Environment-friendly efficient photocatalyst formaldehyde scavenger
A formaldehyde scavenger and photocatalyst technology, applied in the field of chemical industry, can solve the problems of secondary pollution, high toxicity of compounds, limited adsorption capacity, etc., and achieve the effect of mild application conditions and good formaldehyde removal performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0040] An environment-friendly high-efficiency photocatalyst formaldehyde scavenger, which consists of the following components by weight percentage: 10g of silk peptide-based surfactant, 8g of 5,5-dimethylimidazolidine-2,4-dione, platinum-loaded nano-anatase Mineral type titanium dioxide 2g, nano-silver colloid 0.1g, pure water 79.9g.
[0041]The preparation process is as follows:
[0042] (1) Take the platinum-loaded nano-anatase titanium dioxide and nano-silver colloid of the prescription amount and add them to 69.9g of pure water, mix and stir for 30 minutes to obtain a mixed solution;
[0043] (2) Add the silk fibroin peptide-based surfactant and 5,5-dimethylimidazolidine-2,4-dione in the prescribed amount into 10 g of pure water, and stir evenly to obtain a mixed solution;
[0044] (3) Add the mixed solution obtained in step (2) to the mixed solution obtained in step (1), and stir for 30 minutes to obtain the finished product.
Embodiment 2
[0046] An environment-friendly high-efficiency photocatalyst formaldehyde scavenger, which is composed of the following components by weight percentage: 1500g of silk peptide-based surfactant, 500g of 5,5-dimethylimidazolidine-2,4-dione, platinum-loaded nano-anatase Mineral type titanium dioxide 400g, nano-silver glue 50g, pure water 7550g.
[0047] The preparation process is as follows:
[0048] (1) Get the platinum-loaded nano-anatase titanium dioxide and nano-silver colloid of the prescription amount and add them to 6550g pure water, mix and stir for 20 minutes to obtain a mixed solution;
[0049] (2) Take the silk fibroin peptide-based surfactant and 5,5-dimethylimidazolidine-2,4-dione in the prescribed amount and add them to 1000g of pure water, stir evenly to obtain a mixed solution;
[0050] (3) Add the mixed solution obtained in step (2) to the mixed solution obtained in step (1), and stir for 40 minutes to obtain the finished product.
Embodiment 3
[0052] An environment-friendly high-efficiency photocatalyst formaldehyde scavenger, which consists of the following components by weight percentage: 5g of silk fibroin peptide-based surfactant, 10g of 5,5-dimethylimidazolidine-2,4-dione, platinum-loaded nano anatase Mineral type titanium dioxide 8g, nano-silver colloid 0.1g, pure water 76.9g.
[0053] The preparation process is as follows:
[0054] (1) Take the platinum-loaded nano-anatase titanium dioxide and nano-silver colloid of the prescription amount and add them to 66.9g of pure water, mix and stir for 40 minutes to obtain a mixed solution;
[0055] (2) Add the silk fibroin peptide-based surfactant and 5,5-dimethylimidazolidine-2,4-dione in the prescribed amount into 10 g of pure water, and stir evenly to obtain a mixed solution;
[0056] (3) Add the mixed solution obtained in step (2) to the mixed solution obtained in step (1), and stir for 20 minutes to obtain the finished product.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com