Composite spherical activated carbon added with polyester fibers and capable of improving mechanical strength as well as preparation method of composite spherical activated carbon

A spherical activated carbon and polyester fiber technology, applied in the field of materials, can solve the problems of high ash content of coal-based activated carbon, limited application and development, low mechanical strength, etc., and achieve the effects of easy flow, improved adsorption, and improved mechanical strength.

Inactive Publication Date: 2015-11-18
ANHUI CHENGFANG NEW MATERIAL TECH
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, coal-based spherical activated carbon has the advantages of cheap raw materials and wide sources, but coal-based activated carbon has high ash content, many impurities, and low mechanical strength, which limits its application and development.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] specific implementation plan

[0016] The present invention will be described in detail below through specific examples.

[0017] A composite spherical activated carbon with polyester fibers added to improve mechanical strength, prepared from the following raw materials in parts by weight (kg): cyclohexyl acrylate 42, α-methylstyrene 39, butyl formate 25, azobis Isobutyronitrile 2, ethylene glycol dimethacrylate 2, gelatin 2, sodium pyrosulfite 1, appropriate amount of distilled water, appropriate amount of acetone, sulfonated pitch powder 25, polyester fiber 4, silane coupling agent kh5601, graphene 2, seaweed Sodium Acid 1;

[0018] A kind of composite spherical activated carbon that adds polyester fiber to improve mechanical strength of the present invention is made by following specific steps:

[0019] (1) Add gelatin to 100 times the amount of distilled water, heat until completely dissolved, slowly cool down to room temperature, add sodium metabisulfite, stir un...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses composite spherical activated carbon added with polyester fibers and capable of improving mechanical strength. The composite spherical activated carbon is characterized by being prepared from raw materials in parts by weight as follows: 42-46 parts of cyclohexyl acrylate, 39-42 parts of alpha-methyl styrene, 25-28 parts of butyl formate, 2-3 parts of azodiisobutyronitrile, 2-2.5 parts of ethylene glycol dimethacrylate, 2-3 parts of gelatin, 1-1.5 parts of sodium metabisulfite, a proper amount of distilled water, a proper amount of acetone, 25-28 parts of sulfonated asphalt powder, 4-5 parts of the polyester fibers, 1-2 parts of a silane coupling agent kh560, 2-3 parts of graphene and 1-2 parts of sodium alginate. According to the composite spherical activated carbon, the polyester fibers and the graphene are added to an asphalt coating liquid, through a series of modification, the compound components can form a porous three-dimensional structure, the adsorbability of the composite spherical activated carbon to oil substances can be further improved, and the mechanical strength of an asphalt base can also be enhanced. The composite spherical activated carbon is high in purity, low-dust, abrasion-resistant, easy in flowing, easy to fill and broad in application prospect.

Description

technical field [0001] The invention relates to the field of materials, in particular to a composite spherical activated carbon with polyester fibers added to improve mechanical strength and a preparation method thereof. Background technique [0002] Spherical activated carbon has been widely used in related fields such as medicine, environmental protection and catalyst carrier because of its good sphericity, high packing density, less particle shedding and fast adsorption and desorption speed. Spherical activated carbon is mainly divided into three categories according to different raw materials: coal-based spherical activated carbon, polymer resin-based spherical activated carbon and pitch-based spherical activated carbon. Among them, coal-based spherical activated carbon has the advantages of cheap raw materials and wide sources, but coal-based activated carbon has high ash content, many impurities, and low mechanical strength, which limits its application and development...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/30C01B31/08
Inventor 沈向洋刘鹏翔吴杰吴育兵吴悦琪
Owner ANHUI CHENGFANG NEW MATERIAL TECH
Who we serve
  • R&D Engineer