Chloroprene rubber-based pressure sensitive tape and preparation method thereof

A technology based on pressure-sensitive adhesive tape and chloroprene rubber, applied in the field of pressure-sensitive adhesive, can solve the problems of low viscosity, inability to be adhered together by stickies, easy to fall off, etc., to achieve the effect of improving the applicability

Active Publication Date: 2014-10-22
SUZHOU JINHE NEW MATERIAL
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problem to be solved: Ordinary rubber-based pressure-sensitive adhesive tape has a low viscosity, which cannot bond the adherend together well, or it is easy to fall off after use. Find a pressure-sensitive adhesive with a higher viscosity. bring

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] (1) Turn on the agitator, take 32kg of neoprene and 22kg of butadiene, mix and stir the neoprene and butadiene, and obtain the mixture after stirring evenly;

[0017] (2) Turn on the mixer and preheat the mixer. After stabilization, add the mixture obtained in step (1) into the mixer from the feeding port, and then add polyvinyl methyl 7kg of ether, 3kg of diethylenetriamine, and 6kg of acrylonitrile, mixed for 20 minutes, and the mixing temperature was 120°C;

[0018] (3) Add 4kg of glyoxal and 6kg of trimethylsilanol to the mixer from the feeding port, and mix for 15 minutes;

[0019] (4) After degluing, cut the neoprene-based pressure-sensitive adhesive into strips to prepare the neoprene-based pressure-sensitive adhesive tape.

[0020] The viscosity of the neoprene-based pressure-sensitive adhesive tape of Example 1 was measured, and the measurement standard was GB2798-1981, and the viscosity was 102.4 Pa·s.

[0021]

Embodiment 2

[0023] (1) Turn on the agitator, take 36kg of neoprene and 17kg of butadiene, mix and stir the neoprene and butadiene, and obtain the mixture after stirring evenly;

[0024] (2) Turn on the mixer and preheat the mixer. After stabilization, add the mixture obtained in step (1) into the mixer from the feeding port, and then add polyvinyl methyl 9kg of ether, 4kg of diethylenetriamine, and 8kg of acrylonitrile were mixed for 15 minutes at a mixing temperature of 120°C;

[0025] (3) Then add 7kg of glyoxal and 5kg of trimethylsilanol to the mixer from the feeding port, and mix for 10 minutes;

[0026] (4) After degluing, cut the neoprene-based pressure-sensitive adhesive into strips to prepare the neoprene-based pressure-sensitive adhesive tape.

[0027] The viscosity of the neoprene-based pressure-sensitive adhesive tape of Example 2 was measured, and the measurement standard was GB2798-1981, and the viscosity was 103.7 Pa·s.

Embodiment 3

[0029] (1) Turn on the agitator, take 39kg of neoprene and 19kg of butadiene, mix and stir the neoprene and butadiene, and obtain the mixture after stirring evenly;

[0030] (2) Turn on the mixer and preheat the mixer. After stabilization, add the mixture obtained in step (1) into the mixer from the feeding port, and then add polyvinyl methyl 5 kg of ether, 2 kg of diethylenetriamine, and 10 kg of acrylonitrile, mixed for 18 minutes, and the mixing temperature was 120°C;

[0031] (3) Add 5kg of glyoxal and 6kg of trimethylsilanol to the mixer from the feeding port, and mix for 12 minutes;

[0032] (4) After degluing, cut the neoprene-based pressure-sensitive adhesive into strips to prepare the neoprene-based pressure-sensitive adhesive tape.

[0033] The viscosity of the neoprene-based pressure-sensitive adhesive tape of Example 3 was measured, and the measurement standard was GB2798-1981, and the viscosity was 104.9 Pa·s.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a chloroprene rubber-based pressure sensitive tape, which comprises the following components by weight ratio: 32-39 parts of chloroprene rubber, 17-22 parts of butadiene, 5-9 parts of polyvinyl methyl ether, 2-4 parts of diethylenetriamines, 6-10 parts of acrylonitrile, 4-7 parts of glyoxal and 5-6 parts of hydroxytrimethylsilane. A preparation method of the chloroprene rubber-based pressure sensitive tape comprises the following steps: 1)taking chloroprene rubber and butadiene, uniformly mixing chloroprene rubber and butadiene with stirring to obtain a mixture; 2)adding the mixture obtained in the step 1) in a mixing roll from a feed inlet, adding polyvinyl methyl ether, diethylenetriamines and acrylonitrile for mixing in the mixing roll from the feed inlet; 3)adding glyoxal and hydroxytrimethylsilane in the mixing roll and then mixing; and 4)cutting a chloroprene rubber-based pressure sensitive adhesive to obtain the pressure sensitive tape.

Description

technical field [0001] The invention belongs to the field of pressure-sensitive adhesives, and relates to a pressure-sensitive adhesive tape and a preparation method thereof, in particular to a neoprene-based pressure-sensitive adhesive tape and a preparation method thereof. Background technique [0002] Pressure-sensitive adhesive is an adhesive that is sensitive to pressure. When the pressure-sensitive adhesive is pressed by an external force, the pressure-sensitive adhesive will bond with the adherend and is not easy to fall off. Typically, pressure-sensitive adhesive tapes are bonded to related materials, such as films, circuit boards, etc. [0003] There are also many types of pressure-sensitive adhesives, mainly rubber-based pressure-sensitive adhesives and resin-based pressure-sensitive adhesives. Among them, rubber pressure-sensitive adhesives are divided into natural rubber pressure-sensitive adhesives and synthetic rubber pressure-sensitive adhesives. With th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/00C09J4/06C09J11/06
Inventor 陈鑫
Owner SUZHOU JINHE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com