A technology of intrauterine adhesions and gel materials, applied in the field of medical materials, can solve the problems of difficult full coverage of wounds and complicated manipulation of anti-uterine adhesions materials, and achieve the effect of full coverage of wounds, good fluidity and uniform coating

Active Publication Date: 2017-08-11
广州市弘健生物医用制品科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the defects of the existing anti-uterine adhesion materials which are complicated to operate and difficult to fully cover the wound surface, and provide people with an anti-uterine adhesion material with good fluidity, uniform coating, and fast and comprehensive coverage of the wound surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The anti-uterine adhesion material in this example is a temperature-sensitive gel, and the phase transition temperature of the temperature-sensitive gel is 25°C to 40°C.

[0029] The temperature-sensitive gel is composed of a gel body, a humectant, a gelling temperature regulator and pure water. The gel body is poloxamer 407, which accounts for 20% of the total temperature-sensitive gel. The moisturizer is glycerin, which accounts for 20% of the temperature-sensitive gel The mass fraction of the total gel is 5%, the gelling temperature regulator is poloxamer 188, which accounts for 5% of the total temperature-sensitive gel, and the rest is pure water.

[0030] The preparation method of the anti-uterine adhesion material in this example is as follows:

[0031] Disperse Poloxamer 407 and Poloxamer 188 in a container filled with a certain amount of pure water and stir until dissolved; add glycerin to the remaining amount of pure water and dissolve to obtain a glycerin solu...

Embodiment 2

[0033] The anti-uterine adhesion material in this example is a temperature-sensitive gel, and the phase transition temperature of the temperature-sensitive gel is 25°C to 40°C.

[0034] The temperature-sensitive gel is composed of a gel body, a tissue affinity agent, a moisturizing agent, a gelling temperature regulator and pure water; the gel body is poloxamer 407, which accounts for 15% of the total temperature-sensitive gel; The mixture is sodium hyaluronate, which accounts for 0.2% of the total temperature-sensitive gel; the moisturizing agent is glycerin, which accounts for 5% of the total temperature-sensitive gel; the gelling temperature regulator is poloxamer 188, which accounts for The mass fraction of the total amount of glue is 10%, and the rest is pure water.

[0035] The preparation method of the anti-uterine adhesion material in this example is as follows:

[0036] Disperse Poloxamer 407 and Poloxamer 188 in a container filled with a certain amount of pure water...

Embodiment 3

[0038] The anti-uterine adhesion material in this example is a temperature-sensitive gel, and the phase transition temperature of the temperature-sensitive gel is 25°C to 40°C.

[0039] The temperature-sensitive gel is composed of a gel body, a tissue affinity agent, a moisturizing agent, a gelling temperature regulator, and pure water; the gel body is poloxamer 407, which accounts for 25% of the total temperature-sensitive gel; The mixture is hyaluronic acid, accounting for 0.1% of the total temperature-sensitive gel; the moisturizing agent is glycerin, accounting for 10% of the total temperature-sensitive gel; the gelling temperature regulator is Poloxamer 188, accounting for 10% of the total temperature-sensitive gel The mass fraction of the total amount is 10%, and the rest is pure water.

[0040] The preparation method of the anti-uterine adhesion material in this example is as follows:

[0041] Disperse Poloxamer 407 and Poloxamer 188 in a container filled with a certai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
phase transition temperatureaaaaaaaaaa
phase transition temperatureaaaaaaaaaa
phase transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses an intrauterine adhesion prevention material, and belongs to the field of medical materials. The intrauterine adhesion prevention material is characterized in that the intrauterine adhesion prevention material is a temperature-sensitive gel; the phase transition temperature of the temperature-sensitive gel is 25-40 degrees; the temperature-sensitive gel consists of a gel main body, a tissue affinity agent, a humectant, a gelling temperature regulation agent and pure water; the gel main body is one or several of poloxamer 407, a polylactide acid / glycolic acid / polyethylene glycol copolymer, poly(N-isopropylacrylamide), chitosan, sodium beta-glycerophosphate, methoxy polyethylene glycol-(sebacic acid-D,L-lactic acid)polyester anhydride-methoxy polyethylene glycol triblock copolymer, cellulose, a cellulose derivative, and polyethylene glycol / polycaprolactone block copolymer; the tissue affinity agent is hyaluronic acid or sodium hyaluronate; the humectant is glycerol or sodium alginate; and the gelling temperature regulation agent is poloxamer 188 or polyethylene glycol. The intrauterine adhesion prevention material provided for people is good in liquidity and can be coated uniformly, and the surface of a wound can be covered quickly and completely.

Description

[0001] Technical field: [0002] The invention belongs to the field of medical materials, and in particular relates to an anti-uterine cavity adhesion material. [0003] Background technique: [0004] Intrauterine adhesions are a disease that endangers women's health. It mainly causes abdominal pain, infertility, menstrual disorders and other diseases. In addition to natural factors, many human interventions can lead to the occurrence of intrauterine adhesions: such as induced abortion, uterine Intracavitary surgery, etc., and the hysteroscopic surgery that is currently being widely implemented also increases the risk of intrauterine adhesions to a greater extent. Therefore, prevention of intrauterine adhesions is very necessary. [0005] Because intrauterine adhesions are more harmful to women, many materials have been used to prevent intrauterine adhesions: water bags or air bags are used to put them into the uterine cavity after intrauterine surgery. The water or gas in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L31/14A61L31/06A61L31/04
Inventor 朱晓明
Owner 广州市弘健生物医用制品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com