The Boundless Stone Method for Copperwork

A stone inlaid and boundless technology, applied in clothing, applications, jewelry, etc., can solve the problems of difficult inlays and rotten stones, and achieve the effects of reducing difficulty, avoiding rotten stones, and improving production efficiency

Active Publication Date: 2017-03-15
LIUZHOU XUPING JEWELRY
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a method for inlaying copper ornaments without borders, which can solve the problems that the existing method of inlaying without borders is difficult and easily causes rotten stones

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for inlaid stones for copper ornaments without borders, comprising the following steps:

[0017] A. Silver plate production: The silver plate is enlarged and made at a scale of 1.045 times that of the copper decoration, and a zircon pit is reserved; the zircon pit is made into a slot on the cross arm, and the opening size of the slot is 0.2 mm , with a depth of 0.1 mm;

[0018] B. Press the silver plate into a plastic mold for copper ornaments;

[0019] C. Preparing stones: select a plurality of zircon, and open a groove at 0.5 mm below the waistline of each zircon, and the opening width of the groove is 0.2 mm and the depth is 0.1 mm;

[0020] D, making wax mold: inject wax liquid into the plastic mold to make the wax mold of the copper ornament;

[0021] E. Inlay: inlay the zircon prepared in step C on the wax mold made in step D, and when inlaying, the zircon groove should be matched with the groove of the cross arm, Then fill the slot with wax liquid; af...

Embodiment 2

[0025] A method for inlaid stones for copper ornaments without borders, comprising the following steps:

[0026] A. Silver plate production: The silver plate is enlarged and produced at a scale of 1.05 times that of the copper ornament, and a zircon pit is reserved; the zircon pit is made into a slot on the cross arm, and the opening size of the slot is 0.3 mm , with a depth of 0.2 mm;

[0027] B. Press the silver plate into a plastic mold for copper ornaments;

[0028] C. Preparing stones: select a plurality of zircon, and open a groove at 0.6 mm below the waistline of each zircon, and the opening width of the groove is 0.3 mm and the depth is 0.2 mm;

[0029] D, making wax mold: inject wax liquid into the plastic mold to make the wax mold of the copper ornament;

[0030] E. Inlay: inlay the zircon prepared in step C on the wax mold made in step D, and when inlaying, the zircon groove should be matched with the groove of the cross arm, Then fill the slot with wax liquid; a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
depthaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an edgeless stone embedding method for copper decorations, and relates to the technical field of decoration manufacturing. The method includes the steps that A, silver plates are manufactured; B, rubber molds are pressed; C, stone is prepared; D, wax molds are manufactured; E, embedding is conducted; F, rough pieces are manufactured; G, finished products are manufactured. Compared with the prior art, by means of the edgeless stone embedding method, the problems that by means of an existing edgeless stone embedding method, the embedding difficulty is high and smashed stone is prone to being generated can be solved.

Description

technical field [0001] The invention relates to the technical field of jewelry making, in particular to a borderless diamond setting method suitable for copper jewelry. Background technique [0002] In the production process of copper ornaments, in order to increase the color and beauty of copper ornaments, many zircons are often inlaid on the copper ornaments; there are many ways of inlaying zircon, among which the zircon ornaments are inlaid with the borderless method, so that the The zircon has a more prominent appearance; the current borderless setting method is to first make a copper base, and then open a shallow groove on the side of the bottom of the zircon according to the size of the copper base, and then use external force to place the copper base. Squeeze into the slot to fasten the zircon; using this method has high requirements on the operation skills of the stone setting workers, and the setting is difficult, the efficiency is low, it is easy to cause rotten st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A44C27/00
Inventor 李冬梅
Owner LIUZHOU XUPING JEWELRY