Anti-acid steel plate for storage equipment and preparation method of anti-acid steel plate
A steel plate and equipment technology, which is applied in the field of acid-resistant steel plate for storage equipment and its preparation, can solve the problems of corrosion storage equipment, storage equipment damage, increase storage costs, etc., and achieve good strength, toughness, acid resistance and low cost.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0055] This embodiment is an acid-resistant steel plate used for storage equipment. The composition and mass percentage of the steel plate are: C: 0.31%, Mn: 0.45%, Si: 0.07%, P: 0.006%, S: 0.002%, Nb : 0.06%, V: 0.07%, Ti: 0.05%, Al: 0.08%, N: 0.006%, H: 0.00020%, Cu: 0.012%, Cr: 0.4%, Mo: 0.23%, the balance is Fe and not Impurities to avoid;
[0056] In the steel plate of this embodiment, the first phase is ferrite, and the second phase is pearlite. The volume percentage of the second phase from the surface to 1 / 4 thickness is 2.5%, and the volume percentage of the second phase from 1 / 4 thickness to the center is 7.0%, and no band structure; the average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate in this embodiment is 3.5 μm, the average diameter of pearlite clusters is 6.0 m, and the ferrite from 1 / 4 thickness to the center The average grain diameter of the vrite is 5.0 μm, and the average diameter of the pearlite group is 7.0 μm.
[005...
Embodiment 2
[0069] The acid-resistant steel plate used for storage equipment in this embodiment, the composition and mass percentage of the steel plate are: C: 0.32%, Mn: 0.46%, Si: 0.08%, P: 0.007%, S: 0.003%, Nb: 0.07 %, V: 0.08%, Ti: 0.06%, Al: 0.09%, N: 0.002%, H: 0.0001%, Cu: 0.013%, Cr: 0.5%, Mo: 0.24%, the balance is Fe and unavoidable impurities;
[0070] In the steel plate of this embodiment, the first phase is ferrite, and the second phase is pearlite. The volume percentage of the second phase from the surface to 1 / 4 thickness is 2.6%, and the volume percentage of the second phase from 1 / 4 thickness to the center is 7.3%, and no band structure;
[0071] The average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate in this embodiment is 3.6 μm, the average diameter of pearlite clusters is 6.2 μm, and the average grain diameter of ferrite from 1 / 4 thickness to the center is 5.2 μm , The average diameter of the pearlite group is 7.2 μm.
[0072]The p...
Embodiment 3
[0084] The acid-resistant steel plate used for storage equipment in this embodiment, the composition and mass percentage of the steel plate are: C: 0.33%, Mn: 0.47%, Si: 0.09%, P: 0.008%, S: 0.005%, Nb: 0.08 %, V: 0.09%, Ti: 0.07%, Al: 0.1%, N: 0.002%, H: 0.00012%, Cu: 0.015%, Cr: 0.6%, Mo: 0.25%, the balance is Fe and unavoidable impurities;
[0085] In the steel plate of this embodiment, the first phase is ferrite, and the second phase is pearlite. The volume percentage of the second phase from the surface to 1 / 4 thickness is 2.8%, and the volume percentage of the second phase from 1 / 4 thickness to the center is 7.5%, and no band structure; the average grain diameter of ferrite from the surface to 1 / 4 thickness of the steel plate in this embodiment is 3.7 μm, the average diameter of pearlite clusters is 6.3 μm, and the ferrite from 1 / 4 thickness to the center The average grain diameter of the vrite body is 5.3 μm, and the average diameter of the pearlite group is 7.3 μm.
...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com