A papermaking surface sizing agent emulsified by magnetic composite particles and its preparation method

A technology of surface sizing agent and particle emulsification, which is applied in the field of papermaking, can solve the problems of AKD emulsification process complexity, environmental pollution, and difficult control, and achieve the effects of avoiding adverse effects, reducing costs, and improving pollution

Inactive Publication Date: 2016-10-05
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Starch needs to be gelatinized and cooled before use, which makes the AKD emulsification process quite complicated and difficult to control, and often causes problems such as deposition and clogging of blankets
The surfactant also brings certain adverse effects to sizing, and also brings certain pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A papermaking surface sizing agent emulsified by magnetic composite particles, the preparation method of which is as follows:

[0038] (1) Nano-Fe 3 o 4 Granular and Nano SiO 2 The particles were mixed according to the mass ratio of 1:1, and heated and stirred in a water bath at 50°C for 2 hours to obtain silicon dioxide-coated iron ferric oxide nano-solid particles; Disperse ferric oxide nano-solid particles in deionized water, stir evenly to obtain a suspension, adjust the pH value of the suspension to 7 with 0.1mol / L hydrochloric acid, and obtain a well-dispersed, precipitate-free magnetic composite particle suspension after stirring evenly ; Wherein, the mass fraction of ferric iron tetroxide nanometer solid particles coated with silicon dioxide in the magnetic composite particle suspension is 1%;

[0039](2) Add hexadecyl ketene dimer to the reaction kettle, slowly add polyvinyl alcohol, raise the temperature to 80°C to make the additive in the reaction kettle i...

Embodiment 2

[0046] A papermaking surface sizing agent emulsified by magnetic composite particles, the preparation method of which is as follows:

[0047] (1) Nano-Fe 3 o 4 Granular and Nano SiO 2 The particles were mixed according to the mass ratio of 1:1, heated and stirred in a water bath at 60°C for 2 hours to obtain silicon dioxide-coated iron ferric oxide nano-solid particles; Disperse iron oxide nanometer solid particles in deionized water, stir evenly to obtain a suspension, adjust the pH value of the suspension to 8 with 0.1mol / L sodium acetate solution, and obtain well-dispersed, non-precipitating magnetic composite particles after stirring evenly Suspension; wherein, the mass fraction of ferric oxide nanometer solid particles coated with silicon dioxide in the magnetic composite particle suspension is 2%;

[0048] (2) Add the tetradecyl ketene dimer to the reaction kettle, slowly add polyvinyl alcohol, raise the temperature to 85°C to make the additive in the reaction kettle ...

Embodiment 3

[0055] A papermaking surface sizing agent emulsified by magnetic composite particles, the preparation method of which is as follows:

[0056] (1) Nano-Fe 3 o 4 Granular and Nano SiO 2 The particles were mixed according to the mass ratio of 2:1, and heated and stirred in a water bath at 40°C for 2 hours to obtain silicon dioxide-coated iron ferric oxide nano-solid particles; Disperse ferric oxide nanometer solid particles in deionized water, stir evenly to obtain a suspension, adjust the pH value of the suspension to 9 with 0.1mol / L sodium hydroxide solution, and obtain a well-dispersed, precipitation-free magnetic complex after stirring evenly Particle suspension; wherein, the mass fraction of ferric oxide nanometer solid particles coated with silicon dioxide in the magnetic composite particle suspension is 3%;

[0057] (2) Add the dodecyl ketene dimer to the reaction kettle, slowly add polyvinyl alcohol, raise the temperature to 85°C to make the additive in the reaction ke...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
electrical resistivityaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of papermaking, and discloses a papermaking surface sizing agent emulsified by magnetic composite particles and a preparation method thereof. The preparation method is as follows: (1) dispersing ferric ferric oxide nanometer solid particles coated with silicon dioxide in In water, stir evenly to obtain a suspension, adjust the pH value of the suspension to obtain a suspension of magnetic complex particles; (2) Add the alkyl ketene dimer to the reaction kettle, then add polyvinyl alcohol, and heat up to make the additive into a liquid state, insulated and stirred to obtain the modified alkyl ketene dimer sizing oil; (3) heating the magnetic composite particle suspension in a water bath, then adding the modified alkyl ketene dimer sizing oil, After mixing, heat-preserve and emulsify to obtain the papermaking surface sizing agent emulsified by the magnetic composite particles. The paper-making surface sizing agent emulsion is stable, has high sizing efficiency, and can endow paper with water resistance and magnetism; the method does not need to add surfactants, uses less emulsifiers, is low in cost, low in pollution and short in curing time.

Description

technical field [0001] The invention belongs to the technical field of papermaking and relates to paper sizing technology, in particular to a papermaking surface sizing agent emulsified by magnetic composite particles and a preparation method thereof. Background technique [0002] Neutral sizing is a major progress in modern sizing technology, which greatly improves paper quality, expands the range of fillers, reduces pulp consumption, energy consumption, reduces environmental pollution, and prolongs the service life of equipment. inevitable development trend. According to statistics, Europe introduced cationic alkyl ketene dimer (AKD) neutral sizing in Europe in the 1970s. China has only conducted systematic research on it since the 1980s, and began to use medium and alkaline sizing in production, which has gradually become popular in recent years. Currently, alkyl ketene dimer (AKD) and alkenyl succinic Anhydride (ASA)-based. AKD is a reactive medium-alkaline sizing age...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21H21/16
Inventor 林兆云李友明
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap