Nylon fibers and preparation method thereof

A technology of nylon fiber and nylon, applied in fiber processing, melt spinning, single-component copolyamide rayon, etc., can solve the problems of increased production process, long process cycle, high molecular weight, etc., to reduce production cost, operate The effect of simple process and excellent tensile strength

Active Publication Date: 2015-04-29
CATHAY R&D CENT CO LTD +1
View PDF8 Cites 66 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent Document 3 (CN200980118941.2) obtained PA56 filaments that can be used to prepare airbags through boiling water treatment. This preparation method not only increases the production process, but also uses a prepolymerized reinforcement phase to obtain nylon 56 with high molecular weight and narrow distribution. The way of polymerization makes the whole process cycle long and energy-consuming

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nylon fibers and preparation method thereof
  • Nylon fibers and preparation method thereof
  • Nylon fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The preparation method of the nylon fiber of the present invention includes direct spinning after polymerizing raw materials containing 1,5-pentanediamine and adipic acid.

[0043] There are two main ways to realize the industrialization of nylon polymerization process, one is continuous polymerization process, and the other is batch polymerization process. In the present invention, there is no limitation on the way to realize the polymerization reaction of 1,5-pentanediamine and adipic acid, and it can be realized by any one of the above two processes.

[0044] In the preparation method of the nylon fiber of the present invention, the polymerization reaction further includes the following steps: 1) making 1,5-pentanediamine and adipic acid into a nylon salt solution; 2) concentrating the nylon salt solution; 3) Precondensing the concentrated nylon salt solution to obtain a prepolymer; 4) further dehydrating and polymerizing the prepolymer to obtain a nylon 56 melt.

...

Embodiment 1

[0131] Mix 1,5-pentamethylenediamine and adipic acid into 5 tons of 60% aqueous solution in the salt-forming kettle 1, adjust the pH value to 7.6 (dilute the salt solution to 10% test result), control the temperature at 50°C, and pass through the filter Transfer to the intermediate tank 2, then heat up to 90°C by the first preheater 3, and then enter the concentration tank 4 to further concentrate to 80% concentration, the outlet temperature of the concentration tank 4 is 120°C, and the solution passes through the second preheater 5 After further heating to 213°C, it enters the reactor 6. The pressure of the reactor 6 is 1.73MPa, and the outlet temperature is controlled at 240°C. The steam is recovered and reused through the cooling tower. The reaction liquid then enters the flash evaporator 8 to remove most of the water, and the pressure drops to Atmospheric pressure. Finally, the polymerization reaction is completed through the front polymerizer 9 and the rear polymerizer 10...

Embodiment 2

[0134] Mix 1,5-pentamethylenediamine and adipic acid into 5 tons of 60% aqueous solution in salt forming kettle 1, adjust the pH value to 7.6 (dilute the salt solution to 10% test result), add 5% nylon 56 salt weight Nylon 66 salt, the temperature is controlled at 50°C, transferred to the intermediate tank 2 through the filter, and then heated by the first preheater 3 to 90°C, then enters the concentration tank 4 to further concentrate to 80% concentration, and the concentration tank 4 exits The temperature is 120°C. The solution is further heated to 213°C by the second preheater 5 and then enters the reactor 6. The pressure of the reactor 6 is 1.73MPa, and the outlet temperature is controlled at 240°C. The steam is recovered and reused through the cooling tower, and the reaction liquid is subsequently Enter the flash evaporator 8 to remove most of the moisture, and the pressure drops to normal pressure. Finally, the polymerization reaction is completed through the front and r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of nylon fibers. The preparation method comprises the following steps: directly spinning after taking raw materials containing 1,5-pentamethylene diamine and adipic acid to react. The invention further provides the nylon fibers prepared by the method. The method adopts a manner of combining nylon polymerization and fusion direct spinning to prepare nylon 56 wires so that the production cost is reduced, the waste gas is reduced and the pollution to the environment is reduced. The high-performance nylon fibers prepared by the method can be further used for preparing textile materials including yarns, woven fabrics, knitted fabrics or non-woven fabrics, can be widely applied to the fields of clothing material industries, decoration carpets and the like, and has a wide industrial application prospect.

Description

technical field [0001] The invention relates to a nylon fiber and a preparation method thereof, in particular to a nylon 56 fiber and a preparation method thereof. Background technique [0002] Nylon fiber is one of the first synthetic fibers put into industrial production in the world, and its output ranks second among synthetic fibers. Nylon low-denier yarn (200-700dtex) has the characteristics of high breaking strength, wear resistance, fatigue resistance, impact resistance, and good dimensional stability. It is widely used in military products, rubber skeleton materials, airbag wires and ropes, nets, cables fabrics, tarpaulins, industrial filter cloths and other fields; at the same time, because of its soft hand feeling, light texture, good drapability, breathable moisture absorption, good elasticity, easy processing and other good wearability, it is used in high-grade sewing thread silk, T-shirt silk, Umbrella fabrics, sports textiles and other fields have good market ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/60D01F6/80C08G69/28D01D11/00
CPCC08G69/28D01D1/00D01D5/08D01F6/60D01F6/80Y02P20/582
Inventor 刘驰秦兵兵郑毅
Owner CATHAY R&D CENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap