture, and stir at 200-1000r / min at a speed of 25-30°C until completely dissolved to obtain this biological enzyme wood and bamboo protection agent .

Embodiment 2-8

[0025] All the other examples 2-8, the corresponding raw materials and the weight ratio value of the corresponding examples in the table are compared, and the same method as the example 1 is used to obtain the biological enzyme wood and bamboo protective agent, which can reach the technical effect described, wherein Embodiment 7 is preferred.

[0026] The protective agent prepared by the present invention adopts spraying, coating to the easily permeable wood and bamboo and its products.

[0027]

[0028] For wood and bamboo and its products that are difficult to penetrate, use normal pressure impregnation or vacuum pressure impregnation for 0.5-1.0 hours. The material treated with this protective agent has a resistance of more than 85% to bacteria such as Aspergillus niger, Trichoderma, Penicillium citrinum, and discoloration fungus, and the corrosion resistance to white rot fungi and brown rot fungi can reach a strong corrosion resistance level.

[0029] The mechanism of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a bio-enzyme wood and bamboo protective agent which is prepared from the following raw materials in parts by weight: 0.05-0.5 part of laccase with the activity of 0.5U / mg, 0.05-0.5 part of enzyme activator, 200-2000 parts of bactericide substrate and 8000-9800 parts of buffer solution with the concentration of 0.1mol / L and pH value of 4-6. A production method of the protective agent comprises the steps of mixing the rest three raw materials according to the proportion except the laccase, evenly stirring at the temperature of 25-30 DEG C, and feeding the laccase into the mixed solution before use; evenly stirring at the rotating speed of 200-1000r / min under the condition of 25-30 DEG C. When the bio-enzyme wood and bamboo protective agent is used, the wood, the bamboo and products of the wood and the bamboo can be treated in a way of spraying, coating, soaking, pressurizing or vacuum impregnation, and then reaction is carried out for 6-18 hours in the environment of 25-40 DEG C, so that the mould-proof and corrosion-resistant treatment for the wood and the bamboo can be completed. The bio-enzyme wood and bamboo protective agent is simple in production technology, low in cost, convenient to use, non-toxic, free from environment pollution, good in mould-proof and corrosion-resistant effects, high in flow-away resistance and degradability resistance, and lasting in effect.

Description

technical field [0001] The invention relates to a biological enzyme wood and bamboo protective agent for protecting wood and bamboo from mildew and corrosion by means of dipping and the like, and a production and use method thereof. Background technique [0002] As a biopolymer material, wood and bamboo are vulnerable to mold, decay, insects and discoloration caused by biological factors such as fungi and insects. Especially bamboo, due to the high content of sugar and starch in the bamboo tissue, it often reduces or even loses its original value due to mildew during processing, transportation and use, causing serious economic losses to the bamboo product industry. At present, physical treatments such as baking, steaming, microwave, soaking in water, fumigation, etc. or chemical agents such as pentachlorophenol and its sodium salt are mainly used to solve the problem of wood and bamboo mildew. Although chemical antifungal agents are effective, they are toxic to humans and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/02B27K3/50B27K3/52
Inventor 孙芳利鲍滨福张绍勇刘彬彬陈安良
Owner ZHEJIANG FORESTRY UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products