Double-oil-groove forge piece hot-punching technology

A technology for oil grooves and forgings, which is applied in the field of hot stamping technology for double oil groove forgings, can solve the problems of difficult hot punching technology, the width of oil grooves in a figure-eight shape, and low production efficiency, so as to facilitate popularization and utilization, simplify the production process, The effect of improving productivity

Inactive Publication Date: 2015-06-24
安徽众鑫科技股份有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the field of forging, the inner hole of the forging is basically changed from drilling to hot punching, but for the inner hole of the double oil groove forging, it is difficult to realize the hot punching process. The main reason is that the oil groove is deformed after hot punching, resulting in The width is eight-shaped and the bottom of the oil tank is uneven, and the outside is low and the inside is high. Therefore, in the domestic forging field, the inner hole of the double oil tank forging still adopts the drilling process. This process is time-consuming and labor-intensive, and the cost increases. Low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The double oil tank forging hot stamping process is characterized in that it includes the following process steps:

[0019] ①. Blanking: Set the weight of raw materials on the shearing machine to 3.0kg, and the tolerance is controlled within ±10g. The shearing machine is used to unload the material, and then the shearing machine is used to cut and divide the material.

[0020] ②. Heating: The intermediate frequency furnace is heated to 1000 ° C. The temperature should not be too high or too low. If the temperature is too high, the product will be overheated, and if the temperature is too low, the product will be insufficient;

[0021] ③Blank making: use 400T friction press to make the billet, and the diameter of the billet is smaller than the diameter of the mold cavity by 2mm;

[0022] ④ Forming: Forming with a 400T friction press, preheating the forging mold for 10-15 minutes before forming, and then putting the heated billet into the mold cavity for forging. The fina...

Embodiment 2

[0029] The double oil tank forging hot stamping process is characterized in that it includes the following process steps:

[0030] ①. Blanking: Set the weight of raw materials on the shearing machine to 5kg, and the tolerance is controlled within ±10g. The shearing machine is used to unload the material, and then the material is cut and divided by the shearing machine.

[0031] ②. Heating: The intermediate frequency furnace is heated to 1100°C. The temperature should not be too high or too low. If the temperature is too high, the product will be overheated, and if the temperature is too low, the product will be insufficient;

[0032] ③Blank making: use 400T friction press to make the billet, and the diameter of the billet is 2.5mm smaller than the diameter of the mold cavity;

[0033] ④ Forming: Forming with a 400T friction press, preheating the forging mold for 10-15 minutes before forming, and then putting the heated billet into the mold cavity for forging. The final forging...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a double-oil-groove forge piece hot-punching technology and relates to the technical field of forging. The double-oil-groove forge piece hot-punching technology comprises the following steps of blanking, heating, blank making, forming, hot punching, trimming, isothermal normalizing and shot blasting. The double-oil-groove forge piece hot-punching technology has the advantages that the technology is improved, the hot-punching technology is determined, oil grooves are not changed after punching is carried out, the requirement of the technology is met, the production technology is simplified, the production cost is reduced, the production efficiency is improved, and application and popularization of the double-oil-groove forge piece hot-punching technology are facilitated.

Description

technical field [0001] The invention relates to the technical field of forging, in particular to a hot stamping process for forgings with double oil grooves. Background technique [0002] At present, in the field of forging, the inner hole of the forging is basically changed from drilling to hot punching, but for the inner hole of the double oil groove forging, it is difficult to realize the hot punching process. The main reason is that the oil groove is deformed after hot punching, resulting in The width is eight-shaped and the bottom of the oil tank is uneven, and the outside is low and the inside is high. Therefore, in the domestic forging field, the inner hole of the double oil tank forging still adopts the drilling process. This process is time-consuming and labor-intensive, and the cost increases. Low. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a double oil tank forging hot stamping process with simpl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23P15/00
CPCB23P15/00
Inventor 张锦荣
Owner 安徽众鑫科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com