A glass manufacturing and anti-fingerprint technology, applied in the field of wear-resistant and anti-fingerprint glass, can solve the problems of low hardness, weak toughening performance, and easy to form dirt, etc., achieve good anti-fingerprint effect, improve chemical resistance, and surface high intensity effect

Inactive Publication Date: 2015-01-21
昆山濡鑫光电科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Computers have been widely used in people's lives. Both tablet computers and notebook computers are traditionally made of plexiglass materials. The tempering performance is not strong and the hardness is not high. Hands are easy to form dirt, fingerprints, and wipe easily. Defective appearance such as abrasions and scratches

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) One-time cleaning: use 5% detergent by mass and glass water with 5% by mass, and the treatment time is 10s;

[0029] 2) Strengthening: place the cleaned glass at a temperature of 150°C for 24 hours;

[0030] 3) Secondary cleaning: use 5% detergent by mass and glass water with 5% by mass, and the treatment time is 10s;

[0031] 4) Descaling: Treat the glass after the second cleaning with a plasma spray gun for 10s;

[0032] 5) Anti-fingerprint treatment: use AF-102 solution, spray it on the front of the glass according to the flow rate of 2.7g / s, and then bake it at 150°C for 30min to obtain the product.

[0033] The product coating of the product obtained in this embodiment does not fall off after being rubbed back and forth 100 times with 200kg strength by steel wool, and the water drop angle on the product surface reaches more than 100°.

Embodiment 2

[0035] 1) One-time cleaning: use 8% detergent by mass and glass water with 10% by mass, and the treatment time is 10s;

[0036] 2) Strengthening: heat-preserve the cleaned glass at 200°C for 20 hours;

[0037] 3) Secondary cleaning: use 8% detergent by mass and 10% glass water by mass, and the treatment time is 10s;

[0038] 4) Printing: Print UV ink on the glass surface after secondary cleaning;

[0039] 5) Descaling: Treat the printed glass with a plasma spray gun for 20s;

[0040] 6) Anti-fingerprint treatment: use AF-102 solution, spray it on the front of the glass according to the flow rate of 3.0g / s, and then bake it at 120°C for 40min;

[0041] 7) Adhesive adhesive: paste double-sided adhesive on the back of the glass after anti-fingerprint treatment to obtain the product.

[0042] The coating of the product obtained in this embodiment does not fall off after being rubbed back and forth 100 times with 200kg of strength by steel wool, and the water drop angle on the s...

Embodiment 3

[0044] 1) One-time cleaning: use 6% detergent by mass and 8% glass water by mass, and the treatment time is 10s;

[0045] 2) Strengthening: heat-preserve the cleaned glass at 180°C for 22 hours;

[0046] 3) Secondary cleaning: use detergent containing 6% by mass and glass water with 8% by mass, and the treatment time is 10s;

[0047] 4) Printing: Print mirror ink on the glass surface after secondary cleaning;

[0048] 5) Descaling: Treat the printed glass with a plasma spray gun for 15s;

[0049] 6) Anti-fingerprint treatment: use AF-102 solution, spray it on the front of the glass according to the flow rate of 2.8g / s, and then bake it at 140°C for 35min to obtain the product.

[0050] The product coating obtained in this embodiment does not fall off after being rubbed back and forth 100 times with 200kg strength by steel wool, and the water drop angle on the product surface reaches more than 100°, and the mirror ink can make the glass have a mirror effect.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for making abrasion-resistant anti-fingerprint glass. The method sequentially comprises the following steps of: carrying out primary cleaning on a glass substrate, then strengthening at the temperature of 150-200 DEG C for 20-24 hours, and then carrying out secondary cleaning; then descaling by using a plasma spray gun; finally carrying out anti-fingerprint treatment by using an AF-102 anti-fingerprint coating agent to obtain a product. The glass made through the method disclosed by the invention has the advantages of good abrasion-resistant property and good anti-fingerprint property.

Description

【Technical field】 [0001] The invention relates to the technical field of glass surface treatment, in particular to a method for manufacturing wear-resistant and anti-fingerprint glass. 【Background technique】 [0002] Computers have been widely used in people's lives. No matter tablet computers or notebook computers, they are traditionally made of plexiglass materials. The tempering performance is not strong and the hardness is not high. Hands are easy to form dirt, fingerprints, and wipe easily. Appearance defects such as scratches and scratches appear. Now it is made of glass, in order to completely improve the above defects and finally commercialize the glass protective screen, it is necessary to provide a new method of manufacturing wear-resistant and anti-fingerprint glass. 【Content of invention】 [0003] The main purpose of the present invention is to provide a method for manufacturing wear-resistant and anti-fingerprint glass. [0004] The present invention achieve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03B27/012C03C17/00C03C23/00
CPCC03B27/012C03C17/002C03C17/34C03C23/006C03C2217/72C03C2217/78C03C2218/112C03C2218/32C03C2218/365
Inventor 吕俊民
Owner 昆山濡鑫光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap