Preparation method of anti-stripping packing material

A packaging material, anti-peeling technology, applied in packaging, wrapping paper, transportation and packaging, etc., can solve the problems of easy separation of the composite layer of film packaging materials and low peel strength

Active Publication Date: 2014-10-29
江西春光新材料科技股份有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Technical problems to be solved: The peel strength of conventional film packaging materials is low, and the composite layer of film packaging materials is easy to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] (1) Adjust the temperature of the reaction tank to 120°C, take 14kg of polyamide fiber, 10kg of polyparabenamide, 5kg of succinimide, and 12kg of polyisobutylene. , succinimide and polyisobutylene are all put into the reaction tank, keep the temperature constant and react for 1h; The pressing temperature is divided into three sections, the temperature of the first section is 140°C, the temperature of the second section is 180°C, and the temperature of the third section is 220°C. The high-group material mixture is extruded through twin-screws; (3) the extruded The polymer material is hot-calendered, and the hot-calendering temperature is 130°C, and the mixed material is rolled into a film with a thickness of 0.1mm; (4) The mixed film material obtained in step (3) is then hot-pressed with polypropylene, and then hot-pressed. The pressing temperature is 120° C.; (5) Natural cooling after hot pressing is the prepared anti-peeling packaging material.

[0023]

Embodiment 2

[0025] (1) Adjust the temperature of the reaction tank to 110°C, take 19kg of polyamide fiber, 6kg of polyparabenamide, 7kg of succinimide, and 9kg of polyisobutylene, and mix polyamide fiber, polyparabenamide , succinimide and polyisobutylene are all put into the reaction tank, keep the temperature constant and react for 2h; The pressing temperature is divided into three sections, the temperature of the first section is 160°C, the temperature of the second section is 180°C, and the temperature of the third section is 190°C. The high-group material mixture is extruded through twin-screws; (3) the extruded The polymer material is hot-calendered, and the hot-calendering temperature is 130°C, and the mixed material is rolled into a film with a thickness of 0.05mm; (4) The mixed film material obtained in step (3) is then hot-pressed with polypropylene, and the heat The pressing temperature is 120° C.; (5) Natural cooling after hot pressing is the prepared anti-peeling packaging ma...

Embodiment 3

[0028] (1) Adjust the temperature of the reaction tank to 90°C, take 17kg of polyamide fiber, 8kg of polyparabenamide, 6kg of succinimide, and 10kg of polyisobutylene, and mix polyamide fiber, polyparabenamide , succinimide and polyisobutylene are all put into the reaction tank, keep the temperature constant and react for 1h; The pressing temperature is divided into three sections, the temperature of the first section is 140°C, the temperature of the second section is 170°C, and the temperature of the third section is 190°C. The high-group material mixture is extruded through twin-screws; (3) the extruded The polymer material is hot-calendered, and the hot-calendering temperature is 130°C, and the mixed material is rolled into a film with a thickness of 0.1mm; (4) The mixed film material obtained in step (3) is then hot-pressed with polypropylene, and then hot-pressed. The pressing temperature is 120° C.; (5) Natural cooling after hot pressing is the prepared anti-peeling pack...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Peel forceaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of an anti-stripping packing material. The preparation method of the anti-stripping packing material comprises the following steps of firstly, taking polyamide fiber, poly-p-benzamide fiber, succinimid and polyisobutene, putting the polyamide fiber, the poly-p-benzamide fiber, the succinimide and the polyisobutene into a reaction tank, and keeping the temperature constant for the reaction; secondly, taking a high polymer material mixture out of the reaction tank after the reaction, and performing double-screw extrusion to extrude out the high polymer material mixture through double screws; thirdly, performing thermal rolling on the extruded high polymer material mixture and enabling a mixed material to form a film through rolling; fourthly, performing thermal compression bonding on the mixed film material obtained in the third step and polypropylene; fifthly, performing natural cooling after the thermal compression bonding so as to obtain the anti-stripping packing material.

Description

technical field [0001] The invention belongs to the field of polymer materials, and relates to a preparation method of a packaging material, in particular to a preparation method of an anti-peeling packaging material. Background technique [0002] During the use of film packaging materials, the anti-peeling performance, retort resistance performance and puncture resistance performance of film packaging materials are very important. The anti-stripping performance is too poor. During use, when an external force is encountered, the interaction between the composite layers will be reduced, resulting in the separation of the composite layers. Under normal circumstances, some composite layers are bonded by adhesives, and some composite layers are bonded by hot pressing at high temperature. [0003] Conventional composite-layer film packaging materials have low peel strength, which cannot satisfy practical applications. Therefore, we need to change the preparation process of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B65D65/40B65D65/02C08L77/00C08L77/10C08L23/20B29C69/00B29C47/92B29C43/24B32B37/06B32B37/10B29C48/92
Inventor 张太元
Owner 江西春光新材料科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap