A kind of anti-aging steel surface coating material and preparation method thereof

A surface coating and anti-aging technology, applied in the direction of coating, etc., can solve the problems of poor scratch resistance, formaldehyde content, insufficient scratch resistance, etc., achieve good mechanical strength and scratch resistance, and be easy to industrialize Good production and surface gloss

Active Publication Date: 2017-02-08
江苏悠谷未来科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, in many fields, especially the automobile field, the demand for metallic paint is increasing, and the existing metallic paint contains formaldehyde, which will affect human health during use
At the same time, the existing metallic paint is not enough in terms of scratch resistance, so that a slight scratch will leave irreversible scratches on the paint surface
[0004] Chinese patent CN101215438A discloses an anti-fouling and anti-aging stainless steel coating and its preparation method. The coating is formed by mixing acrylic resin, film former, filler, solvent and auxiliary agent, wherein the film former includes fluororesin, water-based polyurethane, Epoxy resin, the filler contains nano-silica, the prepared coating has good aging resistance and UV resistance, but its scratch resistance is not good, which affects its service life and comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Weigh 3kg of alumina nano powder, 0.2kg of triglycidyl isocyanurate and 0.08kg of ethylene bisstearamide, add them to a grinder, and grind for 5 minutes;

[0031] (2) Add 25kg of methyl methacrylate, 11kg of polystyrene with a water absorption rate of 0.03 and 0.5kg of dimethylsiloxane to the ground material, and in the high mixer, at 98°C, at 1780 rpm / min Mix evenly to get the mixed material;

[0032] (3) Mix 5 kg of n-butanol and 105 kg of water evenly, add the mixed material described in step 2, and stir evenly to obtain an aging-resistant steel surface coating material.

[0033] The performance test results of the prepared aging-resistant steel surface coating materials are shown in Table 1.

Embodiment 2

[0035] (1) Weigh 3kg of alumina nano-powder, 0.4kg of triglycidyl isocyanurate and 0.08kg of ethylene bisstearamide, add them to a grinder, and grind for 5 minutes;

[0036] (2) Add 25kg of methyl methacrylate, 11kg of polystyrene with a water absorption rate of 0.03 and 0.8kg of dimethylsiloxane to the ground material, and in the high mixer, at 98°C, at 1815 rpm / min Mix evenly to get the mixed material;

[0037] (3) Mix 5 kg of n-butanol and 105 kg of water evenly, add the mixed material described in step 2, and stir evenly to obtain an aging-resistant steel surface coating material.

[0038] The performance test results of the prepared aging-resistant steel surface coating materials are shown in Table 1.

Embodiment 3

[0040] (1) Weigh 5kg of alumina nanopowder, 0.4kg of triglycidyl isocyanurate and 1.1kg of ethylene bisstearamide, add them to a grinder, and grind for 15 minutes;

[0041] (2) Add 38kg of methyl methacrylate, 14kg of polystyrene with a water absorption rate of 0.03 and 0.8kg of dimethylsiloxane to the ground material, and in the high mixer, at 115°C, at 1815 rpm / min Mix evenly to get the mixed material;

[0042] (3) Mix 8 kg of n-butanol and 121 kg of water evenly, add the mixed material described in step 2, and stir evenly to obtain an aging-resistant steel surface coating material.

[0043] The performance test results of the prepared aging-resistant steel surface coating materials are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ageing resistant steel surface coating material and preparation method thereof. The coating material is prepared from the following components in parts by weight: 25-38 parts of methyl methacrylate, 11-14 parts of polystyrene, 3-5 parts of aluminum oxide, 0.5-0.8 part of dimethyl siloxane, 0.2-0.4 part of triglycidyl isocyanurate, 0.08-1.1 part of ethylene bistearamide, 5-8 parts of n-butyl alcohol, and 105-121 parts of water. The invention further provides a preparation method of the ageing resistant steel surface coating material. The ageing resistant steel surface coating material prepared through the preparation method disclosed by the invention can be widely applied to the surfaces of household appliances, instruments, air purifying devices, and water purifying devices.

Description

technical field [0001] The invention belongs to the field of coating materials, in particular to an aging-resistant steel surface coating material and a preparation method thereof. Background technique [0002] With the wide application of metal materials, the demand for metal surface paint is also increasing. Some of them need to be coated with paint on the surface in order to resist harsh environments, such as high temperature resistance, cold resistance, ultraviolet resistance, corrosion resistance, etc., and some are In order to play a beautiful role. [0003] At present, in many fields, especially the automobile field, the demand for metallic paint is increasing, and the existing metallic paint contains formaldehyde, which will affect human health during use. At the same time, the existing metallic paint is not enough in scratch resistance, so that a slight scratch will leave irreversible scratches on the paint surface. [0004] Chinese patent CN101215438A discloses a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D151/00C09D7/12C08F257/02C08F220/14
CPCC08F257/02C08K3/22C08K5/05C08K9/04C08K13/06C08K2003/2227C08L2201/08C09D151/003
Inventor 葛卫平陈宗美王维根
Owner 江苏悠谷未来科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com