High-strength glue

A high-strength, glue technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of poor environmental performance, insufficient environmental protection, poor comprehensive performance, etc., to meet strict requirements, Improve the effect of environmental protection and superior comprehensive performance

Active Publication Date: 2015-06-24
NANTONG HONGRUI CHEM
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The vinyl acetate used in this glue is highly toxic and not environmentally friendly
[0006] Chinese invention patent application 201410004735.1 (public date: April 16, 2014) discloses an environmentally friendly white latex, the glue includes: polyvinyl alcohol PVA, vinyl acetate VAC, acrylic acid AA, acrylamide AM, persulfuric acid Ammonium, anionic emulsifier A-102, alkyl polyoxyethylene ether LCN-287 nonionic emulsifier; corn starch, transparent powder, plasticizer, diethylene glycol dibenzoate DEDB, preservative KSG-201, hydrogen Sodium oxide, and methanol; but this glue still uses toxic vinyl acetate, which has poor environmental performance
[0007] At the same time, the related glue disclosed in the prior art has poor overall performance in terms of use effect, and cannot yet meet the relevant requirements for the quality of high-grade energy-saving wooden doors and windows.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] This embodiment relates to a high-strength glue and a preparation method thereof; the glue includes the following components in parts by weight:

[0029] Polyvinyl acetate 700,

[0030] Vinyl acetate 300,

[0031] Polyvinyl alcohol 120,

[0032] Dibutyl phthalate 60,

[0033] Diethylene glycol dibenzoate 20,

[0034] Octanol 10,

[0035] Isopropanol 30,

[0036] Allyl methacrylate 10,

[0037] Ethylene glycol dimethacrylate 5,

[0038] Toluene diisocyanate 3,

[0039] Sodium bicarbonate 35,

[0040] water 1400,

[0041] Emulsifier 40, the emulsifier is sodium oleate (i.e. sodium octadecenoate);

[0042] Initiator 5, the initiator is ammonium persulfate.

[0043] All components involved in this example can be obtained through public commercial channels. The preparation method step of high-strength glue in the present embodiment is as follows:

[0044] Step 1, under stirring conditions, take 50-73% by weight of water and polyvinyl alcohol, mix, heat up to 88-...

Embodiment 2

[0050] This embodiment relates to a high-strength glue. The preparation method of the glue refers to Example 1. The glue includes the following components in parts by weight:

[0051] Polyvinyl acetate 1050,

[0052] Vinyl acetate 350,

[0053] Polyvinyl alcohol 145,

[0054] Dibutyl phthalate 100,

[0055] Diethylene glycol dibenzoate 40,

[0056] Octanol 15,

[0057] Isopropanol 45,

[0058] Allyl methacrylate 25,

[0059] Ethylene glycol dimethacrylate 10,

[0060] Toluene diisocyanate 7,

[0061] Sodium bicarbonate 50,

[0062] water 1500,

[0063] Emulsifier 50, the emulsifier is sodium dodecylbenzenesulfonate;

[0064] Initiator 10, the initiator is ammonium persulfate.

Embodiment 3

[0066] This embodiment relates to a high-strength glue. The preparation method of the glue refers to Example 1. The glue includes the following components in parts by weight:

[0067] Polyvinyl acetate 800,

[0068] Vinyl acetate 315,

[0069] Polyvinyl alcohol 125,

[0070]Dibutyl phthalate 80,

[0071] Diethylene glycol dibenzoate 25,

[0072] Octanol 12,

[0073] Isopropanol 35,

[0074] Allyl methacrylate 15,

[0075] Ethylene glycol dimethacrylate 7,

[0076] Toluene diisocyanate 4,

[0077] Sodium bicarbonate 39,

[0078] water 1450,

[0079] Emulsifier 45, the emulsifier is sodium dodecylbenzenesulfonate;

[0080] Initiator 6, the initiator is potassium persulfate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides high-strength glue, which comprises the following components in parts by weight: 700-1050 parts of polyvinyl acetate, 300-350 parts of vinyl acetate, 120-145 parts of polyvinyl alcohol, 60-100 parts of dibutyl phthalate, 20-40 parts of diethylene glycol dibenzoate, 10-15 parts of octanol, 30-45 parts of isopropyl alcohol, 10-25 parts of allyl methacrylate, 5-10 parts of glycol dimethacrylate, 3-7 parts of toluene diisocynate, 35-50 parts of sodium bicarbonate, 1400-1500 parts of water, 40-50 parts of an emulsifier and 5-10 parts of an initiator. The content of vinyl acetate in the glue provided by the invention is greatly reduced; solvents such as formaldehyde do not need to be used; the environmental protection property of the product is fundamentally improved; meanwhile, the glue provided by the invention has excellent performances on the indexes such as thermal stability, initial drying time, hydrolytic resistance, bonding strength and curing time, and has excellent overall performance.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-strength glue. Background technique [0002] At present, the threshold industry of doors and windows is relatively low, and the competition in the industry is relatively chaotic. In order to improve product quality and market competitiveness, continuous improvement is required. High-grade energy-saving wooden doors and windows widely used in building exterior windows include: pure wood doors and windows, aluminum-clad wood doors and windows, and wood-aluminum composite doors and windows. The wood-aluminum composite doors and windows are more suitable for the rainy, high temperature and humid climate conditions in the south because the outer side is made of heat-insulating aluminum alloy profiles and the inner side is made of wood decorative profiles. At present, the structure of wood-aluminum composite doors and windows processed and produced in the domestic ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J151/00C09J11/08C09J11/06
CPCC08F263/04C09J11/06C09J11/08C09J151/00C08L29/04C08K5/12C08K5/05C08F218/08
Inventor 杭春林
Owner NANTONG HONGRUI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com