Matte aluminum foil mylar conductive adhesive tape for electromagnetic wave shielding and preparation method thereof

A conductive tape and electromagnetic wave technology, applied in the direction of conductive adhesives, adhesives, film/sheet adhesives, etc., can solve the problems of surface ink resistance to solvents, restrictions on the large-scale application of aluminum foil MYLAR, and potential safety hazards. Achieve the effects of outstanding electrical and physical properties, good market application prospects, and easy preparation methods

Active Publication Date: 2017-01-18
江苏伊诺尔新材料科技有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, the typical application of matte aluminum foil MYLAR conductive tape is LCD electromagnetic shielding and shading. However, the current domestic aluminum foil MYLAR has poor softness, easy edge warping, surface ink treatment is not resistant to solvents, fingerprints, and is not There are many problems such as scratch resistance, poor or uneven electrical conductivity of the product, and even electrical conductivity on the surface, which leads to safety hazards during use, which restricts the large-scale application of aluminum foil MYLAR

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Stir and mix 100 parts of ink, 30 parts of toluene, 5 parts of curing agent and 10 parts of matting agent evenly to make an ink treatment layer, then fully filter the prepared ink treatment layer with a 400-mesh filter cloth, and seal it for later use ; Then clean the matte aluminum foil MYLAR substrate to remove surface oil and impurities, coat the polyester film surface with an ink treatment layer 3 times, and place the semi-finished product in an oven for aging; then apply the anti-scratch and anti-fingerprint solution 100 parts, 20 parts of ethyl acetate, and 5 parts of matting agent are stirred and mixed evenly to make a functional coating, and to be used, apply the functional coating twice on the mature ink treatment layer; then, on the other side (aluminum foil side) Coat the adhesive layer, and attach the release layer on the adhesive layer; store the prepared matte anti-fingerprint and anti-scratch aluminum foil MYLAR conductive tape for electromagnetic wave shi...

Embodiment 2

[0041] This embodiment is roughly the same as Example 1, the only difference being that the component contents of the ink treatment layer and the functional coating material are different, wherein the components of the ink treatment layer are: 120 parts of ink, 36 parts of toluene, 6 parts of curing agent and 12 parts of matting agent, the components of the functional coating are: 120 parts of anti-scratch and anti-fingerprint solution, 24 parts of ethyl acetate, and 6 parts of matting agent. The rest will not be repeated.

Embodiment 3

[0043] This embodiment is roughly the same as Example 1, the only difference being that the component contents of the ink treatment layer and the functional coating material are different, wherein the components of the ink treatment layer are: 150 parts of ink, 45 parts of toluene, 7.5 parts of curing agent and 15 parts of matting agent, the components of the functional coating are: 150 parts of anti-scratch and anti-fingerprint solution, 30 parts of ethyl acetate, and 7.5 parts of matting agent. The rest will not be repeated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a matt fingerprint-proof and scratch-resistant aluminum foil MYLAR conductive tape for electromagnetic wave shielding and a preparation method. Matt aluminum foil MYLAR is processed and the substrate surface of a base material is coated with an ink processing layer and a functional coating; the preparation method is simple and easy to realize; the matt aluminum foil MYLAR conductive tape having characteristics of good flexing resistance, fingerprint prevention and excellent solvent resistance, scratch resistance and conductivity is obtained; the conductive tape is very outstanding in electric property and physical property, thereby having a good market application prospect.

Description

technical field [0001] The invention relates to an anti-fingerprint, solvent-resistant and scratch-resistant aluminum foil MYLAR conductive adhesive tape for electromagnetic wave shielding and a preparation method, belonging to the technical field of electromagnetic wave shielding. Background technique [0002] With the rapid development of electronic technology, computers and radio communications are widely used and densely configured, which greatly facilitates and technologicalizes our lives. However, at the same time, the radiation of electromagnetic waves will have different effects on our organs, tissues and systems. The degree of harm, long-term exposure to electromagnetic radiation environment may have the risk of cancer. As people pay more and more attention to their own health, there are more and more in-depth researches on how to effectively control electromagnetic radiation. [0003] Aluminum foil MYLAR is a new type of material that is gradually replacing tradit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02C09J9/02
Inventor 张全玲吴卫荣程晓婷
Owner 江苏伊诺尔新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap