Environmental-friendly bending-resistant plastic cement material

A technology of plastic materials and bending resistance, applied in the field of plastic materials, can solve the problems of lack of bending resistance, obvious cracks on the surface, etc., to achieve strong resistance to various chemical corrosion, avoid brittleness, and reduce carbon emissions. Effect

Inactive Publication Date: 2015-06-24
青岛新动力文化传媒有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional plastic magnetic material products do not have bending resistance, and obvious cracks are prone to appear on the surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An environment-friendly bending-resistant plastic material is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0018] 60 parts of recycled plastic, 8 parts of rod-shaped wood wool, 8 parts of ethylene-butene copolymer, 12 parts of polytetrafluoroethylene, 5 parts of barium ferrite magnetic powder, 6 parts of graphite, 3 parts of aluminum oxide with a particle size of 30um, 2 parts of interface compatibilizer composed of maleic anhydride grafted polyethylene and titanate in a weight ratio of 3:2, 2 parts of polyphenylene sulfide, 1 part of silane coupling agent, 0.6 part of antimony dioxide, particle size of 60um Molybdenum disulfide 0.5 parts.

Embodiment 2

[0020] An environment-friendly bending-resistant plastic material is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0021] 65 parts of recycled plastic, 10 parts of rod-shaped wood wool, 10 parts of polymethyl methacrylate, 13 parts of polytetrafluoroethylene, 6 parts of barium ferrite magnetic powder, 7 parts of graphite, 4 parts of aluminum oxide with a particle size of 30um, 3 parts of interface compatibilizer composed of maleic anhydride grafted polyethylene and titanate in a weight ratio of 3:2, 3 parts of polyphenylene sulfide, 2 parts of silane coupling agent, 0.7 part of antimony dioxide, particle size of 70um Molybdenum disulfide 0.6 parts.

Embodiment 3

[0023] An environment-friendly bending-resistant plastic material is characterized in that the components of the raw materials are composed as follows in parts by weight:

[0024] 70 parts of recycled plastic, 12 parts of rod-shaped wood wool, 12 parts of ethylene-acrylic acid copolymer, 15 parts of polytetrafluoroethylene, 8 parts of barium ferrite magnetic powder, 8 parts of graphite, 5 parts of aluminum oxide with a particle size of 40um, horse 4 parts of interfacial compatibilizer, 4 parts of polyphenylene sulfide, 3 parts of silane coupling agent, 0.8 part of antimony dioxide, and 80um particle size are composed of toric anhydride grafted polyethylene and titanate in a weight ratio of 3:2. 0.7 parts of molybdenum sulfide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmental-friendly bending-resistant plastic cement material. The environmental-friendly bending-resistant plastic cement material is characterized in comprising following raw material ingredients, by weight, 60 to 70 parts of reprocessed plastic, 8 to 12 parts of rodlike wood wool, 8 to 12 parts of thermoplastic, 12 to 15 parts of polytetrafluoroethylene, 5 to 8 parts of barium ferrite magnetic powder, 6 to 8 parts of graphite, 3 to 5 parts of aluminium oxide, 2 to 4 parts of an interface compatibilizer, 2 to 4 parts of polyphenylene sulfide, 1 to 3 parts of silane coupling agent, 0.6 to 0.8 part of tellurium dioxide, and 0.5 to 0.7 part of molybdenum disulfide. The environmental-friendly bending-resistant plastic cement material is capable of resisting chemical corrosions preferably, and possesses high temperature resistance, bending resistance, and wear resistance; the adding amount of wood powder is controlled preferably based on a plurality of experiments, so that increasing of composite material fragility is avoided, and processing energy consumption is reduced; and the adding of reprocessed plastic is capable of reducing carbon emission, and realizing recycling, and environmental protection effect is excellent.

Description

technical field [0001] The invention belongs to the technical field of plastic materials, and in particular relates to an environment-friendly bending-resistant plastic material. Background technique [0002] Recycled plastics have broad prospects, turning waste into treasure, and the products (plastic granules) are very popular. The demand of plastic enterprises is large, and the gap of plastic granules is very large, which cannot meet the demand of plastic manufacturers. Therefore, the sales are excellent and the benefits are excellent. There are many sources of raw materials for waste plastics. Where there are people, there are waste plastics, which are easy to purchase and cheap (as in various places). A city consumes more than 10 tons of various plastic products such as plastic food bags every day, and there are also a lot of waste plastics in rural areas that can be recycled. [0003] Wood-plastic composite material is a kind of composite material mainly composed of wo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08L27/18C08L97/02C08L23/08C08L25/06C08L33/12C08K3/22C08K3/04C08K3/30
Inventor 宋修训
Owner 青岛新动力文化传媒有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap